Plasma-assisted CO2 reforming of methane over Ni-based catalysts: Promoting role of Ag and Sn secondary metals

Carbon dioxide (CO₂) and methane (CH₄) are the primary greenhouse gases (GHGs) that drive global climate change. CO₂ reforming of CH₄ or dry reforming of CH₄ (DRM) is used for the simultaneous conversion of CO₂ and CH₄ into syngas and higher hydrocarbons. In this study, DRM was investigated using Ag–Ni/Al₂O₃ packing and Sn–Ni/Al₂O₃ packing in a parallel plate dielectric barrier discharge (DBD) reactor. The performance of the DBD reactor was significantly enhanced when applying Ag–Ni/Al₂O₃ and Sn–Ni/Al₂O₃ due to the relatively high electrical conductivity of Ag and Sn as well as their anti-coke performances. Using Ag–Ni/Al₂O₃ consisting of 1.5 wt% Ag and 5 wt% Ni/Al₂O₃ as the catalyst in the DBD reactor, 19% CH₄ conversion, 21% CO₂ conversion, 60% H₂ selectivity, 81% CO selectivity, energy efficiency of 7.9% and 0.74% (by mole) coke formation were achieved. In addition, using Sn–Ni/Al₂O₃, consisting of 0.5 wt% Sn and 5 wt% Ni/Al₂O₃, 15% CH₄ conversion, 19% CO₂ conversion, 64% H₂ selectivity, 70% CO selectivity, energy efficiency of 6.0%, and 2.1% (by mole) coke formation were achieved. Sn enhanced the reactant conversions and energy efficiency, and resulted in a reduction in coke formation; these results are comparable to that achieved when using the noble metal Ag. The decrease in the formation of coke could be correlated to the increase in the CO selectivity of the catalyst. Good dispersion of the secondary metals on Ni was found to be an important factor for the observed increases in the catalyst surface area and catalytic activities. Furthermore, the stability of the catalytic reactions was investigated for 1800 min over the 0.5 wt% Ag-5 wt% Ni/Al₂O₃ and 0.5 wt% Sn-5 wt% Ni/Al₂O₃ catalysts. The results showed an increase in the reactant conversions with an increase in the reaction time.     

Effect of heat treatment and zircon addition on the properties of low-cement castables based on recycled alumina grog

In this investigation, low-cement castables were prepared using 70% alumina grog aggregates obtained from crushed alumina brick waste. The aggregates were thermally treated at 1550 °C for 3 h. Four types of low-cement castables were prepared with various types of aggregates (alumina grog with or without thermal treatment) and fillers (with or without zircon addition), and they were evaluated in terms of their physical, thermal, and chemical properties. Microstructural analysis via scanning electron microscopy (SEM) was performed on the castables before and after slag attack. Compared to the other fabricated castables, the thermally treated alumina grog castables with zircon showed better physical properties, such as a higher bulk density, cold crushing strength, and modulus of rupture and a lower apparent porosity and water absorption. In addition, they had a higher positive linear thermal expansion, refractoriness under load, permanent linear change, and hot modulus of rupture. The results of the SEM with energy dispersive X-ray analysis of the prepared castables confirmed that the mullite and anorthite phases were predominant when zircon was not added and the zircon–mullite phase additionally appeared upon the incorporation of zircon. A quantitative elemental analysis via X-ray fluorescence spectroscopy was employed to determine the composition of the castables. X-ray diffraction analysis showed that the alumina grog castables had a high mullite and low anorthite content, and the thermally treated alumina grog had a high anorthite, low mullite, and high zircon content. The improvement in the mechanical and thermo-mechanical properties of the castables with thermally treated alumina grog and added zircon can be attributed to the formation of the zircon–mullite phase with a low mullite phase content.     

Preparation and antifouling performance of thin inorganic ultrafiltration membrane via assisted sol-gel method with different composition of dual additives

A novel TiO₂ thin film was prepared on the ceramic hollow fiber by the sol-gel method using poly(vinylpyrrolidone) (PVP) and polyvinyl alcohol (PVA) as additives. SEM images verified the formation of TiO₂ layer with various thickness using different composition of titania sols. The effect of the PVP and PVA contents on the TiO₂ sol properties, the separation and the antifouling performance of the ultrafiltration membranes were investigated thoroughly. When the contents of PVP and PVA were 1.0 wt% and 0.8 wt%, respectively, the resultant membrane showed a thickness of 0.55 μm with a pure water flux of 255 L m^?2 h^?1. In addition, the adherent foulant bovine serum albumin was applied to evaluate the antifouling performance. During the three fouling-recovery cycles, the flux recovery ratio and the flux decay ratio maintained about 99% and 30%. The BSA flux and rejection were still 169 L m^?2 h^?1 and 96.9% after the cycles, indicating a superior antifouling property.     

Performance of surface ionic conduction single chamber fuel cell prepared by the sol gel method

The performance of surface ionic conduction single chamber fuel cell (SIC‐SCFC) prepared by the sol gel method was studied on electric characteristics due to the differences of the operating temperature and humidity, the electrode distance and electrolyte film depth, and multiple cells with the series and parallel connections. The SIC–SCFC was arranged the both anode of Pt and cathode of Au on the boehmite electrolyte. The open circuit voltage (OCV) of single cell achieved a maximum of 530mV in the dry gas mixtures of O₂/H₂=50% in room temperature operation, and but it became decrease as over 60%. The OCV was maintained the constant value between operating temperatures of 30°C to 80°C, and but it was decreased sharply at over 90°C because a humidity on the cell became lower as increasing operating temperature. Then, the cell property was improved to 120°C by adding to the humidity of 70% using a humidifier. The electrode distance and the electrolyte film depth of SIC‐SCFC found to be contributed to the reductions of the cell resistance and the surface roughness on the electrode, respectively. Moreover, the power property of SIC‐SCFC was significantly improved by cell stacks comprised of the series or parallel connection of a cell.     

Polymers dynamics of the nonfluoro,nano-brush repelling agent with self-stratifying property in water-based coatings

While perfluoroalkyl acids (PFAAs), also known as C8s, are used extensively in textile repellent coatings, concerns have arisen for their carcinogenicity and hazardous effects on the environment. In this study, a novel water-based, nonfluoro, and nanobrush textile repelling agent was prepared by conventional sol–gel chemistry using amorphous fumed silica and n-octyltriethoxysilane as the starting materials. Minimal interaction between the designed repelling agent and marketed water-based resins was confirmed using linear viscosity region (LVR) analysis and asymmetric-flow field-flow fractionation (AF4), suggesting the self-stratification potential of the repelling agent. More specifically, the repelling agent exhibited excellent compatibility and self-stratifying ability with a force-emulsified acrylic-based resin, affording a water contact angle of 104.3° when incorporated at 7% solid content. Performance tests carried out on thermoplastic polyurethane (TPU) revealed excellent adhesion (100/100) of a final formulation, and a significant increase in water contact angle from 80.1° to 103.8° after treatment. In addition, the fouling area after the removal of a submerged sample from a mixture of slurry, polymer, and oil decreased from 48 to 1% when the repelling agent was added. Moreover, the sludge-fouling property remained unchanged after 1000 cycles of abrasion. These findings demonstrate the potential of the described nonfluoro, nanobrush repelling agent as an environmentally safe alternative for use with commercial resins, in turn realizing a fully water-based hydrophobic coating. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 48003.     

Cu-Mg/Al_2O_3催化乙醇和乙二胺合成N-乙基乙二胺

在固定床反应器内,乙醇和乙二胺经分子间催化胺化反应合成了N-乙基乙二胺(NEED),考察了一系列铜系催化剂的活性,并筛选出催化性能较好的Cu-Mg/A l2O3催化剂;通过X射线衍射和透射扫描电子显微镜方法表征了助剂Mg对Cu/A l2O3催化剂的改性作用;考察了助催化剂Mg含量、反应温度、反应压力、进料量和乙二胺含量等对Cu-Mg/A l2O3催化剂性能的影响。实验结果表明,Cu-Mg/A l2O3催化剂具有很好的活性和选择性;在200℃、3.0MPa、质量分数20%的乙二胺乙醇溶液、进料量1.0mL/m in的条件下,乙二胺的转化率为71.56%,产物NEED的选择性和收率分别为92.62%和69.86%;经过20 d的连续使用表明,Cu-Mg/A l2O3催化剂具有良好的稳定性。     

Processing of Yttria-Alumina Coated Silicon Nitride Slips by Slip Casting

Si₃N₄powders coated with 6 wt% Y₂O₃and 4 wt% Al₂O₃were prepared by coprecipitation. The resulting powders were dispersed in water at different pH values and with addition of various amounts of ammonium polyacrylate (NH₄PA) to produce 32 vol% slips. The influence of the amount of NH₄PA solution added and pH on the rheological properties of 32 vol% coated Si₃N₄slips were studied. In addition, the sintered density of cast samples was determined and related to the degree of slip dispersion. The adsorption of the NH₄PA on the coated particle surface was rather high and the surface became saturated near 0.86 mg/m²at pH 9.2. High NH₄PA concentrations (1.7–3 wt%) were necessary to obtain well dispersed 32 vol% coated Si₃N₄slips at pH 9.2. The best stabilization was obtained with the addition of 2.3 wt% NH₄PA; in this condition, the viscosity reached a minimum value of 35 mPa.s at 100 s^–1. The slip viscosity increased with increasing pH from 9.2 to 10.2. Slips with low viscosities gave a more dense packing of cast samples and consequently higher sintered density values.     

NaY晶化母液制备硅铝胶的技术探讨

在导向剂法合成Y型分子筛的工艺下，晶化母液中SiO₂的含量为50～55g/l,Na₂O含量为20～25g/l，相当于模数为1.65～2.58的稀水玻璃，将晶化母液分离处理后，在晶化母液中加入一定量的硫酸铝溶液使硅沉淀,经过滤和水洗后即可制备出合格的硅铝胶，以便进行重新利用。     

纳米级BaAl_2O_4微粉的制备和性质

分别用溶胶 -凝胶法、低温固相反应法 ,制得了纳米级BaAl2 O4微粉 ,用电镜观察了其形貌和粒径的大小 ,用X-射线衍射仪进行了物相分析 ,测定了其纯度与晶型 ,讨论了制备方法与粒度大小的相互影响