7055铝合金二次时效特征研究——（Ⅱ）显微组织与断口形貌特征

利用透射电镜和扫描电镜研究了二次时效处理后7055合金显微组织及Kahn撕裂断口形貌特征。结果表明，高温预时效时未析出的溶质原子，在低温二次时效时继续析出造成强度提高：由于二次时效温度降低，析出相长大和粗化速度降低，析出相密度高，可以获得高于单级峰值时效的强度和硬度。提高二次时效温度促进比GP区强化效果更高的矿相析出，从而获得比低温二次时效更高的强度。缩短预时效时间以及降低预时效温度，都有利于残留固溶原子和空位的保留，二次时效时硬化响应更快。晶界析出相的体积分数和形貌变化对7055合金断裂韧性存在显著的影响。低温预时效及低温二次时效获得少量且断续分布的球形沿晶析出相，断裂韧性较高。而提高二次时效温度则促进晶界析出相析出，不利于断裂韧性的改善。     

Dependence on temperature of tensile properties of the single-crystal superalloy DD11

Tensile tests within a temperature range from room temperature (RT) to 1100°C were performed on a novel second-generation single-crystal superalloy DD11. The experimental results indicated that the yield strength (YS) remained constant up to 760°C, while a maximum was reached at 850°C. The elongation and area reduction decreased gradually from RT to 760°C and then they increased rapidly at temperatures above 760°C. As for the deformation mechanism, when the temperature was below 850°C, the γ′ precipitates were sheared by isolated faults, faulted loops and dislocation pairs. The formation of dislocation networks and dislocation climb mechanism were confirmed at temperatures above 980°C. Finally, the relationship between the YS of the DD11 alloy and the operative deformation mechanism was discussed.     

一种含Re单晶高温合金的拉伸断裂行为

研究了Re对单晶高温合金拉伸、持久性能的影响及含Re单晶的拉伸断裂特征。拉伸性能试样采用[001]取向单晶制备，应力轴方向平行于单晶[001]取向，采用扫描电镜观察断口形貌。实验结果表明：Re的加入降低了单晶短时拉伸延伸率，但能提高单晶的高温持久断裂延伸率；含Re单晶室温拉伸表现为滑移开裂特征；高温拉伸断裂失效机制为变形不均匀的蠕变断裂；高温持久断口表现为典型的塑性断裂特征，变形均匀。     

W-N-Cu重合金固溶强化的机理研究

应用宏观力学性能、断裂强度与微观组织结构相结合的分析研究方法,采用JCXA-733型电子探针显微分析仪及二次电子图像(SEH)较系统地观察了液相烧结的W-Ni-Cu重合金的断口形貌,分析研究了断裂行为行径,应用背散射电子图像(BEI),吸收电子图像(AEl),以及W,Ni,Cu的特征X射线做了线扫描、面扫描图像(X-Rayl),同时做了定点定量ZAF的分析,研究了W-Ni-Cu重合金中粘结相的固溶度,探讨了固溶强化和不平衡凝固的机制,阐述了重合金的断裂机理,为提高W-Ni-Cu重合金的强度具有理论和实际意义。     

国产HR3C耐热钢的蠕变断裂研究

HR3C钢是一种新型的奥氏体耐热钢,主要应用于超临界和超超临界机组的过热器和再热器。本文针对国产HR3C耐热钢,进行了持久强度试验,并通过分析蠕变断口的微观形貌,对其蠕变断裂进行了探讨。采用外推法计算出该钢105 h的持久强度极限为104.98MPa。相应的断口观察显示,HR3C钢的蠕变断裂类型属于沿晶断裂。