Centrifugal Casting of High Speed Steel/Nodular Cast Iron Compound Roll Collar

Ｈｉｇｈ ｓｐｅｅｄｓｔｅｅｌ (ＨＳＳ) ,ｉｓｃｈａｒａｃｔｅｒｉｚｅｄｂｙｅｘ ｃｅｌｌｅｎｔｈａｒｄｎｅｓｓ ,ｗｅａｒｒｅｓｉｓｔａｎｃｅ ,ａｎｄ ｇｏｏｄｒｅｄｈａｒｄｎｅｓｓ .Ｒｅｃｅｎｔｌｙ ,ＨＳＳｉｓａｐｐｌｉｅｄｔｏｍａｎｕｆａｃｔｕｒｅｈｏｔｒｏｌｌｉｎｇｒｏｌｌｓｔｏｐｒｏｄｕｃｅｓｔｒｉｐｓｏｆｇｏｏｄｓｈａｐｅａｎｄｓｍａｌｌｃｒｏｗｎｗｉｔｈｅｘｔｅｎｄｅｄｒｏｌｌｓｅｒｖｉｃｅｌｉｆｅ[1,2 ] .ＴｈｅＨＳＳｉｓａｐｐｌｉｅｄｔｏｍａｎｕｆａｃｔｕｒｅｒｏｌｌｃｏｌｌａｒｆｏｒ…     

DISTRIBUTION AND EFFECT OF Ce IN RE BEARING DUCTILE IRON

The dependence of nodularization of graphite upon Ce content in RE bearing nodular castiron,prepared by directional solidification,has been investigated by electrolyticextraction-radioisotope assay analysis of Ce in each phase of the iron together withmeasurement of nodulized graphite.Results show that the Ce occurs mainly as alloyed form.In the graphite phase,the Ce content is believed to be characterization of nodularization.Thegraphite would completely nodulized only the Ce is over a certain content in graphite phase.     

高强度高韧性球铁曲轴的生产

研究了合金化，二次孕育，热处理工艺及圆角滚压对球铁曲轴性能的影响，经实际生产验证，此工艺可使抗拉强度超过800MPa，伸长率超过5％。     

影响中小企业球铁质量稳定的因素

分析了影响中小企业球铁生产稳定性的关键因素,指出在一定的原材料条件下,目前中小型企业生产球铁存在的问题是温度偏低,孕育方法不当。     

大型风电球墨铸铁件的生产实践

以轮毂为例,介绍对大型风力发电机球墨铸铁件生产工艺进行的试验研究。通过优化铸型工艺,采用适当的浇注系统和低温石墨化退火工艺,选择合理的化学成分,控制球化处理与孕育处理,可生产出各项性能指标合格的风电铸件。     

提高离心球墨铸铁管水泥内衬质量的方法

分析影响离心球墨铸铁管水泥内衬质量的因素,对水泥内衬质量不稳定,内衬层厚度不均匀,水泥中间起泡,衬层密实度不够,内裂、离鼓严重,衬层内壁有泪痕等质量缺陷,针对性地采取措施,加强人力资源管理和考核,对承口挡轮、托压轮、搅拌机等相应设备进行改造,对养生池进行扩建,攻关后水泥衬层一级品率由原来的64%提升到99%,取得了预期的效果。     

球化剂中氧化镁临界含量的研究

球化剂中的有效镁含量随着氧化镁含量的增高而降低：所以球化剂中氧化镁越高，其球化能力越低。为了获得良好的球化，球化剂中氧化镁含量应低于一定的临界值。研究了球化剂中氧化镁含量对球化效果、球铁的显微组织和性能的影响，以及球化剂中所能允许的氧化镁临界含量的确定方法。     

确保铸态铁素体球铁排气管质量的关键措施

介绍确保大批量生产的铸态铁素体球铁排气管质量达到和超过康明斯技术标准的关键措施，包括：选用特定炉料，使用专用球化剂和孕育剂，优化铁液化学成分，准确称量，严格控制球化处理，浇注及孕育等关键工序。     

276Q微型汽车发动机曲轴的铸造

276Q铸态球铁曲轴的牌号为QT700-2，要求珠光体不低于90％，硬度240-300HB；采用工频炉熔化，气冲造型，稀土镁球化剂，冲入法球化处理和随流孕育处理。对化学成分的选择和炉料配比进行了介绍。试制结果，性能达到要求。     

中硅钼球墨铸铁的研制

根据国外相关技术标准，设计、研制了中硅钼球墨铸铁，并测试、分析了其铸态组织、力学性能、抗高温氧化性能。结果表明，该成分的材料在铸态下完全符合技术要求。