乙烯齐聚是合成直链低碳α-烯烃最先进的方法，直链低碳α-烯烃可用于生产低密度聚乙烯和高密度聚乙烯等多种精细化学品。本文综述了乙烯齐聚催化体系的研究进展，重点介绍了镍、锆、钛催化剂的组成以及反应时间、反应温度、溶剂、助催化剂等因素对乙烯齐聚活性和选择性的影响，并讨论了典型镍的催化机理。     

Al、Mo含量对铸造钛合金力学性能的影响

运用正交实验 ,考察了Al、Mo含量对Ti Al Mo 1Zr系铸造钛合金力学性能的影响。试验结果表明 :随Al、Mo含量提高 ,铸造合金的强度增加 ,塑性和冲击韧性降低 ,但Al、Mo的交互作用却使合金塑性提高 ,强度和冲击韧性降低     

Mechanical spectroscopy in commercial Fe–6 wt.% Si alloys between 400 and 1000 K

Mechanical spectroscopy, neutron diffraction and differential scanning calorimetry (DSC) were performed on commercial Fe–6 wt.% Si alloy after quenching from high temperature. The damping spectrum shows a peak at around 800 K and an associated modulus defect. The modulus shows an increase during the second and subsequent heating runs. In addition, an anomaly in the modulus behavior has been found at around 400 K. Different thermal treatments allows to obtain two different recovery degrees of the quenched-in defects. The influence of the recovery degree on the 800 K internal friction peak and on the anelastic modulus has been evaluated and confirm the validity of the grain boundary mechanism associated to this peak. Experimental results are discussed on the basis of recovery and ordering processes.     

Formation and growth mechanism of TiC crystal in TiC_p/Ti composites

1　ＩＮＴＲＯＤＵＣＴＩＯＮＰａｒｔｉｃｌｅｓｒｅｉｎｆｏｒｃｅｄｔｉｔａｎｉｕｍａｌｌｏｙｍａｔｒｉｘｃｏｍｐｏｓｉｔｅｓ(ＴＭＣｐ)ｈａｖｅｗｉｄｅａｐｐｌｉｃａｔｉｏｎｆｉｅｌｄｓｆｏｒｔｈｅｉｒａｔｔｒａｃｔｉｖｅｈｉｇｈｓｐｅｃｉｆｉｃｓｔｒｅｎｇ     

Ionic transport in amorphous anodic titania stabilised by incorporation of silicon species

Incorporation of silicon species from an alloy substrate into anodic titania is shown to stabilise the structure of the film, facilitating investigation of the ionic transport processes in amorphous titania grown at high efficiency. Thus, an amorphous anodic film developed on a sputtering-deposited Ti-6 at.%Si alloy formed to 100 V in phosphoric acid electrolyte in contrast to a partially crystalline film developed on relatively pure titanium at <20 V. Silicon species, which are immobile and act as marker species in the growing film, are present in the inner 58% of the film thickness. Evidently, the film material forms simultaneously at the film/electrolyte and alloy/film interfaces by co-operative transport of cations and anions, as is usual in amorphous anodic oxides. The phosphate anions incorporated from the electrolyte migrate inward at 0.34 times the rate of O²⁻ ions and hence are present in the outer 62% of the film thickness.     

Chemical leaching and magnetic properties of non-equilibrium Al(Co–Cu) powders produced by rod milling

We report upon the chemical leaching and magnetic properties of nanoscale crystalline Al_0.6(Co₂₅Cu₇₅)_0.4 alloy powders produced by rod milling. X-Ray diffractometry (XRD), transmission electron microscopy, differential scanning calorimetry, vibrating sample magnetometry, and superconducting quantum interference device magnetometry were used to characterize the as-milled and leached specimens. After 400 h of milling, only the b.c.c. phase of the intermetallic compound γ-Al_3.892Cu_6.10808 was detected by XRD. After annealing the leached specimen at 600 °C for 1 h, the nanoscale crystalline phase was transformed into the f.c.c. Cu phase, and this was accompanied by a change in the magnetic properties. The peaks of the magnetization shifted towards lower temperature with increasing external field. The temperature behavior at T_f (45 K) for direct current (d.c.) magnetic susceptibility measurements was quite different for field cooling and zero-field cooling. After cooling the leached specimen from 800 °C, magnetization increased gradually.     

The corrosion behavior of sputter-deposited aluminum-tungsten alloys

Thin films on aluminum-tungsten alloys were prepared by co-deposition of pure aluminum and pure tungsten, each sputtered by an independently controlled magnetron source, on glass and sapphire substrates. Completely amorphous films were obtained in the Al₈₀W₂₀-Al₆₇W₃₃ composition range. Passivity and corrosion behavior of amorphous Al-W alloys were investigated in 1 M deaerated hydrochloric acid solution using polarization and impedance spectroscopy measurements and have been correlated with the properties of pure alloy components. Tungsten and sputter-deposited Al-W thin films are inherently passive materials while aluminum undergoes pitting corrosion in hydrochloric acid solution. The passive film formed at the OCP on each alloy possesses excellent electric and dielectric properties comparable to those of the isolating film on tungsten. The absolute impedance increases with increasing tungsten content in the alloy. According to electrochemical polarization measurements, alloying Al with W in solid solution significantly enhances the material's resistance to pitting corrosion by shifting the breakdown potential above 2000 mV (Al₆₇W₃₃) and lowering the corrosion rate at the OCP by more than two orders of magnitude. The most likely mechanism explaining the passivity of amorphous Al-W alloys, the Solute Vacancy Interaction Model (SVIM), involves the formation of complexes between highly oxidized solute atoms (W⁺⁶) and mobile cation vacancies, which restrict the transport of Cl⁻ through the oxide film and inhibit its breakdown in hydrochloric acid solution. The role that film stress relaxation effects and microscopic defects in amorphous Al-W films, of the some composition, and deposited on various substrates play in their corrosion resistance is discussed.     

MB8镁合金薄板的搅拌摩擦焊

针对我国航空航天工业常用的MB8镁合金。采用搅拌摩擦焊工艺进行焊接，对其焊缝的成形特点、组织特征和力学性能进行分析。结果表明，采用搅拌摩擦焊焊接镁合金效果良好。     

β21s高强度钛合金的铣削试验研究

针对一种新型的难加工钛合金材料β21s,进行了刀具磨损试验和铣削力的测量试验,对材料的切削加工性进行评价,并且给出优选结果,为实际生产提供参考。     

用硫酸铁铵容量法测定钛精矿中二氧化钛含量

样品在过氧化钠熔融、水浸取及盐酸酸化后，在盐酸和硫酸介质中，隔绝空气，用金属铝将钛(Ⅳ)还原至钛(Ⅲ)，以硫氰酸盐为指示剂，用硫酸铁铵标准溶液滴定。