Localized corrosion of (lean) duplex stainless steels in immersion units of urban wastewater treatment plants

With lower alloying cost and higher mechanical properties, lean duplex stainless steels can be an alternative to the more commonly used austenitic stainless steels. However, these alloys are still not the preferred choice, probably due to a lack of field experience. A study was thus initiated in view of defining the limits of use of selected (lean) duplexes for urban wastewater treatment units. The present paper shows the localized corrosion performance of selected lean duplexes in chloride contaminated solutions. The results are compared with austenitic S30403 and S31603 and with the more standard duplexes S82441 and S32205. The effect of welding was also investigated. Exposures in field municipal wastewater plants were conducted for 1 year in low and high chloride content units. The results show that lean duplexes S32101 and S32202 can be used as alternatives to S30403 and S31603 in low chloride electrolytes. At 500 ppm of chloride content, duplex stainless steel S32304 showed better corrosion resistance than S30403 and S31603. For higher chloride contents (1000 ppm and above) the standard duplexes S82441 and S32205 shall be preferred.     

施工中电焊机的安全使用简述

从电焊机自身电气特点及建筑工地工作环境入手,探讨电焊机安全技术的实施方法。分析电焊机安全隐患及事故的分类以及电焊机在使用过程中产生危险的原因。介绍电焊机在安装以及作业过程中的安全措施。     

Effect of Li2O on the crystallization behavior of CaO-Al2O3-SiO2-Li2O-Ce2O3 mold slags

The effect of Li₂O on the crystallization properties of CaO-Al₂O₃-SiO₂-Li₂O-Ce₂O₃ slags was investigated. With increasing the Li₂O content, LiAlO₂ and CaCeAlO₄ were the main crystalline phases. LiAlO₂ formed for the charge compensating of Li⁺ ions to [AlO₄^5?]-tetrahedrons, and CaCeAlO₄ formed as a result of the charge balance of Ce³⁺ ions, Ca²⁺ ions, and [AlO₆^9?]-octahedrons. Increasing the content of Li₂O to 10%, the crystallization temperature was the highest, and the incubation time was the shortest. The crystallization ability was strong due to the three factors of strengthening the interaction between ions and ion groups, decreasing the polymerization degree, and increasing the melting temperature. Further increasing the content of Li₂O, the crystallization performance was obviously suppressed, because the melting temperature and the force between the cations and the anion groups decreased.     

Linear friction welding of Ti6Al4V: experiments and modelling

Linear friction welding of the Ti6Al4V alloy is studied. A new definition of the energy input rate is proposed, based on an integration over time of the in-plane force and velocity; a strong correlation with the upset rate is then found. The effective friction coefficient is estimated to be 0·5±0·1 for varying frequencies and amplitudes, with only a weak dependence on the processing conditions displayed. A model is proposed that accounts for both the conditioning and equilibrium stages of the process, which is shown to be in good agreement with the experimental data. The model is used to study the mechanism by which the flash is formed. A criterion is proposed by which the rippled nature of its morphology can be predicted.     

Process and joint quality of ultrasonic vibration enhanced friction stir lap welding

In order to improve the process effectiveness and joint quality, ultrasonic vibrations were integrated with friction stir lap welding. Effect of ultrasonic exertion on the process and joint quality of AA 6061-T6 were investigated. Upon ultrasonic exertion, joints owned larger effective lap width, shorter hooks and improved strength. Weld fracture mode changed from a ductile–brittle mixed mode to a more ductile mode while the fracture path shifted from lap interface to beyond the stir zone. Material flow and interface defects were characterised using lap welded dissimilar aluminium alloy joints. Ultrasonic vibration improved the material flow and reduced the interfacial defects. Variations in failure load of joints were found in accordance with the variations in material flow and interfacial defects.     

Improving weld formability by a novel dual-rotation bobbin tool friction stir welding

A novel dual-rotation bobbin tool friction stir welding (DBT-FSW) was developed, in which the upper shoulder (US) and lower shoulder (LS) have different rotational speeds. This process was tried to weld 3.2 mm thick aluminum-lithium alloy sheets. The metallographic analysis and torque measurement were carried out to characterize the weld formability. Experimental results show that compared to conventional bobbin tool friction stir welding, the DBT-FSW has an excellent process stability, and can produce the defect-free joints in a wider range of welding parameters. These can be attributed to the significant improvement of material flow caused by the formation of a staggered layer structure and the unbalanced force between the US and LS during the DBT-FSW process.     

二氧化碳气体保护焊在厚板上的应用

板厚为 5 5mm的 16Mn钢采用CO2 半自动气保焊建造大型转炉炉体的可能性和可靠性如何 ?目前尚缺少足够的试验数据。为了给转炉工程的施工焊接提供可靠数据 ,确保焊接质量 ,对板厚 5 5mm16Mn钢CO2 半自动的焊接性能进行了一系列的试验研究     

通信性能评估的仿真实验研究

研究了流量控制和差错控制对通信性能的综合影响，着重分析了停止-等待协议和连续ARQ协议的优缺点，讨论了信道利用率和帧长的关系。介绍了几种多点接人技术的基本原理，如CSMA和CSMA／CD，并给出了各自相应的性能仿真曲线。所设计的通信性能评估实验，仿真界面形象丰富，与实验知识点紧密结合，可以大大提高实验教学的效率和质量。     

Estimation and Optimization of the Principal H-Maser Parameters

The scale along the coordinate axes in the equations of motion hitherto used for an H-maser (in relative units) is shown to depend on Q as the quality factor for an H-maser. This hinders both analysis of the operation of the H-maser and optimization of its parameters. The modified equations of motion proposed here do not have that shortcoming. We determine the atomic flux into the bulb that gives the H-maser the best metrological characteristics.     

热作模具钢表面激光堆焊耐磨合金层的研究

本文主要通过在H13钢上用大功率CO_2激光束进行堆焊,阐述了激光堆焊工艺变化对堆焊组织和性能的影响,在本试验条件下,得到了高密度弥散金属化合物组织的激光堆焊层,平均硬度为HV800,与基体呈冶金结合,耐磨性比H13模具钢提高149%。