Dense and core-rim structured B4C-TiB2 ceramics with Mo-Co-WC additive

B₄C-TiB₂ ceramics (TiB₂ ranging 5~70 vol%) with Mo-Co-WC as the sintering additive were prepared by spark plasma sintering. In comparison with B₄C-TiB₂ without additive, the enhanced densification was evident in the sintered specimen with Mo-Co-WC additive. Core-rim structured grain was observed around TiB₂ grains. The interface of the rim between TiB₂ and B₄C phases demonstrated different feature: the inner borderline of the rim exhibited a smooth feature, whereas a sharp curved grain boundary was observed between the rim and the B₄C grain. The formation mechanism is discussed: the epitaxial growth of (Ti,Mo,W)B₂ rim around the TiB₂ core may occur as a result of the solid solution and dissolution-precipitation between TiB₂ phase and the sintering additive. It was revealed that the fracture toughness increased as the content of TiB₂ content increased, alongside the decreased hardness. B₄C-30 vol% TiB₂ specimen demonstrated the optimal combination of mechanical properties, reaching Vickers hardness of 24.3 GPa and fracture toughness of 3.33 MPa·m^1/2.     

Characterizations of friction welding joint interface for AISI 316

Because of heat amount is different from peripheral to central of friction welding interface, which is leaded to vary the characterizations along that interface. Current study, respectively, focused on the effect of different friction pressure on micro-structural and mechanical properties of that friction welding joint interface. Presently, these friction pressures are 110, 130, 150 and 170 MPa while kept all other conditions constant. The effects of different friction pressure on welding interface characterization were investigated by EDX, SEM, tensile, compression, impact and hardness tests. The tensile tests carried out on the standardized test piece with diameter 6 mm and 8 mm, thus, compression tests were extracted from the positions of 0°, 45° 90° with test specimen of 4 mm diameter and 6.5 mm length at weld center. Whereas, the impact test pieces were picked up in two positions, the first one is symmetrical, which it obtained to the respect of the rotation axis and the interface, on the other hand, the second one is non-symmetrical with the axis of rotation and symmetrical to the interface, for making the notch head coincide with the center of the welded joint, The obtained results showed that with reducing of friction pressure will present lack of bonding increasing from peripheral toward the welding center, which will responsible on reducing of the mechanical properties such as tensile, compression and impact strength.     

Isolation of antimicrobial agent from the marine algae Cystoseira hakodatensis

Cystoseira hakodatensis is an unutilised brown algae belonging to family Sargassaceae. A crude methanol extract from the algae showed inhibitory effects on the growths of Bacillus cereus and Bacillus licheniformis. To isolate the major antimicrobial agent, a sequential active‐guided isolation procedure was applied: liquid–liquid extraction, column chromatography and bio‐autography. A marked antimicrobial agent (active α) was isolated in hydrophobic fraction and was determined to phenolics without carbohydrates and proteins by phytochemical test. Regarding the antimicrobial potential, the isolated active α showed better inhibitory effects against B. cereus and B. licheniformis at 2 and 4 times of lower concentrations (62.5 and 31.3 μg mL^?1) in comparison with epigallocatechin gallate. These results showed that C. hakodatensis is a potential source of antimicrobial agent capable of preventing the growth of the two bacteria.     

Effects of SiC content on the densification,microstructure, and mechanical properties of HfB2–SiC composites

To investigate the effects of SiC on microstructure, hardness, and fracture toughness, 0, 10, 20, and 30 vol% SiC were added to HfB₂ and sintered by SPS. Upon adding SiC to 30 vol%, relative density increased about 4%; but HfB₂ grain growth had a minimum at 20 vol% SiC. This may be due to grain boundary silicate glass, responsible for surface oxide wash out, enriched in SiO₂ with higher fraction of SiC. By SiO₂ enrichment, the glass viscosity increased and higher HfO₂ remained unsolved which subsequently lead to higher grain growth. Hardness has increased from about 13 to 15 GPa by SiC introduction with no sensible variation with SiC increase. Residual stress measurements by Rietveld method indicated high levels of tensile residual stresses in the HfB₂ Matrix. Despite the peak residual stress value at 20 vol% SiC, fracture toughness of this sample was the highest (6.43 MPa m^0.5) which implied that fracture toughness is mainly a grain size function. Tracking crack trajectory showed a mainly trans-granular fracture, but grain boundaries imposed a partial deflection on the crack pathway. SiC had a higher percentage in fracture surface images than the cross-section which implied a weak crack deflection.     

多元合金化大断面球墨铸铁组织和性能的分析

为了提升大断面球墨铸铁综合力学性能，通过复合添加微量合金元素铜、锑、锡、钼对大断面球墨铸铁进行微合金化处理，借助金相显微镜(OM)、扫描电子显微镜(SEM)及力学性能测试等手段，研究了Cu Sb Sn Mo复合微合金化大断面球墨铸铁微观组织和力学性能。结果表明，试验球墨铸铁具有良好的综合力学性能。大断面球墨铸铁中添加铜、锑、锡、钼后优化了材料的组织结构，基体组织为珠光体＋少量牛眼状铁素体；试样石墨组织细小、圆整，分布均匀。同时，合金元素的复合加入使得其抗拉强度达到800 MPa以上，硬度约为280HB，伸长率达到5%以上。拉伸断口分析表明，微合金化大断面球墨铸铁断裂模式以解理断裂为主，伴有少量的塑性变形。     

A first-principles investigation on mechanical and metallic properties of titanium carbides under pressure

The titanium carbides are potential candidates to achieve both high hardness and refractory property. We carried out a structural search for titanium carbides at three pressures of 0 GPa, 30 GPa and 50 GPa. A phase diagram of the Ti-C system at 0 K was obtained by elucidating formation enthalpies as a function of compositions, and their mechanical and metallic properties of titanium carbides were investigated systematically. We also discussed the relation of titanium concentration to the both mechanical and metallic properties of titanium carbides. It has been found that the average valence electron density and tractility improved at higher concentrations of titanium, while the degree of covalent bonding directionality decreased. To this effect, the hardness of titanium carbide decreases as the content of titanium increases. Our results indicated that the titanium content significantly affected the metallic properties of the Ti-C system.     

高性能大尺寸永磁体粘合强度的测定

介绍了一种用三点弯曲试验法测定高性能大尺寸粘接永磁体粘合强度的方法，及利用布氏硬度计的加载系统，实现100％检验粘接质量的方法。     

Damage Development in Gray Cast Iron under Static Deformation

The authors discuss the results of experimental investigation of structural degradation of gray cast iron at various stages of static tensile deformation. Analysis of the deformation process has revealed that damageability of a material under loading can be assessed by both a special strain parameter and scatter of hardness characteristics or a ratio of the modulus deviation to the current value of the elastic modulus. A correlation between these parameters has been established.