6种金属材料在典型工业大气中的腐蚀规律

选取具有代表性的碳钢、不锈钢、镀锌碳钢、铝、钛和铜挂片,在某企业不同部位投放后进行为期半年的大气腐蚀试验,得出了在半年期中的腐蚀规律。在此基础上,对每种金属材料的腐蚀特点进行总结,并对大气腐蚀的各种影响因素进行分析,提出了行之有效的防护措施。     

井下乳化/水热催化裂解复合降黏开采稠油技术研究

实验考察了胜利孤东稠油井下催化水热裂解和乳化/催化水热裂解降黏效果。所用催化剂为水溶性铁镍钒体系,Fe3+∶Ni2+∶VO4+=5∶1∶1,100 g稠油与30 g 0.5%催化剂水溶液在240℃反应24小时。原始黏度(50℃)11.0和8.36 Pa.s的两种稠油裂解并静置除水后,黏度降低76.2%和75.6%,室温放置60天后降黏率下降小于3个百分点,气相色谱显示裂解后轻组分明显增加,红外光谱显示稠油组分发生脱羧反应且芳环数减少。讨论了稠油催化水热裂解反应机理。所用化学助剂JN-A在油水中均可溶,耐温达250℃,耐矿化度达50 g/L,其水溶液以30∶100的质量比与稠油混合时形成低黏度的O/W乳状液。当水相含1.0%JN-A和0.5%催化剂时,两种稠油水热裂解后的反应混合物为O/W乳状液,黏度仅为319和309 mPa.s,静置除水后的稠油降黏率增加到86.5%和87.3%,其中的轻组分含量进一步增加。该井下乳化/催化水热裂解复合降黏法成功地用于孤东两口蒸汽吞吐井,稠油井作业后初期采出的原油黏度由~9 Pa.s降低到1 Pa.s左右,随采油时间延长而逐渐升高,约50天后超过4Pa.s。图2表6参5。     

River Bifurcation Analysis by Physical and Numerical Modeling

In the framework of a river regulation design of the Po River Delta (Northern Italy), a study on a large physical model of the bifurcation Po di Goro-Po di Venezia was conducted with the main objective of determining the discharge subdivision rate at the river node, in order to assess the inflow conditions in the Po di Goro River for flood risk analysis. In this context, a two-dimensional depth averaged numerical model was tested against measured values, with reference to the prototype. In this paper a comprehensive analysis and discussion of the results is reported in order to highlight the applicability of numerical models in comparison with physical ones in river engineering applications.     

石油沥青60℃动力粘度测定影响因素的探讨

粘度是表征沥青稠度的一个重要指标。通过论述石油沥青粘度测定法(真空毛细管法)中毛细管的选择、温度、真空度、取样量等对试验结果的影响及试验过程中的其它注意事项,表明了在测定石油沥青的60℃动力粘度时,必须严格按照试验方法的要求进行测定,以保证试验结果的准确性。     

Intramolecular crosslinking of poly(vinyl alcohol)

Poly(vinyl alcohol) is crosslinked in dilute solution (c=0.1 wt%) with glutaraldehyde. The reaction product is characterized by viscometry and gel permeation chromatography (g.p.c.). The intrinsic viscosity decreases with increasing degree of crosslinking and does not depend on temperature. G.p.c. reveals that the reaction product is not homogeneous, but consists of a mixture of particles with different sizes, possibly both intra- and intermolecularly crosslinked molecules. The intramolecularly crosslinked molecules are smaller in size than the initial polymer molecules and their size depends on the degree of crosslinking. They possess a narrow particle size distribution even if the initial polymer sample had a broad molecular weight distribution.     

Properties of Carbopol Solutions as Models for Yield-Stress Fluids

ABSTRACT: The effect of pH on the non-Newtonian viscosity (η)of aqueous Carbopol 940 solutions is presented with high resolution (pH increments about 0.4) between pH = 2.8 and 12.7. Aqueous NaOH was used to adjust pH of 1.48 wt % Carbopol solutions. A Contraves viscometer was used to measure steady-flow shear stress at known shear rate (γ) over the range γ= 8 to 195 s⁻¹. Yield stresses and shear-thinning η(γ) were observed. Data were fitted with a Herschel-Bulkley model, whose parameters (including yield stress) were expressed as functions of pH. Comparisons were made of η(γ) to the dynamic viscometric properties η'(ω) and η*(ω) for comparable ranges of γ and frequency (ω): A fairly close match was found between η and η* but η«η'. pH dependence included previously unreported extrema of h(pH) in the range of pH = 6.2 to 6.6. Because of sensitive control of rheological properties with pH, Carbopol solutions can be used to mimic a great range of shear-thinning and yield-stress behavior that should make them useful for model studies directed toward process and equipment design and evaluation.     

交联透明质酸的降解及其释药性能

用己二酸二酰肼（ADH）对透明质酸（HA）进行化学修饰，制备交联透明质酸（HA-ADH）薄膜。粘度法测试表明HA-ADH是一种可降解的生物材料，并且与HA相比，HA．ADH的降解速率减慢。在此基础上，研究了以疏水性的替硝唑（TDZ）和亲水性的头孢唑啉钠（CEZ）为模拟药物的HA-ADH药物载体薄膜的释药性能。紫外-可见（UV-Vis）吸收光谱检测表明，HA-ADH是一种疏水性药物TDZ的优良缓释制荆，这是由于TDZ的疏水性和HA-ADH薄膜的缓慢溶胀和降解性能的结合而得到的，药物的释放主要受扩散机制控制。     

稀土改善09CuPTiRE耐候钢耐蚀性的作用机理

应用扫描电镜(SEM)、离子探针(IMA)、X射线光电子能谱(XPS)和交流阻抗法研究含不同稀土耐候钢稀土提高耐大气腐蚀作用机理。结果表明,合适的稀土含量可显著提高钢的耐腐蚀性,稀土能促进Si、Cu和P在内锈层中以Si~(4+)、Cu~+和P~(5+)形态富集,并观察到锈层中的稀土。钢中加入稀土形成了致密连续厚而粘附性好的含硅铜稀土的复合铁锈层,从而提高了抗大气腐蚀性能。     