Mechanical properties,corrosion resistance,and rubber pad forming of cold differential speed-rolled pure titanium for bipolar plates of proton-exchange membrane fuel cells

Due to problems such as pores on surface-treated coatings, the corrosion resistance of pure titanium bipolar plates for proton-exchange membrane fuel cells can be further improved by increasing the corrosion resistance of pure titanium by using differential speed-rolling (DSR); however, these materials have not yet reached the standard requirements of bipolar plates (corrosion current density i_corr＜10³ nA·cm^?2). In this work, the corrosion resistance of pure titanium was improved by optimizing the DSR process while the strength was maintained. The best corrosion resistance of the DSR pure titanium was achieved when the roller speed ratio was 2, while i_corr was 429 nA·cm^?2 in a solution of 0.5 M H₂SO₄ and 2 mg/L HF at room temperature. The formability of the DSR pure titanium for bipolar plates was verified. The optimal holding pressure range was 6.8–7.0 kN.     

Unipolar plasma electrolytic oxidation: Waveform optimisation for corrosion resistance of commercially pure titanium

This study deals with the anodisation of titanium grade 2 in 0.5-M sulphuric acid using a pulsed signal in a unipolar regime. The electrical parameters investigated are voltage, frequency and duty cycle. The use of duty cycles with a high percentage of anodic polarisation (90%), combined with high frequencies (1000 Hz) and the higher voltage tested (220 V), favoured the establishment of a plasma regime involving strong dielectric discharges, allowing the growth of thicker oxides but with rough architecture. The corrosion resistance of the formed film has been characterised by potentiodynamic tests in 0.5-M NaBr for localised corrosion resistance and by immersion tests in 10% v/v sulphuric acid solution for a uniform corrosion assessment. Current–time curves, visual observations and electron microscope analysis (scanning electron microscopy, energy-dispersive X-ray spectroscopy) were the tools selected to provide a correlation between technological parameters and oxide growth mechanism. For localised and uniform corrosion, anodisation at 220 V with a high level of anodic polarisation (90%) and frequency (1000 Hz) was verified to be particularly advantageous.     

Interfacial failure analysis of functionally graded adhesively bonded double supported tee joint of laminated FRP composite plates

This paper deals with three-dimensional non-linear finite element analyses to assess the structural behavior of adhesively-bonded double supported tee joint of laminated FRP composites having embedded interfacial failures. The onset of interfacial failures is predicted by using Tsai–Wu coupled stress failure criterion with pre-determined stress values. The concept of fracture mechanics principle is utilized to study the sustainability of the tee joint having interfacial failures pre-existed at the critical locations. Individual modes of the strain energy release rates (SERR) G_I, G_II and G_III, are considered as the damage growth parameters and, are evaluated using the Modified crack closure integral (MCCI) technique based on the concept of linear elastic fracture mechanics (LEFM). Based on the stress analyses, it has been observed that the interfacial failures in tee joint structure trigger at the interface of base plate and adhesive layer from both ends of base plate. Depending on the SERR magnitudes, it has been noticed that the interfacial failure propagates under mixed mode condition. Therefore total SERR (G_T) is considered as the governing parameter for damage propagation. Furthermore, efforts have been made to retard damage propagation rate by employing functionally graded adhesive (FGA) instead of monolithic adhesive material. Series of numerical simulations have been performed for varied interfacial failure length in functionally graded adhesively bonded double supported tee joint structure in order to achieve the significant effect of FGA with various modulus ratios on SERR. Material gradation of adhesive indicates significant SERR reduction at the incipient stage of failure which necessitates the use of functionally graded adhesive for the tee joint and prolong the service life of the structure.     

高强WSTi544221合金组织与性能研究

研究了轧制变形量对WSTi544221合金棒材显微组织和力学性能的影响,并对Φ10 mm规格的棒材进行不同制度的固溶+时效处理,对比了不同热处理状态下棒材的组织和力学性能。结果表明,随着轧制变形量的增大,WSTi544221合金棒材的晶粒细化程度增大,强度逐渐提高,但塑性变化不大。经870℃×1 h/WC+520℃×6 h/AC固溶+时效处理后,强度与塑性可以获得良好匹配,当抗拉强度达到1 610 MPa、屈服强度达到1 531 MPa时,延伸率和断面收缩率可分别保持在12%和43%。     

改性纳米TiO2光催化降解苯酚活性的研究

在装有紫外光的光催化反应器中，用锐钛型纳米TiO2为光催化剂，进行了苯酚水溶液的光催化降解性能的研究。考察了溶液的pH值、纳米TiO2用量、镍（Ni^2＋）掺杂量、苯酚的初始质量浓度等因素对苯酚水溶液光催化降解过程的影响。结果表明，在pH值为7时，苯酚水溶液的降解率达95％以上，强酸和强碱条件均不利于苯酚的降解。当TiO2用量为50mg，UV辐照40min时，200mL质量浓度为50mg／L的苯酚水溶液的降解率为96．3％；当TiO2用量为150mg，UV辐照60min时，200mL质量浓度100mg／L的苯酚水溶液的降解率为95．8％。镍掺杂增加了TiO2的光催化活性，用质量分数为10％的二氯化镍水溶液掺杂制备的复合光催化剂，苯酚水溶液的降解率比未掺杂时增加13．6％。     

诱导水解法制备微细高分散金红石型二氧化钛

采用加热TiCl4稀溶液的方式,制备晶种,将其导入一定浓度的TiCl4溶液中进行诱导水解。所得的偏钛酸经干燥、煅烧后得到分散性好,D50为1 mm以下,金红石含量为≥95%的高纯TiO2,可用于生产PTC热敏电阻等铁电陶瓷。