Catalytic behavior in CH4 decomposition of catalysts derived from red mud: Impact of residual Na2O

Catalyst samples for CH₄ decomposition were prepared from red mud (RM) by an acid-leaching neutralization precipitation approach. Water-washing the resultant precipitates multiple times, followed by drying at 105 °C and calcination at 500 °C, resulted in a threshold of residual Na₂O, equivalent to 96% Na₂O removal. Drying the precipitate at a higher temperature of 200 °C, followed by repeated water washing, provided a deeper Na₂O removal of 99% and made the resultant samples more active for the targeted reaction. Subsequently, four catalyst samples with a simulated red mud composition and NaOH contents from 0 to 0.3 wt% were prepared and the catalytic test results revealed that the Na₂O remaining in the RM-derived catalysts did not only inhibit their activation in CH₄ but also lower their maximal activities for CH₄ decomposition. Finally, two catalysts with the same simulated red mud composition and their Na impregnated respectively on Fe₂O₃ and a mixture support of Al₂O₃-SiO₂-TiO₂ were prepared and tested to explore the effect of Na distribution on the activation behavior of RM-derived catalysts for CH₄ decomposition. The activity testing results showed that it was the Na residual dispersed on iron oxides in the RM-derived samples to significantly inhibit the activation of CH₄ decomposition.     

Interfacial microstructure and mechanical properties of Ti3SiC2 ceramic and TC11 alloy joint diffusion bonded with a Cu interlayer

Reliable joints of Ti₃SiC₂ ceramic and TC11 alloy were diffusion bonded with a 50 μm thick Cu interlayer. The typical interfacial structure of the diffusion boned joint, which was dependent on the interdiffusion and chemical reactions between Al, Si and Ti atoms from the base materials and Cu interlayer, was TC11/α-Ti + β-Ti + Ti₂Cu + TiCu/Ti₅Si₄ + TiSiCu/Cu(s, s)/Ti₃SiC₂. The influence of bonding temperature and time on the interfacial structure and mechanical properties of Ti₃SiC₂/Cu/TC11 joint was analyzed. With the increase of bonding temperature and time, the joint shear strength was gradually increased due to enhanced atomic diffusion. However, the thickness of Ti₅Si₄ and TiSiCu layers with high microhardness increased for a long holding time, resulting in the reduction of bonding strength. The maximum shear strength of 251 ± 6 MPa was obtained for the joint diffusion bonded at 850 °C for 60 min, and fracture primarily occurred at the diffusion layer adjacent to the Ti₃SiC₂ substrate. This work provided an economical and convenient solution for broadening the engineering application of Ti₃SiC₂ ceramic.     

Effect of nickel concentration on biohydrogen production: Organic solid waste vs. glucose

In recent years, alternative renewable energy generation sources have been investigated, highlighting the dark fermentation process due to it’s potential to obtain hydrogen-rich gas, which can be used as an energy source. Different trace metals intervene in this biological process. Nickel is one of the most important because it is a component of the [Ni–Fe] hydrogenase enzyme that catalyzes the oxidation of H₂ in numerous bacteria. The aim of this study was to evaluate the effect of nickel on biohydrogen production from organic solid waste (OSW). The experimental setup was carried out in batch tests using OSW as the substrate, glucose as a reference compound and the valuation of Ni²⁺ doses on the operation in a Sequencing Batch Reactor. The results of the batch tests showed that when using glucose as a substrate, 2 mg Ni²⁺/g VS_inoculum generated the highest hydrogen production (774 ± 7.3 mL H₂/L/d) and highest yield (55.8 ± 3.4 mL H₂/g of glucose), which was 34.4% higher than the control. Testing of different concentrations of nickel using OSW as a carbon source showed that the highest production was obtained without Ni²⁺ addition since the nickel concentration in the residue was 0.17 ± 0.06 mgNi/gVS; consequently, hydrogen production was not affected by the lack of Ni. The addition of 0.5 mg Ni²⁺/g VS_inoculum decreased acetate and butyrate production and increased caproate production.     

减水剂类型对赤泥—矿渣基地聚物注浆材料性能的影响及机理研究

针对赤泥等固体废弃物对环境危害性大且利用率低等问题,以碱激发赤泥-矿渣基地聚物注浆材料为 研究对象,研究了不同掺量的聚羧酸(PA)减水剂、醛酮缩合物(AKC)减水剂和萘系(N)减水剂对材料凝结时间、流动 性及强度等的影响,并通过 XRD、傅里叶红外光谱及 SEM 等设备对减水剂的作用机理进行研究。 结果表明:减水剂增 强了材料的流动性但降低了材料的剪切应力;N 和 PA 减水剂能缩短材料的凝结时间,但 AKC 减水剂会延长材料的凝 结时间;N 和 AKC 减水剂能提高材料的强度,但 PA 减水剂会降低材料的强度;N 减水剂对材料的综合性能提升效果 更加明显,其最优掺量为 0. 7%;减水剂对赤泥-矿渣基地聚物性能提升的作用机理主要是促进地聚合物凝胶的形成。 研究成果为拓展赤泥在工程上的使用途径和效率提供了理论指导。     

Cladophora sp. as a sustainable feedstock for dark fermentative biohydrogen production

Macroalgae are rich in carbohydrates which can be used as a promising substrate for fermentative biohydrogen production. In this study, Cladophora sp. biomass was fermented for biohydrogen production at various inoculum/substrate (I/S) ratios against a control of inoculum without substrate in laboratory-scale batch reactors. The biohydrogen production yield ranged from 40.8 to 54.7 ml H₂/g-VS, with the I/S ratio ranging from 0.0625 to 4. The results indicated that low I/S ratios caused the overloaded accumulation of metabolic products and a significant pH decrease, which negatively affected hydrogen production bacteria's metabolic activity, thus leading to the decrease of hydrogen fermentation efficiency. The overall results demonstrated that Cladophora sp. biomass is an efficient fermentation feedstock for biohydrogen production.     

Behavior of 316L stainless steel containing corrosion pits under cyclic loading

The environmental performance of 316L grade stainless steel, in the form of tensile specimens containing a single corrosion pit with various aspect ratios, under cyclic loading in aerated chloride solutions is investigated in this study. Results from environmental tests were compared and contrasted with those obtained using finite element analysis (FEA). Fractography of the failed specimens obtained from experiments revealed that fatigue crack initiation took place at the base of the shallow pit. The crack initiation shifted towards the shoulder and the mouth of the pit for pits of increasing depth. This process is well predicted by FEA, as the strain contour maps show that strain is the highest around the centric strip of the pit. However, for shallow pits, local strain is uniformly distributed around that strip but begins to concentrate more towards the shoulder and the mouth region for increasingly deep pits.     

Interlayer Engineering of Molybdenum Trioxide toward High‐Capacity and Stable Sodium Ion Half/Full Batteries

Orthorhombic molybdenum trioxide (MoO₃) is one of the most promising anode materials for sodium‐ion batteries because of its rich chemistry associated with multiple valence states and intriguing layered structure. However, MoO₃ still suffers from the low rate capability and poor cycle induced by pulverization during de/sodiation. An ingenious two‐step synthesis strategy to fine tune the layer structure of MoO₃ targeting stable and fast sodium ionic diffusion channels is reported here. By integrating partially reduction and organic molecule intercalation methodologies, the interlayer spacing of MoO₃ is remarkably enlarged to 10.40 Å and the layer structural integration are reinforced by dimercapto groups of bismuththiol molecules. Comprehensive characterizations and density functional theory calculations prove that the intercalated bismuththiol (DMcT) molecules substantially enhanced electronic conductivity and effectively shield the electrostatic interaction between Na⁺ and the MoO₃ host by conjugated double bond, resulting in improved Na⁺ insertion/extraction kinetics. Benefiting from these features, the newly devised layered MoO₃ electrode achieves excellent long‐term cycling stability and outstanding rate performance. These achievements are of vital significance for the preparation of sodium‐ion battery anode materials with high‐rate capability and long cycling life using intercalation chemistry.     

Burkholderia thailandensis E264/pBMTL3-tdpR发酵生产抗癌药物ThailandepsinA的研究

在伯克氏菌Bth264野生株产新型抗癌药物Thailandepsin A以及调节基因tdp R正向调控Thailandepsin A生物合成的基础上,利用基因工程菌Bth264/p BMTL3-tdp R发酵生产Thailandepsin A,以提高产量。以0.5%乳糖为诱导剂,确定最佳诱导条件:发酵15 h添加乳糖,诱导时间6 h;通过单因素实验,确定葡萄糖和胰蛋白胨作为碳氮源、装液量65/250 m L以及接种量1%;同时结合优化发酵培养基进行发酵,Thailandepsin A产量达到252.14 mg·L-1,比优化前的产量提高56%;另外在发酵过程中,添加大孔树脂HP-20原位吸附产物,Thailandepsin A产量可达283.75 mg·L-1,比不加树脂提高13.8%;最后,基于RT-PCR和比较Ct值法,基因工程菌和野生菌相比,Thailandepsin A生物合成基因tdp B、tdp C1的转录水平分别提高11.4倍和6.0倍,对应的产量增加4.6倍,从而在很大程度上说明调节基因tdp R的过表达促进生物合成基因转录水平的提高以及产量的增加。