Achieving superior hydrogen storage properties via in-situ formed nanostructures: A high-capacity Mg–Ni alloy with La microalloying

Mg-based hydride is a promising hydrogen storage material, but its capacity is hindered by the kinetic properties. In this study, Mg–Mg₂Ni–LaH_x nanocomposite is formed from the H-induced decomposition of Mg₉₈Ni_1·67La_0.33 alloy. The hydrogen capacity of 7.19 wt % is reached at 325 °C under 3 MPa H₂, attributed to the ultrahigh hydrogenation capacity in Stage I. The hydrogen capacity of 5.59 wt % is achieved at 175 °C under 1 MPa H₂. The apparent activation energies for hydrogen absorption and desorption are calculated as 57.99 and 107.26 kJ/mol, which are owing to the modified microstructure with LaH_x and Mg₂Ni nanophases embedding in eutectic, and tubular nanostructure adjacent to eutectic. The LaH_2.49 nanophase can catalyze H₂ molecules to dissociate and H atoms to permeate due to its stronger affinity with H atoms. The interfaces of these nanophases provide preferential nucleation sites and alleviate the “blocking effect” together with tubular nanostructure by providing H atoms diffusion paths after the impingement of MgH₂ colonies. Therefore, the superior hydrogenation properties are achieved because of the rapid absorption process of Stage I. The efficient synthesis of nano-catalysts and corresponding mechanisms for improving hydrogen storage properties have important reference to related researches.     

Performance of BaZrO3/Y2O3 dual-phase refractory applied to TiAl alloy melting

Vacuum induction melting is a potential process for the preparation of TiAl alloys with good homogeneity and low cost. But the crucial problem is a selection of high stability refractory. In this study, a BaZrO₃/Y₂O₃ dual-phase refractory was prepared and its performance for melting TiAl alloys was studied and compared with that of a Y₂O₃ refractory. The results showed the dual-phase refractory consisted of BaZr_1-xY_xO_3-δ and Y₂O₃(ZrO₂), exhibited a thinner interaction layer (30 μm) than the Y₂O₃ refractory (90 μm) after melting the TiAl alloy. Although the TiAl alloys melted in the dual-phase and Y₂O₃ refractory exhibited similar oxygen contamination (<0.1 wt%), the alloy melted in the dual-phase refractory had smaller Y₂O₃ inclusion content and size than that in the Y₂O₃ refractory, indicating that the dual-phase refractory exhibited a better melting performance than the Y₂O₃ refractory. This study provides insights into the process of designing highly stable refractory for melting TiAl alloys.     

Nickel‒cobalt bimetallic catalysts prepared from hydrotalcite-like compounds for dry reforming of methane

Ni–Co/Mg(Al)O alloy catalysts with different Co/Ni molar ratios have been prepared from Ni- and Co-substituted Mg–Al hydrotalcite-like compounds (HTlcs) as precursors and tested for dry reforming of methane. The XRD characterization shows that Ni–Co–Mg–Al HTlcs are decomposed by calcination into Mg(Ni,Co,Al)O solid solution, and by reduction finely dispersed alloy particles are formed. H₂-TPR indicates a strong interaction between nickel/cobalt oxides and magnesia, and the presence of cobalt in Mg(Ni,Co,Al)O enhances the metal-support interaction. STEM-EDX analysis reveals that nickel and cobalt cations are homogeneously distributed in the HTlcs precursor and in the derived solid solution, and by reduction the resulting Ni–Co alloy particles are composition-uniform. The Ni–Co/Mg(Al)O alloy catalysts exhibit relatively high activity and stability at severe conditions, i.e., a medium temperature of 600 °C and a high space velocity of 120000 mL g^?1 h^?1. In comparison to monometallic Ni catalyst, Ni–Co alloying effectively inhibits methane decomposition and coke deposition, leading to a marked enhancement of catalytic stability. From CO₂-TPD and TPSR, it is suggested that alloying Ni with Co favors the CO₂ adsorption/activation and promotes the elimination of carbon species, thus improving the coke resistance. Furthermore, a high and stable activity with low coking is demonstrated at 750 °C. The hydrotalcite-derived Ni–Co/Mg(Al)O catalysts show better catalytic performance than many of the reported Ni–Co catalysts, which can be attributed to the formation of Ni–Co alloy with uniform composition, proper size, and strong metal-support interaction as well as the presence of basic Mg(Al)O as support.     

Development of a H2-permeable Pd60Cu40-based composite membrane using a reverse build-up method

A new reverse build-up method is developed to fabricate an economical H₂-permeable composite membrane. Sputtering and electroplating are used for the formation of a membrane comprised of a 3.7-μm-thick Pd₆₀Cu₄₀ (wt.%) alloy layer and a 13-μm-thick porous Ni support layer, respectively. The H₂-permeation measurements are performed under the flow of a gaseous mixture of H₂ and He at 300–320 °C and 50–100 kPa of H₂ partial pressure. The H₂/He selectivity values exceed 300. The activation energy at 300–320 °C is 10.9 kJ mol⁻¹. The H₂ permeability of the membrane is 1.25 × 10⁻⁸ mol m⁻¹ s⁻¹ Pa^−0.5 at 320 °C after 448 h. The estimated Pd cost of the proposed membrane is approximately 1/8 of the cost for a pure Pd₆₀Cu₄₀ membrane. This study demonstrates that the proposed method allows the facile production of low-cost, Pd-based membranes for H₂ separation.     

基于面元素重排的三维网格模型数据隐藏算法

目的 为了解决目前三维数据隐藏算法不能兼顾无失真和盲提取的问题，提出一种新的完全无失真的三维网格模型数据隐藏盲算法。方法 首先使用混沌逻辑映射选择嵌入与提取模式，保证数据的安全性。然后利用面元素重排，完全不会造成三维模型失真的性质，通过不同嵌入模式规则对三角面元素进行重排，以嵌入秘密数据。接收端则可根据相应的提取模式规则提取秘密数据。结果 仿真结果与分析表明，该算法不会对三维模型造成任何失真，嵌入容量为每顶点2比特，且能抵抗仿射变换攻击、噪声攻击和平滑攻击等。结论 这种三维数据隐藏盲算法无失真，容量大、安全性高、鲁棒性强，适用于三维载体不容修改的情形，如军事、医学、秘密通信和版权保护等。     

Bifunctional nanoporous ruthenium-nickel alloy nanowire electrocatalysts towards oxygen/hydrogen evolution reaction

A class of ruthenium-nickel alloy catalysts featured with nanoporous nanowires (NPNWs) were synthesized by a strategy combining rapid solidification with two-step dealloying. RuNi NPNWs exhibit excellent electrocatalytic activity and stability for oxygen evolution reaction (OER) and hydrogen evolution reaction (HER) in which the RuNi-2500 NPNWs catalyst shows an OER overpotential of 327 mV to deliver a current density of 10 mA cm^?2 and the RuNi-0 NPNWs catalyst requires the overpotential of 69 mV at 10 mA cm^?2 showing the best HER activity in alkaline media. Moreover, the RuNi-1500 NPNWs catalyst was used as the bifunctional electrocatalyst in a two-electrode alkaline electrolyzer for water splitting, which exhibits a low cell voltage of 1.553 V and a long-term stability of 24 h at 10 mA cm^?2, demonstrating that the RuNi NPNWs catalysts can be considered as promising bifunctional alkaline electrocatalysts.     

Interfacial microstructure and mechanical properties of Ti3SiC2 ceramic and TC11 alloy joint diffusion bonded with a Cu interlayer

Reliable joints of Ti₃SiC₂ ceramic and TC11 alloy were diffusion bonded with a 50 μm thick Cu interlayer. The typical interfacial structure of the diffusion boned joint, which was dependent on the interdiffusion and chemical reactions between Al, Si and Ti atoms from the base materials and Cu interlayer, was TC11/α-Ti + β-Ti + Ti₂Cu + TiCu/Ti₅Si₄ + TiSiCu/Cu(s, s)/Ti₃SiC₂. The influence of bonding temperature and time on the interfacial structure and mechanical properties of Ti₃SiC₂/Cu/TC11 joint was analyzed. With the increase of bonding temperature and time, the joint shear strength was gradually increased due to enhanced atomic diffusion. However, the thickness of Ti₅Si₄ and TiSiCu layers with high microhardness increased for a long holding time, resulting in the reduction of bonding strength. The maximum shear strength of 251 ± 6 MPa was obtained for the joint diffusion bonded at 850 °C for 60 min, and fracture primarily occurred at the diffusion layer adjacent to the Ti₃SiC₂ substrate. This work provided an economical and convenient solution for broadening the engineering application of Ti₃SiC₂ ceramic.     

5A06-O aluminium–magnesium alloy sheet warm hydroforming and optimization of process parameters

The uniaxial tensile test of the 5A06-O aluminium–magnesium (Al–Mg) alloy sheet was performed in the temperature range of 20–300 °C to obtain the true stress–true strain curves at different temperatures and strain rates. The constitutive model of 5A06-O Al–Mg alloy sheet with the temperature range from 150 to 300°C was established. Based on the test results, a unique finite element simulation platform for warm hydroforming of 5A06-O Al–Mg alloy was set up using the general finite element software MSC.Marc to simulate warm hydroforming of classic specimen, and a coupled thermo-mechanical finite element model for warm hydroforming of cylindrical cup was built up. Combined with the experiment, the influence of the temperature field distribution and loading conditions on the sheet formability was studied. The results show that the non-isothermal temperature distribution conditions can significantly improve the forming performance of the material. As the temperature increases, the impact of the punching speed on the forming becomes particularly obvious; the optimal values of the fluid pressure and blank holder force required for forming are reduced.     

Investigation of corrosion properties with Ni–P/TiNO coating on aluminum alloy bipolar plates in proton exchange membrane fuel cell

Aluminum alloy bipolar plates have unique application potential in proton exchange membrane fuel cell (PEMFC) due to the characteristics of lightweight and low cost. However, extreme susceptibility to corrosion in PEMFC operation condition limits the application. To promote the corrosion resistance of aluminum alloy bipolar plates, a Ni–P/TiNO coating was prepared by electroless plating and closed field unbalanced magnetron sputter ion plating (CFUMSIP) technology on the 6061 Al substrate. The research results show that Ni–P interlayer improves the deposition effect of TiNO outer layer and increase the content of TiN and TiO_xN_y phases. Compared to Ni–P and TiNO single-layer coatings, the Ni–P/TiNO coating samples exhibited the lowest current density value of (1.10 ± 0.02) × 10^?6 A·cm^?2 in simulated PEMFC cathode environment. Additionally, potential cyclic polarization measurements were carried out aiming to evaluate the durability of the aluminum alloy bipolar plate during the PEMFC start-up/shut-up process. The results illustrate that the Ni–P/TiNO coating samples exhibit excellent stability and corrosion resistance.     

济阳坳陷下古生界潜山油气藏特征及成藏模式

济阳坳陷下古生界潜山具有多样性、复杂性的特点，潜山差异性的形成演化、油气成藏主控因素和控藏模式不明确，严重制约了该区潜山油气勘探。在潜山分类的基础上，综合利用系统恢复、分类对比和典型解剖等方法，揭示了济阳坳陷下古生界不同类型潜山的形成演化过程和油气成藏主控因素差异性，分类建立了油气成藏模式。研究表明，济阳坳陷下古生界主要发育高位新盖侵蚀残丘潜山、中位古盖拉张断块潜山、中位新古盖拉张剪切断块潜山、中位中古盖挤压拉张断块潜山和低位古盖拉张滑脱断块潜山5种潜山类型。不同类型潜山的形成演化和油气成藏各具特色，其中，高位新盖侵蚀残丘潜山的发育受隆升、侵蚀作用控制，油气成藏主要受控于油源和盖层条件，表现为"单向供烃、砂体-不整合岩溶体联合输导、残丘控藏"的成藏模式；中位古盖拉张断块潜山的发育受掀斜、断裂作用控制，油气成藏主要受控于储集条件，表现为"单向供烃、顺向断层输导、反向断层控藏"的成藏模式；中位新古盖拉张剪切断块潜山的发育受反转、翘倾和走滑切割作用控制，油气成藏主要受控于输导条件，表现为"多源供烃、断溶体立体输导、断裂控藏"的成藏模式；中位中古盖挤压拉张断块潜山的形成受强烈挤压、拉张滑脱作用控制，油气成藏主要受控于储集条件，表现为"多源供烃、断缝体输导、断褶控藏"的成藏模式；低位古盖拉张滑脱断块潜山的形成受强烈拉张滑脱作用控制，油气成藏主要受控于输导条件，表现为"顶部供烃、断缝体输导、断裂控藏"的成藏模式。