Mechanical properties,corrosion resistance,and rubber pad forming of cold differential speed-rolled pure titanium for bipolar plates of proton-exchange membrane fuel cells

Due to problems such as pores on surface-treated coatings, the corrosion resistance of pure titanium bipolar plates for proton-exchange membrane fuel cells can be further improved by increasing the corrosion resistance of pure titanium by using differential speed-rolling (DSR); however, these materials have not yet reached the standard requirements of bipolar plates (corrosion current density i_corr＜10³ nA·cm^?2). In this work, the corrosion resistance of pure titanium was improved by optimizing the DSR process while the strength was maintained. The best corrosion resistance of the DSR pure titanium was achieved when the roller speed ratio was 2, while i_corr was 429 nA·cm^?2 in a solution of 0.5 M H₂SO₄ and 2 mg/L HF at room temperature. The formability of the DSR pure titanium for bipolar plates was verified. The optimal holding pressure range was 6.8–7.0 kN.     

Freeze-drying and mechanical redispersion of aqueous PEDOT:PSS

Poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) (PEDOT:PSS) films are attracting famous applications in antistatic coating, energy storage and conversion, printed electronics, and biomedical fields due to their conductivity, optical transparency and flexibility. However, PEDOT:PSS has poor dispersion stability during long-term storage and transport. Moreover, the dried PEDOT:PSS films are insoluble in any solvent and cannot be redispersed again. In comparison to bake drying, here, a feasible strategy to achieve mechanically redispersed PEDOT:PSS with the help of freeze-drying process was reported. The redispersed PEDOT:PSS can recover not only the initial characters such as pH, chemical composition, viscosity, and particle size under similar solid contents, but also conductivity and surface morphology of treated films. In addition, the treated film exhibits self-healing properties similar to pristine film in terms of mechanical and electrical properties. This technology enables reuse and overcomes the technical problems of PEDOT:PSS dispersion, realizing real-time processing to meet variable applications.     

Coil‐Type Asymmetric Supercapacitor Electrical Cables

Cable‐shaped supercapacitors (SCs) have recently aroused significant attention due to their attractive properties such as small size, lightweight, and bendability. Current cable‐shaped SCs have symmetric device configuration. However, if an asymmetric design is used in cable‐shaped supercapacitors, they would become more attractive due to broader cell operation voltages, which results in higher energy densities. Here, a novel coil‐type asymmetric supercapacitor electrical cable (CASEC) is reported with enhanced cell operation voltage and extraordinary mechanical‐electrochemical stability. The CASECs show excellent charge–discharge profiles, extraordinary rate capability (95.4%), high energy density (0.85 mWh cm⁻³), remarkable flexibility and bendability, and superior bending cycle stability (≈93.0% after 4000 cycles at different bending states). In addition, the CASECs not only exhibit the capability to store energy but also to transmit electricity simultaneously and independently. The integrated electrical conduction and storage capability of CASECS offer many potential applications in solar energy storage and electronic gadgets.     

Adaptive robust boundary control of shaft vibrations under perturbations with unknown upper bounds

This paper presents robust and adaptive boundary control designs to stabilize the two‐dimensional vibration of hybrid shaft model. The hybrid shaft is mathematically represented by a set of partial differential equations, governing the shaft vibrations, coupled to ordinary differential equations, describing rigid body spinning and dynamic boundary conditions. The control objective is to stabilize the transverse vibrations of the perturbed shaft while regulating the spinning rate. To achieve this, the paper first establishes robust boundary control laws that fulfil the control objective in the presence of modeling uncertainties and external disturbances operating over the shaft domain and boundary. Lyapunov‐based analyses show that the proposed robust control exponentially stabilizes the shaft with vanishing distributive perturbations, while assuring ultimately bounded vibrations in the case of nonvanishing perturbations. Then, adaptive control philosophy is utilized to achieve redesigned robust controllers that only use online adaptation of control gains without acquiring the knowledge of bounds on perturbations, as well as dynamic parameters. An advantage of this design is avoiding an overconservative robust control law, which may induce poor stability and chattering in tackling system perturbations with unknown upper bounds. Simulations through finite element method illustrate the results. Copyright © 2014 John Wiley & Sons, Ltd.     

[Zr0.73(Cu0.59Ni0.41)0.27]87Al13合金过冷液相区热塑性成形研究

为探究[Zr_(0.73)(Cu_(0.59)Ni_(0.41))_(0.27)]_(87)Al_(13)非晶合金的热塑性成形性能以及绘制其对应的热加工图谱,用Gleeble3500型热模拟压缩实验机对该非晶合金进行不同参数下的热模拟压缩实验。结果表明,合金在压缩过程中变形行为由牛顿流变演变为非牛顿流变;同时,过高或过低的热加工温度均能导致合金晶化;进一步对数据分析得到该合金在不同热塑性成形参数下的功率耗散图与流变失稳图,并绘制出相应的热加工谱图,谱图分析结果表明,该合金在温度为420与430℃、应变速率为10~(-3) s~(-1)时具有较高功率耗散系数且没有失稳区域,因此,合金可选的热塑性加工参数为温度420～430℃,应变速率10~(-3) s~(-1)。     

An efficient manufacturing method for I-shaped cross-sectional CFRP beam with arbitrary arrangement of carbon fiber using electro-activated resin molding

Abstract

The I-shaped cross-sectional beam of CFRP (CFRP I-beam) is usually manufactured by the continuous protrusion method. Carbon fibers can only be arranged in the longitudinal direction. The CFRP I-beam with arbitrary arrangement of carbon fiber was manufactured with applying the electro-activated deposition molding method. The carbon fiber fabric was immersed in the deposition solution and energized, epoxy resin precipitated around carbon fiber and impregnated. The resin-impregnated fabric was installed to the mold, and the CFRP I-beam was fabricated. The CFRP I-beam was subjected to three-point bending tests, and the relationship between load-deflection was simulated by finite-element analysis.     

Bulging in incremental sheet forming of cold bonded multi-layered Cu clad sheet: Influence of forming conditions and bending

Bulge is a defect that causes geometrical inaccuracy and premature failure in the innovative incremental sheet forming (ISF) process. This study has two-fold objectives: (1) knowing the bulging behavior of a Cu clad tri-layered steel sheet as a function of forming conditions, and (2) analyzing the bending effect on bulging in an attempt to identify the associated mechanism. A series of ISF tests and bending analysis are performed to realize these objectives. From the cause-effect analysis, it is found that bulge formation in the layered sheet is sensitive to forming conditions in a way that bulging can be minimized utilizing annealed material and performing ISF with larger tool diameter and step size. The bending under tension analysis reveals that the formation of bulge is an outgrowth of bending moment that the forming tool applies on the sheet during ISF. Furthermore, the magnitude of bending moment depending upon the forming conditions varies from 0.046 to 10.24 N·m/m and causes a corresponding change in the mean bulge height from 0.07 to 0.91 mm. The bending moment governs bulging in layered sheet through a linear law. These findings lead to a conclusion that the bulge defect can be overcome by controlling the bending moment and the formula proposed can be helpful in this regards.     

东营凹陷王庄-宁海地区流体包裹体分析与流体充注研究

利用流体包裹体分析技术，系统地分析了东营凹陷王庄-宁海地区覆盖所有含油层位的流体包裹体样品。包裹体荧光观察和均一温度特征分析揭示了包裹体发育期次为5期，说明该区油藏存在5次流体充注过程；据此确定了备期烃类的成藏期次。东营组沉积时期和明化镇组沉积末期的油气运聚均在成藏后遭受大气淡水淋滤和降解作用。沙三段原油可能经历至少2期稠油化作用。荧光观察进一步证实该区主要发生2期充注、2期成藏。     

柔性联轴节在减小转子系统扭转冲击运动中的作用

通过对大型振动磨机运动特性的研究分析,把其旋转系统简化为由两个柔性联轴节连接的三转子系统。建立了柔性连接的三转子系统在冲击转矩作用下的运动方程,对方程求解得到了柔性连接转子系统的扭转冲击响应。通过对冲击响应随柔性联轴节扭转刚度和阻尼变化规律的讨论分析,发现减小柔性联轴节的扭转刚度和增大柔性联轴节的阻尼,可以减小转子系统的扭转冲击响应。