Effect of Biochar as Reductant on Magnetizing-roasting Behavior of Pyrite Cinder

The effect of biochar substituted for anthracite as reductant on magnetizing-roasting pyrite cinder was investigated.The key of magnetizing-roasting is the gasification reaction between reductants and CO2.Since biochar could react with CO2 more rapidly at lower temperature,the reactivity of biochar is better than that of anthracite.The gasification of biochar could produce reducing condition ofφCO/(φCO+φCO2)about 10%-20% between 700-800 ℃,which is in accord with the atmosphere and temperature of Fe2O3 reduction.So it is beneficial to the reduction of iron mineral of pyrite cinder.Compared with anthracite,biochar could decrease the roasting temperature from825 to 750 ℃ and roasting time from 20 to 15min,which shows that a better effect of magnetization could be obtained in the condition of lower temperature and shorter time.Using biochar as reductant,iron concentrate extracted from pyrite cinder as about 64%iron grade could be produced,and the recovery is over 90% under the condition of above 90% grinding particle less than 0.045 mm and magnetic intensity of 0.124-0.194 T.     

Scale Up from Small Oven-Drying Tests of Mineral Concentrate to Pilot-Scale Drying with a Heated Pad

While Fickian diffusion models are commonly used in other applications, there are few reports of them being applied to the batch drying of a mineral concentrate. Diffusion coefficients estimated from small-scale oven-drying tests were used to predict the drying behavior of a concentrate sample 1 m × 1 m in area and 50 cm deep, with a heated bottom pad. These pilot-scale tests included both daily turning of the sample and turning every three days. The excellent quantitative agreement between the predicted and observed pilot-scale behavior gives a high level of confidence in the model predictions and suggests that a Fickian diffusion model is adequate to predict the behavior of mineral concentrates at the low moisture contents used here.     

用硫酸铁铵容量法测定钛精矿中二氧化钛含量

样品在过氧化钠熔融、水浸取及盐酸酸化后，在盐酸和硫酸介质中，隔绝空气，用金属铝将钛(Ⅳ)还原至钛(Ⅲ)，以硫氰酸盐为指示剂，用硫酸铁铵标准溶液滴定。     

锌精矿制粒沸腾焙烧新工艺的应用与改进

介绍了锌精矿制粒沸腾焙烧新工艺的工业化生产应用与技术改进情况 ,阐述了取得的成果及存在的问题     

钛精矿回转窑直接还原过程结圈可能性的探讨

通过煤种，入窑球冷态强度和还原过程强度，以及钛精矿与煤灰混合物的软化温度等分析探讨了钛精矿预热球团回转窑直接还原产生结圈的可能性，获得了可以避免结圈的结论。     

影响铁精矿K2O、Na2O、SiO2含量的因素分析

用统计分析方法 ,分析了影响精矿K2 O、Na2 O、SiO2 含量的因素 ,并根据分析结论提出了对生产工艺进行定向控制的条件     

硫铁矿沸腾炉内蒸发管组防磨技术的探讨

为减少磨损,沸腾炉内蒸发管采用加焊半圆形钢板防磨.探讨了沸腾炉内蒸发管加焊半圆形钢板的防磨机理.实际使用情况表明,加焊半圆形钢板防磨大大降低了维修费用,显著提高了防磨效果.     

包钢选矿厂降低铁精矿中氟含量的技术攻关

为了降低铁精矿氟含量,通过采取控制磨矿粒度、改进浮选工艺、采用高效捕收剂等措施,使包钢选矿厂铁精矿氟含量由1999年的0.75%降低到2000年的0.65%、2001年的0.58%,为包钢环保工作目标的完成做出了突出贡献.