Cr对低碳Si-Mn系TRIP钢组织与力学性能的影响

主要研究了Cr对低碳Si-Mn系TRIP钢组织与力学性能的影响。首先利用Formastor-F型膨胀仪测定了含Cr和不含Cr两种低碳钢的连续冷却转变(CCT)曲线,分析指出了Cr对连续退火工艺的潜在影响;然后采用Gleeble-3800热/力模拟试验机对两种钢的薄板试样进行了连续退火模拟实验,并通过拉伸试验测定了力学性能;最后采用金相、扫描电镜、X-射线衍射分析等技术考察分析了两种钢的显微组织。结果表明:含Cr的TRIP钢的组织比较细小,铁素体晶粒近似等轴分布;两种TRIP钢的残余奥氏体含量相近,但含Cr钢的残余奥氏体中的含碳量较高。分析认为这是由于含Cr钢在热轧阶段较易生成细小的组织,而在热处理阶段则抑制贝氏体的生成,最终获得稳定的残余奥氏体。     

珠钢不锈钢冶炼技术探讨

本文阐述了不锈钢冶炼的关键技术，为生产准备提供帮助。     

Transport of chromium(VI) through a Cyanex 921‐supported liquid membrane from HCl solutions

The transport of chromium(VI) through a flat‐sheet supported liquid membrane containing Cyanex 921 as a carrier has been investigated. The permeation of the metal is investigated as a function of various experimental variables: hydrodynamic conditions, concentration of chromium(VI) and HCl in the feed phase, carrier concentration and diluent in the membrane and strippant concentration in the stripping phase. The mass transfer coefficient and the thickness of the aqueous boundary layer were calculated from the experimental data. Furthermore, the selectivity of Cyanex 921‐based flat‐sheet supported liquid membrane towards different metal ions and the behaviour of the system against other carriers are presented. Copyright © 2003 Society of Chemical Industry     

Modified Imidazoles: Degradation Inhibitors and Adhesion Promoters for Polyimide Films on Copper Substrates

Polyimide films on copper substrates that are exposed to elevated temperatures and an oxidizing environment will be subject to degradation. In order to halt this degradation without changing the properties of the system, a polymeric agent could be placed between the polyimide and the copper. This paper will investigate three such materials that will not only slow down the degradation of the polyimide and the oxidation of the copper, but will also improve adhesion within the system. Fourier transform infrared reflection-absorption spectroscopy (FTIR-RAS) will be used to investigate the polyimide/polymeric agent/copper system.     

不锈钢冶炼过程中相关热力学问题的解析(Ⅰ)--原料预处理时的热力学问题

针对“电弧炉 多功能转炉 VOD”三步法不锈钢冶炼工艺，以脱磷为主线，从冶金热力学的角度对流程中涉及的几个重要工艺环节的可行性(包括电弧炉去硅保铬、铁水包同时脱磷脱硫等问题)进行了理论分析和计算。在此基础上，提出了强化冶炼和脱磷的工艺措施，从而为不锈钢冶炼全流程控制磷及优化脱磷工艺提供了理论依据。     

碳铬镍含量对高铬铸铁测温保护管性能的影响

通过高温氧化和高温磨损实验,研究了C、Cr、Ni 3个主要元素对高铬铸铁在高温条件下抗氧化和抗磨损性能的影响。结果表明:Cr含量越高,抗氧化性能和抗磨损性能越好;提高碳含量,明显提高高铬铸铁的高温抗磨性能;当w(Cr)=16％时,加入Ni能提高高铬铸铁的高温抗氧化性能;w(Cr)=30％时,Ni对高铬铸铁的抗氧化性能和抗磨损性能影响不明显.在1100℃以下,选用w(C)=2.8％,w(Cr)=30％、不加Ni的高铬铸铁铸造高温抗磨热电偶保护管,既有较好的使用寿命,又可降低成本.     

Effect of Rare Earth Elements on Thermal Fatigue Property of Low Chromium Semi-Steel

The effect of rare earth elements on eutectic carbide‘s morphology of low chromium semi-steel in as-cast state and after heat treatment was investigated, and accordingly, the thermal fatigue property of this material was studied. The results show that RE can improve the eutectic carbide‘s morphology, inhibit the formation and propagation of thermal fatigue cracks, therefore, promote the thermal fatigue property, which is more noticeable in case of the RE modification in combination with heat treatment. The optimal thermal fatigue property can be obtained when treated with 0.2% RE modification as well as normalization at 950℃ for 3h.     

Contact interaction of double titanium and chromium diboride with Fe-Cr alloys

The kinetics of wetting double titanium and chromium diboride by iron-based alloys with different chromium content is studied. It is shown that contact angles are formed in such systems over the range 0–10°. The energy parameters of wetting are calculated. It is established that chromium as a surface-active element promotes Fe-Cr alloy spreading on the diboride surface. The microstructure of the interaction area is studied. It is shown that terminal solid solutions and eutectics are formed in the TiCrB₂-(Fe-Cr) system. The optimum compositions of the metallic binder are determined for TiCrB₂-based composite materials. __________ Translated from Poroshkovaya Metallurgiya, Vol. 46, No. 1–2(453), pp. 109–115, 2007     

摩擦诱发高铬铸铁相变的透射电镜研究

利用透射电子显微镜研究了高铬铸铁在摩擦过程中的显微组织变化。结果表明：奥氏体基体在摩擦应力的作用下发生相变。摩擦表面形成α‘Ｍ。次表层形成γ与α’Ｍ共存区；γ与．ε共存区；γ位错丛聚区。     

Analysis of the effect of polypyrrole synthesis conditions on its capacity to reduce hexavalent chromium

This paper reports the capacity of polypyrrole to reduce toxic hexavalent chromium (Cr(VI)). The influence of using different electrolytes during the polymer's synthesis has been studied. To improve the reduction of Cr(VI), the parameters considered were the polypyrrole morphology and the amount of conducting polymer. Polypyrrole obtained by cyclic voltammetry at a low sweep rate using KBr as supporting electrolyte showed better performance for Cr(VI) reduction compared to coatings obtained by constant potential or cyclic voltammetry at high sweep rates.