A highly active composite electrocatalyst Ni–Fe–P–Nb2O5/NF for overall water splitting

This work demonstrates a facile Nb₂O₅-decorated electrocatalyst to prepare cost-effective Ni–Fe–P–Nb₂O₅/NF and compared HER & OER performance in alkaline media. The prepared electrocatalyst presented an outstanding electrocatalytic performance towards hydrogen evolution reaction, which required a quite low overpotential of 39.05 mV at the current density of ?10 mA cm^?2 in 1 M KOH electrolyte. Moreover, the Ni–Fe–P–Nb₂O₅/NF catalyst also has excellent oxygen evolution efficiency, which needs only 322 mV to reach the current density of 50 mA cm^?2. Furthermore, its electrocatalytic performance towards overall water splitting worked as both cathode and anode achieved a quite low potential of 1.56 V (10 mA cm^?2).     

Optimised phase compositions and improved microwave dielectric properties based on calcium tin silicates

The Ca_(1+2y)Sn_(1-x)Si_(1+y)O_(5-2x+4y) low-permittivity microwave dielectric ceramics were prepared through solid-state reaction at 1350–1450 °C for 5 h. The relations between microwave dielectric properties and phase compositions for non-stoichiometric Ca_(1+2y)Sn_(1-x)Si_(1+y)O_(5-2x+4y) ceramics have been investigated. A single CaSnSiO₅ phase with abnormally positive temperature coefficient of resonant frequency (τ_f = + 62.5 ppm/°C) was synthesised at 1450 °C. This composition was an effective τ_f compensator of CaSiO₃ and Ca₃SnSi₂O₉ phases with typically negative τ_f value. The CaSiO₃ second phase was related to the Sn deficiency in the CaSn_(1-x)SiO_(5-2x) (0 < x < 1.0) composition, whereas the Ca₃SnSi₂O₉ second phase was obtained by controlling the Ca:Sn:Si ratios on the basis of the Ca_(1+2y)SnSi_(1+y)O_(5+4y) (0 < y < 1.0) composition. A promising low-permittivity millimetre-wave ceramic with most excellent microwave dielectric properties (ε_r = 10.2, Q×f = 81,000 GHz and τ_f = −4.8 ppm/°C) was produced from the Ca_(1+2y)SnSi_(1+y)O_(5+4y) (y = 0.4) ceramic.     

Simplification of the Plasma Load of Negative-Pulse-Bias Source Used in Arc Ion Plating

Based on the voltage and current fluctuating phenomenon in the arc plasma load under the negative-pulse-bias, usingthe plasma physics theory and analysis of computer simulation expatiates that the nature of plasma load in vacuumarc plasma is a capacitance     

陶瓷表面化学镀的前处理工艺新进展

综述了非金属表面化学镀前处理工艺的现状和发展，对陶瓷化学镀的粗化和活化工艺的新进展进行了评述，侧重讨论了离子型、胶体钯型、浆料型、分子自组装吸附钯型、贱金属型活化工艺特点和进展，并展望了今后发展方向。     

化学复合镀层激光处理研究

研究了激光处理对Ni-P -SiC化学复合镀层的影响。借助于扫描电镜、能谱仪、X射线衍射、显微硬度计等设备对激光处理后复合镀层的表面形貌、组织结构及性能进行了综合分析。结果表明 ,对复合镀层进行激光处理可以获得与炉内加热同样的镀层硬度 ,且当激光功率 4 0 0W ,扫描速度 1.5m /min时 ,镀层硬度高于炉内加热的硬度     

玻璃微珠的表面化学镀银及红外辐射性能研究

采用化学镀方法在玻璃微珠表面镀银,考察了预处理条件、反应温度和反应时间等因素对玻璃微珠表面镀银的影响,并通过扫描电镜和X-射线衍射分析仪,对镀银后玻璃微珠的表面形貌和结构进行了观察和表征。将镀银玻璃微珠用于涂料中,考察了玻璃微珠在涂料中的应用及其红外辐射率的变化,探讨了化学镀条件对涂料红外辐射率的影响,结果表明,在控制反应温度和浓度的条件下,可使镀银玻璃微珠的红外辐射率由原来的1.02降为0.70,将其应用于涂料后,涂层的红外辐射率为0.80。     

镍层耐硝酸腐蚀性测试——一种简单的预先探测ENIG镍层“黑盘”现象的测试方法

随着更加精细的SMT、BGA等表面贴装技术的运用,化学沉镍金(ENIG)作为线路板最终表面处理得到了越来越广泛的应用,同时可怕的“黑盘”现象也随之更广泛地“流行”起来,直接导致贴装后元器件焊接点不规则接触不良。为了贯彻执行最好的流程控制和采取有效的预防措施,了解这种焊接失败的产生机理是非常重要的,及早的观测到可能发生“黑盘”现象的迹象变得同样关键。本文介绍了一种简单的预先探测ENIG镍层“黑盘”现象的测试方法-镍层耐硝酸腐蚀性测试,这种测试可以用于作为一种常规的测试方法监测一般化学沉镍溶液在有效使用寿命范围内新鲜沉积的镍层的质量。利用Weibull概率统计分析在不同的金属置换周期(MTO)下镍层的可靠性能表现。结合试验结果得出了一个镍层耐硝酸腐蚀性的判定标准。     

SnO2超微粒子薄膜的气敏特性研究

作者用自行设计的直流气体放电活化反应蒸发装置制备出平均粒径约为40nm的SnO_2超微粒子薄膜.研究了不同氧分压下所得SnO_2超微粒膜的形貌、结构和组成等特性,以及不同样品对各种易燃气体的气敏特性,得出了灵敏度随氧分压及灵敏度随工作温度的变化曲线.     

铜线材酸性高速电镀致密光亮锡、锡铜合金

为了寻找低成本、低腐蚀、低污染高速电镀锡、锡铜合金工艺 ,在含光亮剂、柔软剂DL0 1、0 2、0 3的硫酸槽中在不同的电流密度、不同的搅拌速度下 ,在Φ0 .5mm的铜线上电镀Sn和Sn Cu合金镀层。DL0 1、0 2的主要成分是无芳香族的希夫碱 ,DL0 3的主要成分是醇醛缩合物。结果表明 ,在含有DL0 1、0 2、0 3和 35g/LSnSO4 ,137g/LH2 SO4 的镀液中 ,在Jc=10～ 90A/dm2 ,v=16 0～ 314m/min时 ,所得镀层致密、柔软、光亮。在含CuSO4 ·5H2 O 0 .5 ,3.5g/L的硫酸镀槽中 ,在Jc=9,18A/dm2 ,v=16 0m/min时获得了致密、柔软、光亮的Sn (0 .3%～ 0 .6 % )Cu合金镀层。