Separation of hematite from banded hematite jasper (BHJ) by magnetic coating

The separation of iron oxide from banded hematite jasper(BHJ) assaying 47.8% Fe, 25.6% Si O2 and 2.30%Al2O3 using selective magnetic coating was studied. Characterization studies of the low grade ore indicate that besides hematite and goethite,jasper, a microcrystalline form of quartzite, is the major impurity associated with this ore. Beneficiation by conventional magnetic separation technique could yield a magnetic concentrate containing 60.8% Fe with 51% Fe recovery. In order to enhance the recovery of the iron oxide minerals, fine magnetite, colloidal magnetite and oleate colloidal magnetite were used as the coating material. When subjected to magnetic separation, the coated ore produces an iron concentrate containing 60.2% Fe with an enhanced recovery of56%. The AFM studies indicate that the coagulation of hematite particles with the oleate colloidal magnetite facilitates the higher recovery of iron particles from the low grade BHJ iron ore under appropriate conditions.     

The effects of electrical comminution on the mineral liberation and surface chemistry of a porphyry copper ore

The surface chemistry and mineral liberation changes of a porphyry copper ore after high voltage pulse (HVP) electrical comminution have been investigated using X-ray photoelectron spectroscopy (XPS) and mineral liberation analysis (MLA). Previous studies suggest that electrical comminution has the potential to improve downstream flotation recoveries, due to increased mineral liberation. However, until now the effects on the surface chemistry have not been investigated in detail.The mineral liberation results showed that chalcopyrite was more liberated in the electrical comminution product than in mechanical comminution, noticeably in the coarser size fractions. The surface chemistry of pure chalcopyrite was investigated, using XPS, and high resolution scans of iron and sulphur showed that both comminution methods led to iron oxidising preferentially leaving behind a passivating film of copper sulphides. However, the HVP product oxidisation was more severe with more iron oxide being produced and further oxidation of the remaining copper sulphides into copper sulphate. An attrition grinding stage may be useful in removing the oxidised layer from the surface of the particles prior to flotation separation. This paper presents a new application of the HVP technology in hybrid procedures using electrical comminution and mechanical grinding to prepare the flotation feed, rather than using excessive pulse energy to fully disintegrate ore to the flotation size. Better liberation and flotation performance were achieved through the hybrid procedures than the comparative mechanical comminution.     

轧制始极片

本文介绍了轧制法生产始极片的工艺，比较了轧制法和传统的钛种板生产始极片的优缺点，讨论了采用轧制始极片的经济效益和应用前景。     

Synthesis and characterization of biocompatible hydroxyapatite coated ferrite

Ferrite particles coated with biocompatible phases can be used for hyperthermia treatment of cancer. We have synthesized substituted calcium hexaferrite, which is not stable on its own but is stabilized with small substitution of La. Hexaferrite of chemical composition (CaO)_0.75(La₂0₃)_0.20(Fe₂O₃)₆ was prepared using citrate gel method. Hydroxyapatite was prepared by precipitating it from aqueous solution of Ca(NO₃)₂ and (NH₄)₂HPO₄ maintaining pH above 11. Four different methods were used for coating of hydroxyapatite on ferrite particles. SEM with EDX and X-ray diffraction analysis shows clear evidence of coating of hydroxyapatite on ferrite particles. These coated ferrite particles exhibited coercive field up to 2 kOe, which could be made useful for hysteresis heating in hyperthermia. Studies by culturing BHK-21 cells and WBC over the samples show evidence of biocompatibility. SEM micrographs and cell counts give clear indication of cell growth on the surface of the sample. Finally coated ferrite particle was implanted in Kasaulli mouse to test its biocompatibility. The magnetic properties and biocompatibility studies show that these hydroxyapatite coated ferrites could be useful for hyperthermia.     

Ni-Al2O3纳米复合电镀工艺的初步研究

初步研究了复合电镀各工艺条件：电流密度、镀液pH值和温度以及搅拌方式对Al2O3纳米微粒在镍基复合镀层中含量的影响。研究表明：电流密度增大不利于提高镀层中纳米微粒的含量；pH值增大也明显使复合量降低;镀液温度升高，镀层中微粒的复合量随之略有改变；电镀时，加强搅拌或适当改变搅拌方式，可以使复合镀居中的纳米微粒含量提高。还利用扫描电镜及能谱对Ni-Al2O3镀层表面进行了观察与分析。     

Cu基络合物催化甲醇液相氧化羰化反应

针对甲醇液相氧化羰基化法合成碳酸二甲酯(DMC)工艺,开发了新型Cu基络合催化剂(CuB rnLm)。对CuB rnLm催化剂的活性及其稳定性进行了研究。实验结果表明,采用该催化剂,甲醇转化率和DMC选择性较高;元素价态和物质结构分析表明,CuB rnLm催化剂循环使用5次后仍保持较好的稳定性。采用正交设计和中心响应曲面法设计实验,并使用S tatistica软件进行统计分析,寻求出反应的主要影响因素,并得到优化的工艺条件:反应温度100~110℃、反应压力3.0~3.5M Pa、反应时间4~6h、CuB rnLm催化剂质量浓度(以甲醇的体积计)0.15~0.20g/mL。在此工艺条件下,甲醇转化率可达23%以上,DMC的选择性为96%~98%。     

TEM Studies of High Temperature Corrosion Behaviour of TiAl Intermetallics with Surface Modifications

The oxidation/sulphidation behaviour of a Ti‐46.7Al‐1.9W‐0.5Si alloy with a TiAl₃ diffusion coating was studied in an environment of H₂/H₂S/H₂O at 850^oC. The kinetic results demonstrate that the TiAl₃ coating significantly increased the high temperature corrosion resistance of Ti‐46.7Al‐1.9W‐0.5Si. The SEM, EDX, XRD and TEM analysis reveals that the formation of an Al₂O₃ scale on the surface of the TiAl₃‐coated sample was responsible for the enhancement of the corroison resistance. The Ti‐46.7Al‐1.9W‐0.5Si alloy was also modified by Nb ion implantation. The Nb ion implanted and as received sampels were subjected to cyclic oxidation in an open air at 800^oC. The Nb ion implantation not only increased the oxidation resistance but also substantially improved the adhesion of scale to the substrate.     

化学复合镀层激光处理研究

研究了激光处理对Ni-P -SiC化学复合镀层的影响。借助于扫描电镜、能谱仪、X射线衍射、显微硬度计等设备对激光处理后复合镀层的表面形貌、组织结构及性能进行了综合分析。结果表明 ,对复合镀层进行激光处理可以获得与炉内加热同样的镀层硬度 ,且当激光功率 4 0 0W ,扫描速度 1.5m /min时 ,镀层硬度高于炉内加热的硬度