基于压电陶瓷动态信息的结构裂纹识别方法

利用压电陶瓷的动态特性和压电系统的动态信息,对铝梁的裂纹损伤进行了分析研究。随着梁裂纹尺寸的增加,压电陶瓷片的导钠幅值下降,且系统固有频率减小。利用导钠幅值的变化和系统的动态信息,可以对裂纹的位置和尺寸大小进行识别。实验证明该方法的有效性。     

Synthesis and characterization of biocompatible hydroxyapatite coated ferrite

Ferrite particles coated with biocompatible phases can be used for hyperthermia treatment of cancer. We have synthesized substituted calcium hexaferrite, which is not stable on its own but is stabilized with small substitution of La. Hexaferrite of chemical composition (CaO)_0.75(La₂0₃)_0.20(Fe₂O₃)₆ was prepared using citrate gel method. Hydroxyapatite was prepared by precipitating it from aqueous solution of Ca(NO₃)₂ and (NH₄)₂HPO₄ maintaining pH above 11. Four different methods were used for coating of hydroxyapatite on ferrite particles. SEM with EDX and X-ray diffraction analysis shows clear evidence of coating of hydroxyapatite on ferrite particles. These coated ferrite particles exhibited coercive field up to 2 kOe, which could be made useful for hysteresis heating in hyperthermia. Studies by culturing BHK-21 cells and WBC over the samples show evidence of biocompatibility. SEM micrographs and cell counts give clear indication of cell growth on the surface of the sample. Finally coated ferrite particle was implanted in Kasaulli mouse to test its biocompatibility. The magnetic properties and biocompatibility studies show that these hydroxyapatite coated ferrites could be useful for hyperthermia.     

TEM Studies of High Temperature Corrosion Behaviour of TiAl Intermetallics with Surface Modifications

The oxidation/sulphidation behaviour of a Ti‐46.7Al‐1.9W‐0.5Si alloy with a TiAl₃ diffusion coating was studied in an environment of H₂/H₂S/H₂O at 850^oC. The kinetic results demonstrate that the TiAl₃ coating significantly increased the high temperature corrosion resistance of Ti‐46.7Al‐1.9W‐0.5Si. The SEM, EDX, XRD and TEM analysis reveals that the formation of an Al₂O₃ scale on the surface of the TiAl₃‐coated sample was responsible for the enhancement of the corroison resistance. The Ti‐46.7Al‐1.9W‐0.5Si alloy was also modified by Nb ion implantation. The Nb ion implanted and as received sampels were subjected to cyclic oxidation in an open air at 800^oC. The Nb ion implantation not only increased the oxidation resistance but also substantially improved the adhesion of scale to the substrate.     

Evaluation of the Properties of Si3N4/Si3N4 Joint Brazed Using a Filler Alloy Containing Pd

Si3N4 ceramic was jointed to itself using a filler alloy of Cu76.5Pd8.5Ti15, and the mechanical properties of the jointwere measured and analyzed. By using a filler alloy of Cu76.5Pd8.5Ti15, the SisN4/SisN4 joints were obtained bybrazing at 1373～1473 K f     

化学复合镀层激光处理研究

研究了激光处理对Ni-P -SiC化学复合镀层的影响。借助于扫描电镜、能谱仪、X射线衍射、显微硬度计等设备对激光处理后复合镀层的表面形貌、组织结构及性能进行了综合分析。结果表明 ,对复合镀层进行激光处理可以获得与炉内加热同样的镀层硬度 ,且当激光功率 4 0 0W ,扫描速度 1.5m /min时 ,镀层硬度高于炉内加热的硬度     

T8钢－聚有机硅氧烷仿生减粘降阻复合涂层的特性

研究了Ｔ８钢－聚有机硅氧烷仿生减粘降阻复合涂层的表面润湿性、磨料磨损特性及对土壤的减粘降阻性能与金属材料相比，仿生复合涂层的表面憎水性显著提高，水在其表面上的接触角达９２°；与４５钢相比，其磨料磨损的体积相对耐磨系数为６３％，降阻率达１５．２２％～２２．２７％     

Improving Wear Resistance of the Ni-base Thermal Spray-Welding Coating Using Rare Earths

ＩｍｐｒｏｖｉｎｇＷｅａｒＲｅｓｉｓｔａｎｃｅｏｆｔｈｅＮｉｂａｓｅＴｈｅｒｍａｌＳｐｒａｙＷｅｌｄｉｎｇＣｏａｔｉｎｇＵｓｉｎｇＲａｒｅＥａｒｔｈｓＺｈａｉＧｕａｎｇｊｉｅ（翟光杰）（ＩｎｓｔｉｔｕｔｅｏｆＰｈｙｓｉｃｓ，ＡｃａｄｅｍｉｃａＳｉ...     

埋地管道涂层检测技术现状

文章对各种埋地管道涂层检测技术进行了综述,并指出了各种技术的优缺点及应用前景.     

提高自蔓延高温合成陶瓷内衬钢管性能的研究

在概括了自蔓延高温合成陶瓷内衬钢管的制备原理基础上，从降低陶瓷层孔隙率，减少陶瓷层裂纹和提高陶瓷层结合强度等方面，论述了提高自蔓延高温合成陶瓷内衬钢管性能的措施，对自蔓延高温合成陶瓷内衬钢管的应用现状及展望进行了评述。     

Preparation and properties of novel polyurethane insulating coatings based on glycerin‐terminated urethane prepolymers and blocked isocyanate

Novel polyurethane insulating coatings were prepared from the reaction of glycerin‐terminated polyurethane prepolymers (GPUPs) and a blocked isocyanate curing agent (BIC). The GPUPs were prepared from the reaction of one equivalent of polycaprolactone polyol (CAPA 210) with an excess amount of 4,4′‐methylene bis(phenyl isocyanate) (MDI) and subsequent reaction of the NCO‐terminated polyurethane with glycerin. The BIC was prepared from the reaction of trimethylol propane (TMP), toluene diisocyanate (TDI) and N‐methylaniline (NMA). The polyols and curing agent were characterized by conventional methods while the curing condition was optimized via gel content measurements. The curing kinetics of the polyurethane coating were investigated and the kinetic parameters derived. The crosslink densities of the samples were determined via the equilibrium swelling method, using the Flory–Rehner equation. The relationships between the crosslink density and the electrical, physical, mechanical and dynamic mechanical properties of the coatings were also studied. Copyright © 2005 Society of Chemical Industry