Sol-Gel Preparation and Luminescence Properties of BaMgAl10O17∶Eu2+ Phosphors

The synthesis of BaMgAl10O17∶ Eu2 (BAM) phosphors using the sol-gel method and their luminescence properties were reported. The blue-light emitting BAM was synthesized using citric acid and ethylene glycol as chelating materials. Emission of blue-light was obtained from these phosphors. The luminescent intensity increases as the temperature of heat treatment is increased. This study investigated the effects of the molar ratio of ethylene glycol to citric acid (Φ value), with respect to the phase formation and luminescence properties of BAM. The variation of the Φ value resulted in the change of the sol-gel reaction mechanism and the microstructures of the resultant powders. An increase in Φ value leads to an increase in the rate of BAM phase formation. The photoluminescent intensity of the prepared phosphors increases with heating temperatures because of enhanced crystallization.     

BaFe12O19/SiO2-B2O3微晶玻璃陶瓷的制备和微波性能

采用柠檬酸sol-gel工艺合成了BaFe12O19/SiO2-B2O3微晶玻璃陶瓷，研究了SiO2-B2O3玻璃的含量，Ba/Fe原子比和热处理温度对体系析出晶相的影响，以及介电常数和磁异率在1MHz-6GHz频率范围的变化规律，结果表明，休系中SiO2-B2O3玻璃的含量和Ba/Fe比越高，BaF312O19相的析出越困难，前驱体合适的热处理温度为1000℃，介电常数和磁导率基本上随测试频率的增而加下降；介电损耗的最大值为0．43，磁损耗较小。     

Sol-Gel Preparation of LaNiO3 and Its Physical and Chemical Properties

LaNiO3 was synthesized by sol-gel method in which lanthanum nitrate and nickel nitrate were used as start materials and citric acid was used as complex for gel formation.The precursor was dried and subsequently heated at elevated temperature to form the desired product.XRD analysis shows that pure LaNiO3 was synthesized.Electrical conductivity and electrochemical performance of the material were tested.The electrical conductivity decreases from 34.5that there are current peaks in the curve, which is the evidence of the electrochemical activity of LaNiO3.     

Nonepitaxial Orientation in Sol–Gel Bismuth Titanate Films

Control over crystallographic orientation in ceramic thin films is important for highly anisotropic structures. Layered perovskites, like Bi₄Ti₃O₁₂, have interesting properties associated with their ferroelectric nature, which may be fully exploited only when films are highly textured. Textured films of this titanate were fabricated via a sol–gel technique without using epitaxial growth. Orientation in the film is confirmed by XRD and SEM, and supported by refractive index and dielectric measurements. In an attempt to explain the orienting effect, light scattering experiments were conducted to yield information about the molecular size, shape, and conformation of macromolecules as the sol–gel solution ages and condensation reactions proceed. These experiments clearly show an increase in the size of molecular clusters with time. We believe that it is the organization of these large clusters during spin coating, and the relationship of the backbone chemistry to the crystal structure of Bi₄Ti₃O₁₂, that are responsible for the observed orientation.     

YAG：Ce Phosphors for WLED via Nano-Pesudoboehmite Sol-Gel Route

The sub-micron sized YAG ： Ce phosphors were synthesized via a modified sol-gel method by peptizing nano-pesudoboehmite particulate. It is found that YAG phase from the dried gel powders appears at 1000 ℃ then the pure YAG phase exists at a relatively lower sintering temperature of 1400 ℃. The smaller sizes of phosphors in the ranges of 1 - 3 μm are obtained due to the contribution of seeding effects of nano-sized alumina particles to strengthen each step of the processes. Both the excitation and emission spectra of photoluminescence of the phosphor obtained at 1400 ℃ meet well with the spectroscopic requirements of the WLED phosphors.     

溶胶-凝胶法制备纳米氧化锡及其性能表征

以SnCl4·5H2O为原料,采用溶胶-凝胶法制备了纳米SnO2粒子,研究了焙烧温度、碱的种类及反应物浓度对纳米SnO2粒子大小和分散状态的影响。采用XRD、TEM、ED等技术对SnO2纳米粒子的性能进行了表征。实验结果表明:用氨水和尿素作为沉淀剂,控制反应结束时pH值为7,在600℃焙烧,制备得到粒子尺寸约为15nm、分散性良好的纳米SnO2粒子。     

溶胶-凝胶法制备磷钨酸-硅胶催化合成苹果酯

采用溶胶-凝胶法制备了一系列磷钨酸-硅胶催化剂(PW/SG),考察了该催化剂催化乙酰乙酸乙酯与乙二醇液相缩合制备苹果酯的反应性能。实验结果表明,PW质量分数为40%时的PW/SG催化剂表现出最佳的催化活性;40%PW/SG催化剂制备苹果酯的最佳工艺条件为:n(乙酰乙酸乙酯)∶n(乙二醇)=1∶1.2,催化剂用量占反应物质量的0.36%,带水剂环己烷用量占反应物体积的30%,反应温度383K,反应时间90min;在此条件下,乙酰乙酸乙酯的转化率可达95.5%,苹果酯的选择性大于97%;催化剂稳定性实验表明,经5次重复使用,40%PW/SG催化剂的活性基本保持不变,乙酰乙酸乙酯转化率稳定在95.0%左右。     

稀土稳定氧化锆超细粉末的合成机理研究

依据Al(Ⅲ )、Zr(Ⅳ )的水解聚合机理 ,把锆、铝和钇的无机盐溶液按一定组成混合在一起 ,通过加入乙二醇作为络合剂和调节溶液的PH值来获得溶胶 ,并直接蒸馏溶胶来获得干凝胶 ,最后制得ZrO2 (Y2 O3 ) -Al2 O3 系粉末。研究结果表明 :该工艺不仅制粉时间快、成本低、产量大 ,而且粒子均匀 ,粒径在 2 0～ 5 0nm之间 ,具有一定的可行性     

Sol-Gel Alumina Coating for Improved Cyclic Oxidation Resistance of Silicon Nitride

A 25 nm thick α-alumina layer was deposited on a turbine-grade silicon nitride by sol-gel dip coating and subsequent heat treatment in air at 1200°C. This layer had a nanometer grain structure. Silicon nitride protected by this thin layer showed a significant improvement in oxidation resistance over its uncoated counterpart after 200 cyclic exposures in air at 1250°C. The oxide layer grown on the coated silicon nitride also exhibited superior surface morphology, compared with the uncoated silicon nitride.     

多孔陶瓷分离膜

多孔陶瓷膜由于其优良的耐高温、耐腐蚀、耐微生物侵蚀等性质，近年来被快速地应用于分离领域。本文介绍其制备方法、性能测定及应用前景。