High-temperature oxidation behavior of monolithic Zr3[Al(Si)]4C6 and its composite incorporating 30vol% ZrB2-SiC: Providing a basis for broadening the service temperature

To provide a basis for the high-temperature oxidation of ultra-high temperature ceramics (UHTCs), the oxidation behavior of Zr₃[Al(Si)]₄C₆ and a novel Zr₃[Al(Si)]₄C₆-ZrB₂-SiC composite at 1500 °C were investigated for the first time. From the calculation results, the oxidation kinetics of the two specimens follow the oxidation dynamic parabolic law. Zr₃[Al(Si)]₄C₆ exhibited a thinner oxide scale and lower oxidation rate than those of the composite under the same conditions. The oxide scale of Zr₃[Al(Si)]₄C₆ exhibited a two-layer structure, while that of the composite exhibited a three-layer structure. Owing to the volatilization of B₂O₃ and the active oxidation of SiC, a porous oxide layer formed in the oxide scale of the composite, resulting in the degradation of its oxidation performance. Furthermore, the cracks and defects in the oxide scale of the composite indicate that the reliability of the oxide scale was poor. The results support the service temperature of the obtained ceramics.     

Microstructure,wear and corrosion characteristics of multiple-reinforced (SiC–B4C–Al2O3) Al matrix composites produced by liquid metal infiltration

In this study, AA7075 aluminum matrix composites reinforced with the combination of SiC, Al₂O₃, and B₄C particles were fabricated by the liquid metal infiltration method. The effects of the relative ratio of B₄C and Al₂O₃ particles on the microstructural, wear, and corrosion features of the composite samples were analyzed using XRD, light metal microscopy, SEM, EDS, Brinell hardness, ball-on-disc type tribometer, and potentiodynamic polarization devices. It was determined that infiltration occurred more successfully, and homogenously distributed particles with reduced porosity were obtained as the amount of Al₂O₃ increased. Worn surface studies revealed that the specimens were predominantly worn by abrasion and adhesion. The increase in B₄C/Al₂O₃ ratio caused a decrease in the hardness and wear strength, whereas it increased the corrosion resistance.     

Preparation of Pt/Ce–Zr–Y mixed oxide/anodized aluminium oxide catalysts for hydrogen passive autocatalytic recombination

The use of a Pt-based catalyst was evaluated for autocatalytic hydrogen recombination. The Pt was supported on a mixture of Ce-, Zr- and Y-oxides (CZY) to yield nanosized Pt particles. The Pt/CZY/AAO catalyst was then prepared by the spray-deposition of the Pt/CZY intermediate onto an anodized aluminium oxide (AAO) layer on a metallic aluminum core. The Pt/CZY/AAO catalyst (3 × 1 cm) was evaluated for hydrogen combustion (1–8 vol% hydrogen in the air) in a recombiner section testing station. The thermal distribution throughout the catalyst surface was investigated using an infrared camera. The maximum temperature gradient (ΔT) for the examined hydrogen concentrations did not exceed 36 °C. The Pt/CZY/AAO catalyst was also evaluated for prolonged hydrogen combustion duration to assess its durability. An average combustion temperature of 239.0 ± 10.0 °C was maintained for 53 days of catalytic hydrogen combustion, suggesting that there was limited, or no, catalyst deactivation. Finally, a Pt/CZY/AAO catalytic plate (14.0 × 4.5 cm) was prepared to investigate the thermal distribution. An average surface temperature of 212.5 °C and a maximum ΔT of 5.4 °C was obtained throughout the catalyst surface at a 3 vol% hydrogen concentration.     

5A06-O aluminium–magnesium alloy sheet warm hydroforming and optimization of process parameters

The uniaxial tensile test of the 5A06-O aluminium–magnesium (Al–Mg) alloy sheet was performed in the temperature range of 20–300 °C to obtain the true stress–true strain curves at different temperatures and strain rates. The constitutive model of 5A06-O Al–Mg alloy sheet with the temperature range from 150 to 300°C was established. Based on the test results, a unique finite element simulation platform for warm hydroforming of 5A06-O Al–Mg alloy was set up using the general finite element software MSC.Marc to simulate warm hydroforming of classic specimen, and a coupled thermo-mechanical finite element model for warm hydroforming of cylindrical cup was built up. Combined with the experiment, the influence of the temperature field distribution and loading conditions on the sheet formability was studied. The results show that the non-isothermal temperature distribution conditions can significantly improve the forming performance of the material. As the temperature increases, the impact of the punching speed on the forming becomes particularly obvious; the optimal values of the fluid pressure and blank holder force required for forming are reduced.     

Investigation on thermal conductivity and mechanical properties of Si3N4 ceramics via one-step sintering

High thermal conductivity Si₃N₄ ceramics were fabricated using a one-step method consisting of reaction-bonded Si₃N₄ (RBSN) and post-sintering. The influence of Si content on nitridation rate, β/(α+β) phase rate, thermal conductivity and mechanical properties was investigated in this work. It is of special interest to note that the thermal conductivity showed a tendency to increase first and then decrease with increasing Si content. This experimental result shows that the optimal thermal conductivity and fracture toughness were obtained to be 66 W (m K)^-1 and 12.0 MPa m^1/2, respectively. As a comparison, the nitridation rate and β/(α+β) phase rate in a static pressure nitriding system, i.e., 97% (MS10), 97% (MS15), 97% (MS20) and 8.3% (MS10), 8.3% (MS15), 8.9% (MS20), respectively, have obvious advantages over those in a flowing nitriding system, i.e., 91% (MS10), 91% (MS15), 93% (MS20) and 3.1% (MS10), 3.3% (MS15), 3.3% (MS20), respectively. Moreover, high lattice integrity of the β-Si₃N₄ phase was observed, which can effectively confine O atoms into the β-Si₃N₄ lattice using MgO as a sintering additive. This result indicates that one-step sintering can provide a new route to prepare Si₃N₄ ceramics with a good combination of thermal conductivity and mechanical properties.     

Graphene added multilayer ceramic sandwich (GMCS) composites: Structure,preparation and properties

The multilayer ceramic composites (MLC) consist of two ceramic materials insoluble in each other and sequentially piled in a symmetric manner whereas they can be divided into two groups: multilayer composites with weak interfaces and composites with strong interfaces. The graphene added multilayer ceramic sandwich (GMCS) composite was developed. The multilayer stack of Si₃N₄ with 5 and 30 wt% graphene addition were stratified in sandwich structure. So formed multilayer stacks with 5 and 7 layers were sintered by hot issostatic pressing (HIP). The homogenity of graphene addition, the effect of layered structures and the position of layers with lower and higher graphene content on the final properties were studied.     

Influence of ZrB2 hard ceramic reinforcement on mechanical and wear properties of aluminum

In this work, the effect of ZrB₂ (0, 5, 10 and 20?vol%) ceramic reinforcement on densification, structure, and properties of mechanically alloyed Al was investigated. The milling of Al-ZrB₂ powder compositions resulted in formation of agglomerates with varied size. In particular, the size of agglomerates was reduced considerably with increased addition of ZrB₂ to Al. Interestingly, the densification of hot pressed Al increased from 96.06% to 99.22% with ZrB₂ addition. The reduction of agglomerates size was attributed to the enhanced densification of Al-ZrB₂ composites. Pure Al showed relatively low hardness (0.94?GPa) and it was improved to 1.78?GPa with the addition of 20?vol% ZrB₂. The mechanical properties have significantly been improved for Al-ZrB₂ composites. Especially Al - 20?vol% ZrB₂ possessed a very high yield strength (529?MPa), compressive strength (630?MPa) and compressive strain of 19.25%. Realization of such a good combination of mechanical properties is the highest ever reported for Al composites so far in the literature. The coefficient of friction (COF) of Al-ZrB₂ varied narrowly between 0.33 and 0.40 after dry sliding wear against steel disc. The wear rate of Al-ZrB₂ composites was within mild wear regime and varied between 98.88?×?10^?6 and 34.66?×?10^?6 mm³/Nm. Among all the compositions, Al - 20?vol% ZrB₂ composite exhibited the lowest wear rate and high wear rate was noted for pure Al. Mild abrasion, tribo-oxidation, third body wear (wear debris) and delamination were the major material removal mechanisms for Al-ZrB₂ composites. Overall the hardness, strength and wear resistance of Al - 20?vol% ZrB₂ composite was improved by 84.3%, 84.3% and 64.2%, respectively when compared to pure Al.     

Raman and X-ray photoelectron spectroscopy study on the influence of La2O3 on the melt structure of SiO2–CaO–Al2O3–MgO

In order to gain more insights into the influence of rare earth elements on the melt structure of SiO₂–CaO–Al₂O₃–MgO glass ceramics, Raman and X-ray photoelectron spectroscopy techniques were used to study the influence of La₂O₃ on the Si–O/Al–O tetrahedron structure within SiO₂–CaO–Al₂O₃–MgO–quenched glass samples in this study. Results showed that some Raman peak shapes at low frequencies (200–840 cm^?1) changed significantly after the addition of La₂O₃, compared to the high frequency (840–1200 cm^?1) region that corresponds to the [SiO₄] structure, suggesting that the depolymerization of the low-frequency T–O–T (T=Si or Al) structure was more prevalent with La³⁺ addition. Besides, the depolymerization extent of the Si–O/Al–O tetrahedral network varied when the melt composition altered. Most notably, depolymerization is the most significant at a low CaO/SiO₂ ratio (0.25) and a high Al₂O₃ content (8%). Meanwhile, La³⁺ can promote the transformation of Si–O–Si and Al–O–Al bonds to the Si–O–Al ones, thereby forming a complex ionic cluster network interwoven with Si–O and Al–O tetrahedrons.