铁锈渣对氧气生产的危害

介绍铁锈、铁锈渣对氧气生产的危害 ,分析一起因铁锈、铁锈渣引起的氧压机着火而殃及氧气囊燃烧的事故 ,针对分析的原因提出预防措施。     

Taxonomy for protective ability of rust layer using its composition formed on weathering steel bridge

For a quantitative evaluation of the protectiveness of a rust layer formed on a weathering steel bridge, the relationship between the corrosion rate of the bridge and the composition of the rust layers formed on the girders was first investigated. These corrosion rates were clearly classified by the protective ability index (PAI) of α/γ^∗ and (β + s)/γ^∗, where α, γ^∗, β and s are the mass ratio of crystalline α-FeOOH, the total of γ-FeOOH, β-FeOOH and the spinel-type iron oxide (mainly Fe₃O₄), β-FeOOH and spinel-type iron oxide, analyzed by XRD, respectively. The inequality of the former index α/γ^∗ > 1 expressed the protectiveness criterion of the rust layer, while that of the latter index, (β + s)/γ^∗< 0.5 or > 0.5, classified the corrosion rate of the non-protective rust layer. The PAI is useful for a quantitative evaluation of the protectiveness of a rust layer formed on a weathering steel bridge and is an important item for the corrosion assessment of the bridge.     

The effects of water pollution on the immersion corrosion of mild and low alloy steels

The short-term immersion corrosion of mild and low alloy steels in seawaters is known to be proportional to the concentration of dissolved oxygen (DO) in the bulk water. Longer-term corrosion is a function of the activity of sulphate-reducing bacteria and is influenced by the concentration of nutrients in the bulk water. These influences are examined in more detail for the corrosion of steels in the brackish waters of the River Thames and for several immersion corrosion sites on the Eastern Australian seaboard and in the North Sea. The published data sources were supplemented with plausible assumptions about environmental conditions. New interpretations of the data are provided based on the previously published model for immersion corrosion. For waters with negligible salinity and sulphate levels early corrosion loss was shown to depend on the dissolved oxygen content of the waters, and later corrosion loss was a direct function of nitrogenous nutrient (pollution) levels. This also applies to longer-term corrosion.     

Indoor atmospheric corrosion in Cuba. A report about indoor localized corrosion

Indoor weight loss of steel, chloride, sulphur compounds and dust deposition rate were determined in six storehouses having different characteristics. Relative humidity and temperature were determined in three storehouses. A model for indoor corrosion of steel depending on time of exposure and deposition of dust, sulphur compounds and chlorides is proposed. Dust deposition plays an important role indoors. The position of the sample has also a significant influence on corrosion. Indoor corrosion aggressivity in Cuban storehouses ranges in classification IC3 and IC4 according to the new ISO proposal of indoor aggressivity.A report about the presence of localized corrosion indoors (filiform like) using a special designed sample is made.     

玻璃钢筋混凝土的有限元计算与试验

钢筋混凝土广泛应用于土木工程领域，但其结构耐久性因钢筋本身的锈蚀成为现今急待解决的问题。人们一直在寻找对钢筋混凝土进行改良的途径，用玻璃钢筋代替普通钢筋是解决这一问题的一个有效的方法，为此进行了试验和ANSYS有限元分析，结果证明此法具有可行性。     

In situ observation of initial rust formation process on carbon steel under Na2SO4 and NaCl solution films with wet/dry cycles using synchrotron radiation X-rays

Atmospheric corrosion of steel proceeds under thin electrolyte film formed by rain and dew condensation followed by wet and dry cycles. It is said that rust layer formed on steel as a result of atmospheric corrosion strongly affects the corrosion behavior of steel. The effect of environmental corrosiveness on the formation process and structure of the rust layer is, however, not clear to date. In this study, in situ observation of the rusting process of a carbon steel covered with a thin film of Na₂SO₄ or NaCl solution was performed under a wet/dry repeating condition by X-ray diffraction spectroscopy with white X-rays obtained from synchrotron radiation. The present in situ experiments successfully detected initial process of the rust formation. In the early cycles, the rust constituents were not well crystallized yet, but the presence of Fe(OH)₂ and Fe(OH)₃ was confirmed. In the subsequent cycles, two different solutions resulted in difference in preferential phase of the rust constituents. α-FeOOH was preferentially formed in the case of the Na₂SO₄ solution film, whereas β-FeOOH appeared only under the NaCl solution film.     

磷酸镁水泥在工程结构中的修复加固研究进展

综述了近年来磷酸镁水泥(MPC)作为修复加固材料的研究进展,介绍了在工程结构中MPC的修复、加固及防锈作用,并解释了其修复、加固作用的原理及应用效果,还指出了目前存在的问题和今后的研究趋势.     

Enhancement the Adhesion between Epoxy Coating and Rusted Structural Steel by Tannic Acid Treatment

An eco-friendly rust converter treatment based on tannic acid was optimized by orthogonal experiment, and the adhesion of the epoxy top-coating system was evaluated. The results showed that the adhesion between the epoxy coating and the rusted steel after treatment was enhanced from 1.93 to 5.97 MPa. This adhesion improvement was attributed to the formation of the micro-cracked tannic conversion layer and the increase of the compactness of the rust layer. The failure analysis suggested that the remainder rust was still the key issue for the further adhesion improvement of the coating system.     

环保型水溶性带锈防锈涂料的研制

为省去除锈除油等表面预处理工序，以简化涂漆工艺，减轻劳动强度，降低涂装成果，采用改性脲醛树脂作为水溶性带锈涂料的成膜物与转化液的最佳配比，研制出一种环保型水溶性带锈防锈涂料，较好地解决了水溶性带锈涂料耐水性和装饰性差的问题。     

油罐空气泡沫产生器立管清扫口的设计补充建议

石油储罐空气泡沫产生器的立管设计中,规定在管下部设锈渣清扫口,但没有具体尺寸的规定,形成了五花八门的现状,以致于有的企业在火灾扑救时出现问题,本文对锈渣清扫口设计提出具体补充意见。