叠栅图在碳化物沉淀相研究中的一些应用

借助于叠栅图观察了合金钢中细小沉淀相的形貌和分布特征，确定了沉淀相的点阵常数及其同母相（或另一沉淀相）的错配度，并确认了沉淀相或母相中存在的位错及其滑移面。     

A new precipitate phase in Al-4wt. % Cu thin-film interconnects

We report here the identification of a new precipitate phase in thin-film Al-4wt.%Cu metallization used for interconnects on integrated circuits. The phase is based on a trigonal distortion of a face centered cubic lattice. Computer simulation of electron diffraction intensities suggests that the basis structure is isomorphous with Al₂Ca but with a large and ordered population of vacancies on Cu sites. The reason for the formation of the new phase and its implications for electromigration reliability are discussed.     

控轧控冷工艺对高强度锚杆钢组织和性能的影响

随着矿井深度的增加,对锚杆支护强韧性的要求越来越高,为了应对这一情况,需要研发出更高强度的锚杆钢。利用锚杆钢研究了轧制工艺、冷却工艺与珠光体、铁素体相比例,析出相析出行为及力学性能的关系。研究结果表明,在中轧后、精轧前采用适当水冷+回复段处理的复合工艺可使晶粒更细小、组织更均匀。对超高强度锚杆钢进行热压缩变形试验,由热模拟试验结果确定相转变温度为A_c1=737 ℃、A_c3=886 ℃。最终筛选出入精轧温度为810 ℃、回复段温度为800 ℃时,可获得的晶粒尺寸达4 μm,珠光体体积分数为66.8%,铁素体体积分数为33.2%,珠光体片层间距达200 nm;另外调整V、Cr、N等析出以提高锚杆钢的强韧性,较低的回复温度有利于细小、弥散、V(C/N)析出相的析出,V(C/N)的析出可进一步改善锚杆钢的力学性能。由该控轧控冷工艺轧制的锚杆钢屈服强度为780 MPa、抗拉强度为930 MPa、硬度为291HV、伸长率为20%。     

含Li的Al-Zn-Mg-Cu合金沉淀析出过程的定量分析

应用小角度X射线散射技术结合TEM分析定量的描述Al-Zn-Mg-Cu-Li合金时效过程中析出相尺寸分布和形貌等信息。通过分析确定合金在几种时效状态下析出相为轴比在0．2～0．4之间的扁回转椭球形。确定了析出相特征尺寸的对数正态分布和质量依回转半径的Maxwell分布。并分析分布曲线随动力强度Ks的变化特征，可以看出，析出相尺寸和质量分布曲线基本满足随动力强度增加，几何平均值增加，分布范围变宽。     

New Process for the Preparation of Monodispersed, Spherical Silica Particles

A new method is presented for preparing highly monodispersed silica particles using a two-stage semibatch/batch hydrolysis reaction of Si(OC₂H₅)₄. The slower rate of hydrolysis of the tetraethylorthosilicate (TEOS) that occurred during the semibatch process resulted in larger silica particles with a higher yield and narrower size distribution. This was in direct contrast to the batch process. In addition, the ability of four different mixed processes to produce silica particles with good packing density, narrower particle-size distribution, and higher yield were evaluated. These were batch/batch (B-B), batch/semibatch (B-S), semibatch/batch (S-B), and semibatch/semibatch (S-S) processes. The S-S system produced the largest particles with the highest yields. The size of the silica particles obtained by the S-B method decreased with increasing reaction time, while the particles obtained by the B-S process had the best particle-size distribution and packing density. In conclusion, a mixed batch/semibatch system was the best way to produce an extremely narrow particle-size distribution and a good packing density.     

坝体坝基渗水及其析出物对大坝影响分析

坝基坝体渗水对大坝安全运行有不利影响。本文采用现场检查、水样试验、析出物试验、资料分析等手段,对碾压混凝土坝运行期渗水及其析出物对大坝的影响进行了较全面的分析,并提出了运行期需关注的问题。     

Fabrication of NiO Nanoparticle-Coated Lead Zirconate Titanate Powders by the Heterogeneous Precipitation Method

NiO nanoparticle-coated lead zirconate titanate (PZT) powders are successfully fabricated by the heterogeneous precipitation method using PZT, Ni(NO₃)₂·6H₂O, and NH₄HCO₃ as the starting materials. The amorphous NiCO₃·2Ni(OH)₂·2H₂O are uniformly coated on the surface of PZT particles. XRD analysis and the selected-area diffraction (SAD) pattern indicate that the amorphous coating layer is crystallized to NiO after being calcined at 400°C for 2 h. TEM images show that the NiO particles of ∼8 nm are spherical and weakly agglomerated. The thickness of the nanocrystalline NiO coating layer on the surface of PZT particle is ∼30 nm.     

Fe-9.7Cr-2.65Mn-xC-0.22V-2W-0.1Ta-1.5Si-yN马氏体耐热钢相图计算

利用Thermo-Calc软件和相关数据库对Fe-9.7Cr-2.65Mn-xC-0.22V-2W-0.1Ta-1.5Si-yN马氏体耐热钢随N含量变化的相分数进行计算。结果发现,当保持x+y=0.24wt.%时,随着N的质量分数从0.015增加到0.10wt.%时,相图没有发生实质性的变化;但对室温组织和碳化物Cr23C6、TaC和VN的析出产生了显著的影响,从而改变了Fe-9.7Cr-2.65Mn-xC-0.22V-2W-0.1Ta-1.5Si-yN马氏体耐热钢奥氏体化后的析出序列。当N含量升高到0.085wt.%时,出现了新相Cr2N。XRD及萃取实验结果与计算相符。这些计算结果可为Fe-9.7Cr-2.65Mn-xC-0.22V-2W-0.1Ta-1.5Si-yN马氏体耐热钢的成分设计、热处理工艺设计和显微组织观察等提供依据。     

REACTIVE DIFFUSION BETWEEN Si AND NbC AT 1300℃

ＲＥＡＣＴＩＶＥＤＩＦＦＵＳＩＯＮＢＥＴＷＥＥＮＳｉＡＮＤＮｂＣＡＴ１３００℃Ｃ．Ｒ．Ｋａｏ（ＤｅｐａｒｔｍｅｎｔｏｆＣｈｅｍｉｃａｌＥｎｇｉｎｅｅｒｉｎｇＮａｔｉｏｎａｌＣｅｎｔｒａｌＵｎｉｖｅｒｓｉｔｙＣｈｕｎｇＬｉ，Ｔａｉｗａｎ）Ｊ．Ｗｏｏｄｆ...