Eco-friendly tape casting of borosilicate glass/Al2O3 sheets for LTCC applications

This work reports the innovative development of a borosilicate glass/Al₂O₃ tape for LTCC applications using an eco-friendly aqueous tape casting slurry. Polyvinylpyrrolidone (PVP) and polyacrylic acid (PAA) were the respective dispersants, while carboxymethyl cellulose (CMC) and styrene acrylic emulsion (SA) were the respective binders. The results showed that PVP was more suitable than PAA as the dispersant for the aqueous casting slurry, and that 1.5 wt% PVP would achieve well dispersion of CABS glass/Al₂O₃ powder in the aqueous slurry. Moreover, a small amount of 2.0 wt% CMC binder could yield smooth CABS glass/Al₂O₃ tapes crack free. A high-quality CABS glass/Al₂O₃ tape with a smooth surface was made from an aqueous slurry containing 1.5 wt% PVP dispersant, 2.0 wt% CMC binder, and 2.0 wt% PEG-400 plasticizer. The density, tensile strength, and surface roughness of the green tape were 2.05 g/cm³, 0.87 MPa, and 148 nm, respectively. The resulting CABS glass/Al₂O₃ composites sintered at 875 °C exhibited a bulk density of 3.14 g/cm³, a dielectric constant of 8.09, a dielectric loss of 1.0 × 10^?3, a flexural strength of 213 MPa, a thermal expansion coefficient of 5.30 ppm/^°C, and a thermal conductivity of 3.2 W m^?1 K^?1, thus demonstrating its broad prospects in LTCC applications.     

Anisotropic thermal expansion and ionic conductivity of a crystal-oriented,Mg2+-conducting NASICON-type solid electrolyte

Multivalent ion-conducting ceramics are required for the manufacture of high-safety, high-capacity rechargeable batteries. However, the low ionic conductivity of solid electrolytes and discrepancies in the thermal expansion between the battery components limit their widespread application. Furthermore, anisotropic thermal expansion in crystals during battery manufacturing and the charge-discharge cycles causes the formation of microcracks, which degrade the battery performance. The physical properties of ceramic materials with anisotropic crystal structures can be modified by varying the crystallographic orientation of their grains. In this study, a co-precipitation approach was used to synthesize an Mg²⁺-conducting (Mg_0.1Hf_0.9)_4/3.8Nb(PO₄)₃ solid electrolyte, and the grain orientation in the bulk sample was controlled using strong magnetic fields during the slip casting process. The results showed that inducing an orientation along the c-axis enhanced the apparent ionic conductivity of the bulk sample. It was also observed that (Mg_0.1Hf_0.9)_4/3.8Nb(PO₄)₃ crystal has a negative volumetric thermal expansion despite a positive linear thermal expansion along its c-axis. By adjusting the c-axis orientation of the grains, (Mg_0.1Hf_0.9)_4/3.8Nb(PO₄)₃ electrolytes with negative or positive linear thermal expansion coefficient have been produced. The findings of this study suggest that solid-electrolytes with negative, positive, or zero linear thermal expansion can be produced to create more compatible and higher-performance solid-state devices.     

压裂水平井产能预测方法研究进展

水平井压裂技术在低渗透及非常规储层中得到了广泛应用,压裂后水平井的产能预测关系到油田开发方案的制定,因此,国内外学者对压后渗流模型的建立和求解方法做出了不懈的努力。本文详细回顾了国内外学者所建压裂水平井产能预测模型及求解方法,指出了不同模型和求解方法的优缺点,并展望了压裂水平井产能模型的发展方向。     

Hierarchical electromagnetic absorption in micro-waveguide stuffed with magnetic media for resin-based composites of graphene nanosheets and manganese oxides

Waveguide configurations of hierarchical system are proposed as new microstructures for composites in absorbing enhancement. Supercritical fluid (SCF) one-pot exfoliation of layered graphite and manganese oxide mixing materials is developed to obtain a hierarchical system, containing graphene nanosheets (GNS) and exfoliated manganese oxides (EMO) in different sizes. Composites with GNS–EMO embedded in epoxy resin matrix are produced for a design of dielectric and magnetic loss integrated absorber. Volume fraction of GNS–EMO in composites is given for an optimal quantity of resin epoxy in fixation and formation. The effect of mixing ratios between electric and magnetic components is provided for the design of dielectric and magnetic loss integrated absorbers. Frequency shifting phenomena are revealed in the component adjusting course. Excluding the offsetting sizes, reflection loss of composites is enhanced as thickness increases. Synergistic effect of electric and magnetic coordinated materials demonstrates the superiority of micro-waveguide structures in GNS–EMO composite absorber.     

Effect of Li2O on the crystallization behavior of CaO-Al2O3-SiO2-Li2O-Ce2O3 mold slags

The effect of Li₂O on the crystallization properties of CaO-Al₂O₃-SiO₂-Li₂O-Ce₂O₃ slags was investigated. With increasing the Li₂O content, LiAlO₂ and CaCeAlO₄ were the main crystalline phases. LiAlO₂ formed for the charge compensating of Li⁺ ions to [AlO₄^5?]-tetrahedrons, and CaCeAlO₄ formed as a result of the charge balance of Ce³⁺ ions, Ca²⁺ ions, and [AlO₆^9?]-octahedrons. Increasing the content of Li₂O to 10%, the crystallization temperature was the highest, and the incubation time was the shortest. The crystallization ability was strong due to the three factors of strengthening the interaction between ions and ion groups, decreasing the polymerization degree, and increasing the melting temperature. Further increasing the content of Li₂O, the crystallization performance was obviously suppressed, because the melting temperature and the force between the cations and the anion groups decreased.     

Quasi-static compressive behaviour of aluminium cenosphere syntactic foams

In this paper, cenosphere particles embedded in AA2014 aluminium matrix are used to fabricate syntactic foam by stir casting method. The particle size is about 100?µm and foam density is about 1990?kg?m^?3. Compression tests at strain rate 0.001/s are performed on foam samples to characterise their mechanical properties which are then used in numerical analysis on commercial finite element analysis software ABAQUS/CAE with isotropic elastic-plastic material model. Experimental and numerical results show good conformity in deformation behaviour with elastic and plateau zones showing average deviations less than 5% and 20%, respectively. Foams showed high yield stress and energy absorption capabilities that can be useful in making blast and impact resistant structures.     

Methodology for optimization of pouring variables using bottom pour for low masses of SS304 (<300 kg) in investment casting process (case study)

Bottom pour ladles with stopper rod systems are commonly used in the metal casting industry. However, stopper rod bottom-pouring systems have not yet been developed for the lower thermal masses of alloys typically used in the investment casting industry. Large thermal masses used with bottom pour systems are typically limited for ladles larger than 700 kg and to certain alloys with higher fluidity and longer solidification time like cast iron, aluminum alloys etc. In this study, bottom pour ladle designs and low thermal mass refractory systems have been developed and evaluated in production investment foundry trials with 300 kg pouring ladle. The ladles system and pouring practices used will be described along with the results from the pouring trials for SS304 that represents typical alloys used in Investment casting industries. Optimization of the variables used in an experimentation using Genetic algorithm is also explained.     