Phase formation,structure and properties of light-weight aluminosilicate proppants based on clay-diabase and clay-granite binary mixes

One of the drawbacks of fusible clays is the narrow sintering interval due to a sharp increase in the amount of iron-silicate melt at a temperature of 1000–1100 °C, which hardens in the form of a glass phase upon cooling. This leads to a relatively low mechanical strength of the calcined samples and causes the danger of melting the granular material surface from such clays during the firing process. To increase the strength of samples of fusible clays, the influence of diabase and granitoid rocks was considered. It was found that the strengthening effect of diabase and granitoid rock additives in an amount of 20–50% in a mixture with fusible clay is due to an increase of total content of the crystalline phase (mullite, cristobalite and residual quartz) from 18–20% in clays without additives to 22–28 % - in mixtures with diabase and to 28–34% - with granitoid additives) at a temperature of 1050–1100 °C. This increase is due to the activation of synthesis processes of secondary mullite and crystallization from alkali-rich feldspar melt of amorphous silica, released from the structure of clay minerals. The established influence of the igneous rocks used made it possible to develop compositions and propose process flow sheet for producing aluminosilicate proppants based on fusible clays. The use of granitoid and diabase rocks in an amount of 20–70% with fusible clays produces lightweight aluminosilicate proppants with bulk density of 1.40–1.46 g/cm³ at temperature range of 1050–1100 °C, which can endure destructive pressures up to 34.5–52 MPa.     

Hetero-assembly of colloidal particles in concentrated non-aqueous suspensions by polymer dispersant design

Although many colloidal assembling systems have been reported, most systems suffer from severe aggregation under high solid concentrations, which can often be observed in typical hetero-aggregation system. In this study, we created a hetero-assembly system using concentrated (~50 vol%) suspensions by mixing large SiO₂ particles modified with polyacrylic acid partially complexed with oleylamine (PAA-OAm) and small SiO₂ particles modified with polyethyleneimine partially complexed with oleic acid (PEI-OA) in a non-aqueous solvent. We demonstrated that hetero-assembly is driven by the interactions between the uncomplexed carboxyl/amine groups of the PAA/PEI present on the particles, while severe aggregation is simultaneously prevented by the steric repulsions of the aliphatic oleyl chains. Comparison of the cross sections of the in-situ solidified hetero-assembled suspensions with those of ideally assembled structures which were reproduced by a simulation considering the statistical distribution of particles strongly supported successful particle assembling via the proposed approach. The results revealed that the OA content in the PEI-OA complex was the dominant factor that controlled the dispersion and assembling state of the binary particles. The significance of this study is that our findings will provide a class of colloidal dispersion state which binary particles were assembled in a high solid content suspension without forming strong aggregates.     

Relationship between the adhesion properties of UV-curable alumina suspensions and the functionalities and structures of UV-curable acrylate monomers for DLP-based ceramic stereolithography

Digital light processing (DLP)-based ceramic stereolithography has attracted significant attentions due to the high printing speed and high dimensional accuracy of DLP printers. However, undesired dropping of unfinished ceramic parts during printing, owing to inadequate adhesion between the first cured layer and the substrate of the building platform, still remains a challenge. In this study, the relationship between the adhesion properties of ultraviolet (UV)-curable alumina (α-Al₂O₃) suspensions and the functionalities and structures of UV-curable acrylate monomers was investigated. With an increase in the proportions of monofunctional monomers, the adhesion abilities of UV-curable alumina suspensions enhanced because of reduced volume shrinkage, however, inferior curing performances were observed due to a decrease in the double bond densities. Furthermore, the large-volume branched chain structures in monofunctional monomers and ethyoxyl groups in polyfunctional monomers effectively decreased the volume contraction, improving the adhesion performances of UV-curable alumina suspensions and facilitating the conversion of double bonds to provide excellent curing properties, further guaranteeing strong adhesion of these suspensions to the substrate.     

Experimental study on the permeability and self-healing capacity of geosynthetic clay liners in heavy metal solutions

Geosynthetic clay liners (GCLs), which have a very low permeability to water and a considerably high self-healing capacity, are widely used in liner systems of landfills. In this study, a series of experimental tests were carried out under complex conditions on typical commercial GCLs from China. In particular, the effects of pH values and lead ions (Pb²⁺) were tested in addition to other factors. The swelling properties of natural bentonite encapsulated between geotextile components in the GCLs were tested first. The swelling capacity was reduced rapidly at pH values < 3 and concentrations of Pb²⁺ >40 mM. Permeability tests on GCLs with different concentrations of lead ions were then performed by using the self-developed multi-link flexible wall permeameter, and data showed that increases in lead ion concentrations greatly improved the permeability. Finally, self-healing capacity tests were conducted on needle-punched GCLs under different levels of damage. Results showed that the GCLs have a good self-healing capacity with small diameter damage holes (2 mm, close to three times the original aperture), but with a damage aperture larger than 15% of the sample area, the self-healing capacity could not prevent leakage; hence, in certain situations it will be necessary to repair the damage to meet the anti-seepage requirement.     

Critical state model for structured soil

Structure is an evident determinant for macroscopic behaviors of soils. However, this is not taken into account in most constitutive models, as structure is a rather complex issue in models. For this, it is important to develop and implement simple models that can reflect this important aspect of soil behavior. This paper tried to model structured soils based on well-established concepts, such as critical state and sub-loading. Critical state is the core of the classic Cam Clay model. The sub-loading concept implies adoption of an inner (sub-loading) yield surface, according to specific hardening rules for some internal strain-like state variables. Nakai and co-workers proposed such internal variables for controlling density (ρ) and structure (ω), using a modified stress space, called t_ij. Herein, similar variables are used in the context of the better-known invariants (p and q) of the Cam Clay model. This change requires explicit adoption of a non-associated flow rule for the sub-loading surface. This is accomplished by modifying the dilatancy ratio of the Cam Clay model, as a function of the new internal variables. These modifications are described and implemented under three-dimensional (3D) conditions. The model is then applied to simulating laboratory tests under different stress paths and the results are compared to experiments reported for different types of structured soils. The good agreements show the capacity and potential of the proposed model.     

玉门减压深拔减五线生产微晶蜡的工艺研究及应用

对玉门减压深拔减五线生产微晶蜡的工艺进行了研究并进行了工业应用,生产结果表明:以减压深拔减五线为原料经酮苯脱蜡脱油、白土精制生产微晶蜡,操作过程平稳,酮苯脱蜡脱油过程过滤速度较快,脱蜡油和粗蜡的平均收率可达到78.24%。微晶蜡产品质量符合SH/T 0013-1999标准要求。     

酮苯脱蜡装置用加氢裂化尾油生产优质白油料

加氢裂化尾油经酮苯脱蜡和白土精制工艺可生产高质量润滑油基础油.该基础油具有很好的低温流动性能,且对添加剂感受性好,硫、氮含量低,饱和烃含量高,可以调合中、高档润滑油,制备白油.加氢裂化尾油的综合利用具有明显的经济效益.     

忠武输气管道悬索跨越设计创新及探讨

忠武输气管道有4次悬索跨越,分别是蚂蝗溪悬索跨越、木龙河悬索跨越、马水河悬索跨越、野三河悬索跨越。文章介绍了这几座悬索跨越管桥设计中采用的多项新技术,如采用热聚乙烯半平行钢丝索代替以往的钢丝绳;采用钢管塔架代替以往的角钢塔架;根据地形地貌特点变换风索型式或取消塔架等。这些新技术、新设计在工程中均取得了良好的效果。另外,文章还针对悬索跨越桥面结构型式、预拱度设置、不对称荷载的影响、风索基础的设置等问题进行了探讨。     

含混合金属的羟基镍铝交联蒙托石的合成

用两种方法——取代法和共聚法合成了一系列羟基镍铝交联蒙托石(GNiAl-CLM和NiAl-CLM),首次利用两种方法,交联前和交联后高温老化处理,对交联蒙托石的热稳定性进行改进。结果表明:取代法合成的羟基镍铝交联蒙托石具有均一的(001)面衍射,底面间距d(001)值均为1.8nm左右,而共聚法合成的羟基镍铝交联蒙托石出现两个(001)面衍射,d(001)值分别为1.8nm和1.55nm;高温处理后,热稳定性得到明显改进,热稳定性可高达700℃以上。