氮化硅/石墨激光合金化涂层的组织结构与性能研究

为获得金属表面特别是高副接触金属表面含自润滑特性且具有高硬度耐磨特性的功能材料 ,研究了 45 # 钢表面激光合金化氮化硅 /石墨复合涂层的工艺方法、组织特征、界面形态及其形成机制 ,利用光学显微镜、扫描电镜和X射线能谱对所形成合金化层的元素分布和含量进行了分析 ,并对试样硬度进行了测定。结果表明 ,合金化层中元素Fe ,Co ,Si,C分布均匀 ;C含量达到了 15 6 9%,大部分以石墨的形式存在 ,具有一定的自润滑性能 ;但在形成合金化层的温度条件下 ,氮化硅分解严重 ;合金化层硬度提高的主要原因是Si Fe ,Co Fe固溶体的强化作用及高碳马氏体的生成和高硬度碳化物的存在。     

Processing of Yttria-Alumina Coated Silicon Nitride Slips by Slip Casting

Si₃N₄powders coated with 6 wt% Y₂O₃and 4 wt% Al₂O₃were prepared by coprecipitation. The resulting powders were dispersed in water at different pH values and with addition of various amounts of ammonium polyacrylate (NH₄PA) to produce 32 vol% slips. The influence of the amount of NH₄PA solution added and pH on the rheological properties of 32 vol% coated Si₃N₄slips were studied. In addition, the sintered density of cast samples was determined and related to the degree of slip dispersion. The adsorption of the NH₄PA on the coated particle surface was rather high and the surface became saturated near 0.86 mg/m²at pH 9.2. High NH₄PA concentrations (1.7–3 wt%) were necessary to obtain well dispersed 32 vol% coated Si₃N₄slips at pH 9.2. The best stabilization was obtained with the addition of 2.3 wt% NH₄PA; in this condition, the viscosity reached a minimum value of 35 mPa.s at 100 s^–1. The slip viscosity increased with increasing pH from 9.2 to 10.2. Slips with low viscosities gave a more dense packing of cast samples and consequently higher sintered density values.     

Transmittance and cathodoluminescence of AlN ceramics sintered with Ca3Al2O6 as sintering additive

Aluminum nitride ceramics were prepared by sintering with 0–4.8 mass% of Ca₃Al₂O₆ (C₃A) as a sintering additive. The transmittance in the range of 260–550 nm increased with increasing amount of C₃A. The cathodoluminescence intensity attributed to oxygen-induced defects decreased with increasing amount of C₃A. From the results, the increase of the transmittance in the range of 260–550 nm was considered to be related to the decrease of the oxygen-induced defect density.     

反应离化团束（RICB）法生长CN硬质薄膜

用反应离化团束（ＲＩＣＢ）法，以低分子量聚乙烯为蒸发材料，氨气为反应气体，在ＮａＣｌ（１００）和Ｓｉ（１００）衬底上淀积Ｃ－Ｎ薄膜，透射电子衍射（ＴＥＭ）分析表明薄膜中含有β－Ｃ３Ｎ４晶粒，Ｘ射线光电子谱（ＸＰＳ）和红外吸收谱（ＩＲ）表明存在Ｃ，Ｎ原子的化学键合。     

高性能各向异性Sm2Fe17Nx磁粉的制备

本文研究了高性能各向异性Ｓｍ２Ｆｅ１７Ｎｘ磁粉的制备工艺路线与工艺参数。优化了制备与工艺参数。已制备出磁性能达到：Ｂｒ＝１．３９Ｔ，Ｈｃｉ＝８５０ＫＡ／ｍ和（ＢＨ）ｍ＝２３６ＫＪ／ｍ＾３的各向异性Ｓｍ２Ｆｅ１７Ｎ２．８８磁粉，该磁粉的各向异性场ＨＡ达到２０Ｔ。     

氮化硅的性能及其聚合物材料

叙述了氮化硅（Ｓｉ３Ｎ４）的性能并制备了含Ｓｉ３Ｎ４的聚合物材料，这种材料在医学上具有重要价值，对改变医学方面的概念、和对促进人类健康长寿具有重要意义。     

热力学相图计算技术在闪速燃烧合成氮化硅铁中的应用

将热力学相图计算技术应用于Si-Fe-O-N体系,以评估由FeSi75粉闪速燃烧合成氮化硅铁的条件和目标产物。结果表明:将闪速燃烧温度控制在1200～1500℃之间较为适宜,此时平衡态产物中除主要含有Si3N4以外,还有一定量的Fe与Si间化合物和少量稳定的SiO2存在。此计算结果与实际试验结果吻合良好。     

Oxidation of porous nanocrystalline titanium nitride. II. Scale structure and composition

We have used x-ray phase analysis to study the composition of the products of reaction between oxygen and nanocrystalline powders with particle sizes 15, 40, 55, and 80 nm, and also specimens pressed (and sintered) from them. The powders were oxidized in air at 100°C (400 h) to 500°C (5 min), while the sintered specimens were oxidized at 600–900°C for 15, 120, and 240 min. In all cases, in the initial oxidation step the oxynitride Ti(O_xN_y) is formed, which over time is oxidized to TiO, Ti₂O₃, Ti₃O₅, TiO₂ (anatase) and TiO₂ (rutile). In the range 600–800°C, formation of a continuous oxide layer and conversion of anatase to rutile slows down diffusion of oxygen in the scale. We have established that at 900°C, the growth rate of the scale thickness increases and so the reflections from the oxynitride are barely noticeable on the diffraction patterns taken from the surface of the oxidized specimen. In these diffraction patterns, along with strong reflections from the rutile, we also observed weak reflections from lower oxides and anatase, which may be due to reaction between oxygen and the titanium ions diffused to the scale surface. We have concluded that at T > 850°C, the mechanism for oxidation of TiN changes. This is due to superposition of counterdiffusion of titanium ions on the diffusion of oxygen. __________ Translated from Poroshkovaya Metallurgiya, Nos. 3–4(448), pp. 72–78, March–April, 2006.