Impact of gypsum on flotation of scheelite and fluorite using sodium oleate as collector

ABSTRACT

In this study, effect of calcium and gypsum on scheelite and fluorite was investigated using sodium oleate as collector. Micro-flotation and contact angle results showed that the adsorption of calcium could inhibit the hydrophobicity of scheelite and fluorite. Moreover, sulfate could enhance the inhibition. FT-IR results showed that calcium could be priori precipitated into calcium oleate and adsorb on mineral surface. The adsorption of calcium could increase the scheelite potential to IEP, while it showed limited effect on fluorite potential. However, the interaction of calcium on scheelite and fluorite in gypsum solution was more complex than that in calcium solution.     

石膏转化制硫酸钾结晶动力学及结晶添加剂研究

研究了浓氨介质中石膏与氯化钾直接转化制硫酸钾的结晶动力学及结晶添加剂的作用效果。结果表明 ,硫酸钾在氨介质中的成核速率与晶体生长速率、悬浮密度、搅拌速率存在如下关联式 :B0 =5 .64 13×10 8G3.32 0 8Mt0 .0 559np0 .2 92 8。加入异丙醇、OP乳化剂及十二烷基苯磺酸钠等添加剂 ,可使硫酸钾结晶产品纯度提高 ,晶体形态整齐均匀     

Continuous precipitation of calcium sulfate dihydrate from waste sulfuric acid and lime

Precipitation of calcium sulfate dihydrate, gypsum, from (i) a pure sulfuric acid/lime suspension and (ii) a waste sulfuric acid/lime suspension in a continuous pilot plant in the temperature range from 40 °C to 80 °C was studied. It was observed that in the case of waste sulfuric acid with a high content of Mg²⁺ and Fe²⁺ ions, several hours after the beginning of the precipitation, partial dissolution of the product and modification of the crystals from needle‐ and plate‐like to agglomerated structures occurred. It is suggested that the secondary changes occur due to the increased concentration of Mg²⁺ and Fe²⁺ ions in the reactor. Below 60 °C, and above 70 °C plate‐like and needle‐like single crystals respectively were formed. The mean size (d₅₀) of the crystals was found to increase with increasing temperature and decrease with the initial concentration of lime. Gypsum produced between 70 °C and 80 °C is suitable for further processing for construction plaster. In a precipitation process with pure sulfuric acid only single perfect needle‐like crystals occurred. Copyright © 2005 Society of Chemical Industry     

Observation and Analysis of Gypsum Particleboard using SEM

The microstructures of gypsum board and gypsum particleboard were observed by SEM. The effects of retarder and waterproof agent on the shape and the average dimension of the gypsum crystal were discussed. The mechanism was investigated as well. Four typical instances, i e, the gypsum crystal shape, the gypsum combined with particles on the particles surface, the gypsum combined with particles on the wood cross section and the gypsum combined with particles inside the wood cell cavity were selected and observed. Furthermore, the agglomeration and cementation mechanism between gypsum and particle were studied.     

亚硫酸钙氧化为石膏的研究

进行了亚硫酸钙氧化为二水石膏的研究 ,考察了初始 p H值、反应温度、空塔气速、固含量和停留时间对氧化率的影响 ,给出了适宜的反应条件 .在这些条件下 ,氧化率达 96 %以上     

石膏制品防水防潮剂的研制与开发

本文提出采用高分子有机材料配合，生产石膏制品防水防潮剂的生产方法和工艺。该剂还可以应用到氧化镁系列板材，同时提出开发珠光或彩色防水防潮剂，能达到满足的装饰效果，值提开发推广。     

几种添加剂对模型石膏性能的影响

研究了N型减水剂、硅溶胶等添加剂对模型石膏凝结时间、强度、吸水率、溶蚀率等性能的影响,并确定了有关性能与添加量之间的关系,得出了最佳添加量。     

Laboratory study of air-water-coal combustion product (fly ash and FGD solid) mercury exchange

Recent laboratory research has indicated that coal fly ash derived from subbituminous and bituminous type coals is a sink for atmospheric mercury (Hg), however lignite-based ash was found to emit Hg to the air. Solids collected from systems with components that enhance Hg removal (i.e. activated carbon injection (ACI), flue gas desulfurization (FGD), and selective catalytic reduction (SCR) or selective non-catalytic reduction (SNCR)) may have higher Hg concentrations and therefore a higher potential for Hg release. For this study we investigated the potential for Hg release to the air and water from coal combustion products (CCPs) collected from coal-fired units with FGD equipment, SCR and SNCR equipment, and sorbent injection for Hg removal. In the laboratory study, most dry samples acted as sinks for atmospheric Hg in the dark at 25 °C. When exposed to light or increased temperature (45 °C), deposition of Hg to the fly ash substrates in most cases continued but decreased. Wet FGD samples emitted Hg. However, they became a sink for atmospheric Hg or exhibited low Hg emission rates when dried. Mercury flux in the dark at 25 °C was correlated with fly ash carbon content (LOI). Most liquid extracts derived using the synthetic precipitation leaching procedure (SPLP EPA method 1312) had very low Hg concentrations (<13 ng/l).     

高纯天然石膏水热法制备硫酸钙晶须研究

以高纯天然石膏为原料，加压水热法制备高品质硫酸钙晶须。采用常规分析方法、XRD和扫描电镜等手段分析和表征石膏原料和硫酸钙晶须产品。结果表明，制备硫酸钙晶须的最优条件为：料浆质量分数为6.0%，转晶剂氯化镁加入量为石膏质量的0.05%，硫酸加入量为水体积的1.0%，反应时间为4.0 h，快速过滤干燥即得硫酸钙晶须产品。分析结果表明：硫酸钙晶须长度最大为280.4 μm，最小为19.59 μm，平均长度为80 μm；硫酸钙晶须直径最大为5.86 μm，最小为0.20 μm，平均直径为2.67 μm；通过统计分析可知，长径比范围为10～80。     

3000m~3/h排烟循环流化床脱硫工艺中试实验研究

介绍了采用真实烟气的 30 0 0m3 /h排烟循环流化床烟气脱硫工艺 (CFB FGD)及其中间试验装置 ,通过实验研究了钙硫摩尔比 (Ca/S)、近绝热饱和温度差 (ΔT)、烟气湿度、喷水量、入口SO2 浓度、浆液雾化质量、脱硫灰循环等对脱硫效果的影响。实验表明 ,CFB FGD工艺在停留时间小于 6s、烟气流速v =4— 6m/s、Ca/S =1.2、ΔT =10— 12℃时可实现高达 90 %的脱硫效率。