Structural silicone sealants after exposure to laboratory test for durability assessment

During the service life of structural sealant glazing (SSG) facades, the load-bearing capacity of the silicone bonds needs to be guaranteed. Laboratory tests can assess the durability of SSG-systems based on mechanical characteristics of the bond after simultaneous exposure to both climatic and mechanical loads. This article studies how the material characteristics of two common structural sealants are affected by laboratory and field exposure. Dynamic mechanical analysis (DMA) confirms a reduction in the dynamic modulus of exposed silicone samples. Results from thermogravimetric analysis, Fourier-transform infrared spectroscopy, differential scanning calorimetry, and small-angle X-ray scattering/wide-angle X-ray scattering show differences between the two sealants and indicate no/minor changes in the composition and morphology of the laboratory and field exposed sealants. Mechanical characterization methods, such as DMA, and tensile and shear testing of the structural bond, are shown to be sensitive toward the combined climatic and mechanical loadings, and are hence suitable for studying degradation mechanisms of structural sealants.     

蛋类礼盒包装结构的缓冲性能研究

目的研究蛋类礼盒包装结构的缓冲性能。方法以蛋类尺寸为基础,建立可发性聚乙烯(expandable polyethylene. EPE)缓冲单元结构和组合结构,进行静态仿真分析和实验验证,比较结构在形状、叠合层数、组合形式等参数变化时的载荷与位移。结果结构层数变化相同时,单元结构的极限载荷从143N增加到236 N,组合结构的极限载荷从224 N增加到476 N,均呈近线性增长。结论蛋类礼盒包装中,组合结构的承载能力优于单元结构,通过单元结构的组合,可满足不同蛋类的包装要求。     

In vitro cyclic fatigue and hydrothermal aging lifetime assessment of yttria-stabilized zirconia dental ceramics

The in vitro lifetime assessment of dental zirconia has been the focus of researchers. This work mainly studied the cyclic fatigue lifetime in saliva and aging lifetime of three commercial zirconia dental materials: two kinds of 3 mol%-yttria stabilized zirconia ST(super-translucence) and MT(medium-translucence), in which MT contains a small amount of alumina; a 5 mol%-yttria stabilized zirconia TT(tooth-translucency). ST and MT materials have higher initial mechanical strength (flexural strength) and initial crack propagation threshold than TT materials, thus they have longer cycle fatigue lifetime, but TT has best aging resistance(no aging) in existing aging procedures. MT has a higher initial mechanical strength and better aging resistance than ST samples due to the influence of alumina at grain boundary, but has lower strength reliability. Finally the service lifetime of the three materials was evaluated, and some guidance for their use is provided.     

Behavior of 316L stainless steel containing corrosion pits under cyclic loading

The environmental performance of 316L grade stainless steel, in the form of tensile specimens containing a single corrosion pit with various aspect ratios, under cyclic loading in aerated chloride solutions is investigated in this study. Results from environmental tests were compared and contrasted with those obtained using finite element analysis (FEA). Fractography of the failed specimens obtained from experiments revealed that fatigue crack initiation took place at the base of the shallow pit. The crack initiation shifted towards the shoulder and the mouth of the pit for pits of increasing depth. This process is well predicted by FEA, as the strain contour maps show that strain is the highest around the centric strip of the pit. However, for shallow pits, local strain is uniformly distributed around that strip but begins to concentrate more towards the shoulder and the mouth region for increasingly deep pits.     

基于滑模的运载器主动段俯仰通道姿控系统设计

与传统比例-积分-微分（PID）控制方法相比，滑模控制（SMC）方法可以比较容易地将不确定性纳入控制器设计中，从而增强系统的鲁棒性。探索了SMC技术在运载器主动段姿态控制中的工程应用，首先通过分析基于趋近律的SMC系统，提出了降低不连续切换项系数的需求，然后研究了基于干扰上界的SMC方法。三通道小偏差仿真结果验证了两种方法的控制效果，表明第2种控制器的鲁棒性更好，稳态误差小，同时发动机喷管摆角需求较小。     

Modelling dislocation assisted tempering during rolling contact fatigue in bearing steels

Rolling contact fatigue in bearing steels is manifested by dark-etching regions, which are attributed to deformation induced tempering. In order to quantitatively explain this phenomenon, a model is suggested for martensite tempering assisted by dislocation glide during rolling contact fatigue. In the model, dislocations transport carbon from the matrix to carbide particles, provided that the carbon is located at a certain distance range from the dislocation contributing to the tempering process. By calculating the amount of carbon in the matrix, the kinetics of carbide thickening and hardness reduction are computed. It is found that the dark-etching region kinetics can be controlled by both bearing operation conditions (temperature and deformation rate) and microstructure (type, size, and volume fraction of carbides). The model is validated against tested bearings, and its limitations are discussed.     

Influence of domain switching process on the electrical fatigue behavior of ferroelectrics

We report an experimental approach, designed based on the recent findings that domain switching in ferroelectric ceramics can be separated into three regimes during antiparallel electric field loading, to investigate the influence of domain switching process on the electrical fatigue behavior of ferroelectrics. Uniaxial compressive stress (−2 MPã -100 MPa) and thermal loading (20 °C–150 °C) were used to tune the domain switching process. Under the same loading condition, the bipolar electrical fatigue behavior of soft lead zirconate titanate ceramics was systematically characterized. The amplitude and frequency of the applied electric field are 2 kV/mm and 10 Hz, respectively. By analyzing the evolution of the domain switching process, combined with the measured polarization and strain response, as well as the cracks observed on the surface of the specimen, it is found that the fatigue of ferroelectric ceramics was mainly related to the domain switching process near the coercive electric field: the regime 2 defined in this paper. The underlying mechanism was further discussed by considering the interplay between the domain switching process with the main factors affecting the electrical fatigue of ferroelectrics, namely defect redistribution, charge carrier injection, and crack initiation.     

Low cycle fatigue behavior of a eutectic 80Au/20Sn solder alloy

The eutectic 80Au/20Sn solder alloy is widely used in high power electronics and optoelectronics packaging. In this study, low cycle fatigue behavior of a eutectic 80Au/20Sn solder alloy is reported. The 80Au/20Sn solder shows a quasi-static fracture characteristic at high strain rates, and then gradually transforms from a transgranular fracture (dominated by fatigue damage) to intergranular fracture (dominated by creep damage) at low strain rates with increasing temperature. Coffin-Manson and Morrow models are proposed to evaluate the low cycle fatigue behavior of the 80Au/20Sn solder. Besides, the 80Au/20Sn solder has enhanced fatigue resistance compared to the 63Sn/37Pb solder.     

粉土界面恒刚度循环剪切试验研究

竖向循环荷载作用下桩土界面的作用机理是研究桩土摩擦疲劳的关键。针对循环荷载作用下桩-粉土界面的剪切性能,使用改进的剪切试验装置在恒刚度条件下进行循环剪切试验,研究循环次数、累积位移和法向刚度对其摩擦疲劳性能、循环后单调剪切性能的影响。试验结果表明,粉土在循环剪切过程中,法向应力和剪应力在初始10个循环内随循环数增加快速衰减,随着循环进行,逐渐趋于稳定;单次循环内在剪切位移方向变化时,土体呈现表现出剪缩-剪胀-剪缩交替现象,总体变形呈现剪缩的趋势;循环荷载作用下,粉土界面的法向应力和剪应力随法向刚度增大衰减速率增大,达到稳定的累积循环位移越小;粉土循环后的单调剪切、法向应力恢复的单调剪切的剪应力比小于首次单调剪切试验值,且法向应力恢复的循环后剪切试验的剪胀程度较小,表明循环剪切过程中界面处粉土颗粒棱角破碎,颗粒变得光滑。在对试验数据分析的基础上,提出了与累积位移、法向刚度和初始应力相关的无量纲累积位移,建立了法向应力和界面摩擦角随累积位移的衰减方程。     

一类两性分枝过程条件均值增长率的极限性质

本文主要研究随机环境中配对依赖人口数两性 Galton-Watson 分枝过程的条件均值增长率的极限性质．利用上可加函数的性质，得到配对单元平均增长率的极限性质和该过程条件均值的上界和下界．文中给出了关于过程条件均值增长率的两个序列，利用配对单元平均增长率的性质，获得了这两个序列的极限性质．随机环境中配对依赖人口数两性分枝过程比较复杂，本文的结论推广了现有的研究成果．