Zn-Ni合金共沉积影响机理的拉曼光谱研究

首次利用现场表面增强拉曼光谱研究了Zn-Ni合金共沉积的机理。通过研究Ni电极在NiCl2溶液与纯水中的拉曼光谱、Ni电极与Au电极在KCl溶液中的拉曼光谱以及这2种电极在NiCl2溶液中现场电沉积的拉曼光谱,并根据前人提出的理论,得出如下结论:Zn-Ni合金共沉积中存在着较易在电极表面放电的NiClad,使Ni沉积的过电位降低,促进了Ni的沉积,导致Zn的异常共沉积。     

Development of compositionally modulated multilayer Zn-Ni deposits as replacement for cadmium

Compositionally modulated multilayer (CMM) Zn-Ni deposits were electrodeposited from single acidic bath (pH = 4.7) by using a potentiostatic sequence. The Zn and Ni composition in the alloy was tailored as a function of distance from the steel substrate. X-ray diffraction studies of the deposit showed the presence of γ-phase with a composition of Ni₅Zn₂₁. The corrosion properties of modulated multilayer coatings were studied in 5% NaCl solution using electrochemical corrosion techniques. The polarization resistance of the deposits varied as a function of Ni content between 1700 and 3440 Ω. CMM Zn-Ni with 20 wt% Ni exposed in ASTM B117 salt spray test did not show any red rust formation after 400 h.     

DCOIT复合Zn-Ni合金抗菌镀层的制备及其耐SRB腐蚀性能研究

目的 提高Zn-Ni合金镀层的耐微生物腐蚀性能。方法 在硫酸盐电镀液中添加梯度浓度的4,5-二氯-N-辛基-4-异噻唑啉-3-酮（DCOIT）,利用恒电流沉积方法,在碳钢表面阴极电沉积获得DCOIT复合Zn-Ni合金镀层。通过电沉积电位监测与电流效率计算评价DCOIT对电沉积过程的影响,利用扫描电子显微镜、电子能谱、X射线晶体衍射等研究DCOIT对Zn-Ni复合镀层形貌、结构与Ni含量的影响,使用傅里叶红外吸收光谱和荧光显微观察法验证DCOIT的成功复合及复合镀层的抗菌性能,最后将DCOIT复合Zn-Ni合金镀层暴露于硫酸盐还原菌（SRB）中,监测菌液的pH与菌体浓度,同时计算镀层的腐蚀速率,并观察镀层的腐蚀形貌,评价复合镀层的耐SRB腐蚀性能。结果 DCOIT在电沉积过程中会吸附在沉积表面,造成沉积电位负移,并略微降低了电流效率。DCOIT的添加显著改变了复合镀层的形貌、结构与Ni含量,其Ni含量与DCOIT的添加量呈线性增长关系,导致其晶体结构转变。DCOIT以有效形式存在于复合Zn-Ni合金镀层中,并显示出抗菌性能,DCOIT添加量为2 mmol/L时,镀层中的复合量最高,抗菌性能最好。最后,DCOIT复合Zn-Ni合金镀层能有效抑制环境中SRB的生长与代谢,自身腐蚀速率减慢,耐蚀性能明显增强。结论 DCOIT能够以有效形式复合于Zn-Ni合金镀层内部,并有效提高了镀层的抗菌性能,使其获得增强的耐SRB腐蚀性能。     

聚乙二醇-600对酸性Zn-Ni合金的电沉积行为及镀层耐蚀性影响的研究

采用循环伏安(CV)曲线研究了聚乙二醇-600 (PEG-600)在酸性Zn-Ni合金基础镀液中对Zn-Ni合金电沉积行为的影响;采用电化学阻抗谱(EIS)、动电位极化曲线与表面形貌分析方法研究了酸性Zn-Ni合金基础镀液中,聚乙二醇-600的浓度对Zn-Ni合金镀层表面微观形貌及耐蚀性的影响.结果 表明,PEG-60...     

Electrochemical studies of Zn-Ni alloy coatings from non-cyanide alkaline bath containing tartrate as complexing agent

The Zn-Ni alloys have been electro-deposited from a non-cyanide alkaline bath containing tartrate as a complexing agent for Ni²⁺ ions. A water soluble polymer is used as a brightener. It was prepared by the reaction of epiclorohydrin with hexamethylenetetramine and mercaptobenzimidazol. Its effect on co-deposition process was examined. It was found that adding brightener in plating bath has a great effect on the cyclic voltammogram and galvanostatic measurements during the electrodeposition. Under the examined conditions, the electrodeposition of the alloys was of anomalous type. X-ray diffraction measurements revealed that the alloys consisted δ-phase (Ni₃Zn₂₂). The composition and morphology of the deposits were also studied by using scanning electron microscopy (SEM) and energy dispersive analysis X-ray (EDAX), respectively. The effect of optimum plating bath conditions on the corrosion resistance is studied by Tafel polarization.     

电镀Zn-Ni和化学镀Ni-P交替镀层的抗腐蚀性能

为了提高铸钢基体的耐腐蚀、耐磨性能，通过在铸钢基体上沉积化学镀Ni-P和电镀趾Ni的交替镀层的方法获得了一系列多层镀层。考察了多层镀层的外观和在5％NaCl中的抗腐蚀性能。研究表明，化学镀Ni-P在电镀趾Ni层上的沉积以及在铸钢基体上沉积Zn-Ni与Ni-P的交替镀层是可行的；所有交替镀层的耐腐蚀性优于相同厚度的Ni-P化学镀层；亚层厚度为1μm和2μm的交替镀层比相同厚度的Zn-Ni单层镀层的耐腐蚀性更为可靠；镀层厚度相同且Ni-P亚层的厚度超过0．5μm时，交替镀层的耐腐蚀性随着层数和Zn-Ni亚层厚度的增加而增加，这主要是多层效应的结果；在长达1a的浸泡腐蚀试验期同，所有镀层的外观都是令人满意的，都没有出现鼓泡和剥裂现象。     

碱性锌-镍合金镀液及镀层中锌、镍的测定

酸性锌-镍合金镀液中锌、镍的测定方法报道很多，而碱性镀液中锌、镍的测定报道很少。采用过硫酸铵作氧化剂，在碱性介质中，镍与丁二酮肟生成红色络合物借此比色，求出镍含量；用EDTA滴定法确定锌、镍总量，然后减去镍量从中得到锌含量。此方法也可用于镀层中的锌及镍测定。本方法测定结果准确、快速，能满足实际生产的要求。     

镁合金化学镀镍前浸镀锌-镍合金的研究

研究了镁合金表面无氰浸镀锌-镍合金后直接化学镀Ni-P合金新工艺.分析了化学镀Ni-P合金镀液主盐质量浓度、还原剂质量浓度、镀液pH及温度对镀速和镀层耐蚀性的影响.结果表明:本工艺可以在镁合金表面获得均匀致密的浸镀层,最终得到的化学镀镍层硬度高,具有良好结合力和耐腐蚀性能.     

高强钢电镀低氢脆Zn-Ni合金工艺的研究

研究了弱酸性氯化钾-乙酸铵体系电镀Zn-Ni合金工艺,开发了适于本体系的光亮剂,深入探讨了镀液组成及工艺条件对镀层组成的影响,获得全光亮Zn-Ni合金镀层的最佳工艺.在最佳工艺条件下,镀层中镍的质量分数约为13%,主要由γ相Ni5Zn21组成.缺口试样持久拉伸试验及镀件中氢的质量分数测试表明:Zn-Ni合金镀层具有较低的氢脆性,适合于高强钢的电镀.     

温度对Zn-Ni一次电池性能的影响

介绍了用Zn作负极活性物质、自制NiOOH作正极活性物质制成的圆柱形环式ZR6型Zn—Ni一次电池的常温和低温放电性能,并与碱性Zn—MnO2电池作了对比。实验结果表明：常温(约25℃)500mA恒电流放电至1．10V,Zn—Ni电池容量为碱性Zn—MnO2电池的2倍;-15℃时为碱性Zn—MnO2电池的5倍。