Behavior of 316L stainless steel containing corrosion pits under cyclic loading

The environmental performance of 316L grade stainless steel, in the form of tensile specimens containing a single corrosion pit with various aspect ratios, under cyclic loading in aerated chloride solutions is investigated in this study. Results from environmental tests were compared and contrasted with those obtained using finite element analysis (FEA). Fractography of the failed specimens obtained from experiments revealed that fatigue crack initiation took place at the base of the shallow pit. The crack initiation shifted towards the shoulder and the mouth of the pit for pits of increasing depth. This process is well predicted by FEA, as the strain contour maps show that strain is the highest around the centric strip of the pit. However, for shallow pits, local strain is uniformly distributed around that strip but begins to concentrate more towards the shoulder and the mouth region for increasingly deep pits.     

Formation and wear mechanism of nickel titanium intermetallics during heat treatment of nickel coating on Ti-6Al-4V substrate

In the present work, inter-diffusion of nickel and titanium and formation of Ni-Ti intermetallic compounds on Ti-6Al-4V substrate have been studied. Initially, nickel was electrodeposited on the alloy using a modified Watts bath solution at a current density of 2 A dm^?2 for 1?h. The coated specimens were then heat treated for different durations at 750, 800 and 850 °C under argon atmosphere. The effects of temperature and time on the characteristics, hardness and wear resistance of intermetallic phases were investigated. The results showed that a multilayer structure was formed after heat treatment, an outer layer of residual nickel, an area of intermetallic layers with different compositions followed by a solid solution of Ni-Ti. It was also observed that an increase in time or temperature at first led to the formation of thicker intermetallic layers; however, after passing a critical point, the intermetallic layers seem to dissolve into the substrate. Furthermore, the wear rates of the diffusion treated samples were four times lower compared to Ti-6Al-4V alloy when sliding against AISI 52100 hardened steel.     

Effect of microstructure on the fatigue crack growth behaviour of a near-α Ti alloy

Fatigue crack growth behaviour of Ti–6Al–2Zr–1.5Mo–1.5V (VT-20 a near-α Ti alloy) was studied in lamellar, bimodal and acicular microstructural conditions. Fatigue crack growth tests at both increasing and decreasing stress intensity factor range values were performed at ambient temperature and a loading ratio of 0.3 using compact tension samples. Lamellar and acicular microstructures showed lower fatigue crack growth rates as compared to the bimodal microstructure due to the tortuous nature of cracks in the former and the cleavage of primary α in the latter. The threshold stress intensity factor range was highest for acicular microstructure.     

基于压电陶瓷动态信息的结构裂纹识别方法

利用压电陶瓷的动态特性和压电系统的动态信息,对铝梁的裂纹损伤进行了分析研究。随着梁裂纹尺寸的增加,压电陶瓷片的导钠幅值下降,且系统固有频率减小。利用导钠幅值的变化和系统的动态信息,可以对裂纹的位置和尺寸大小进行识别。实验证明该方法的有效性。     

低密度微泡沫压井液的研究与应用

吐哈油田部分区块地层压力系数小于0.9,常规水基压井液对储层伤害大,若使用油基压井液成本高,环境污染严重。通过实验优选出了一种低密度水基微泡沫压井液。该压井液具有密度低、泡沫强度高、稳定性好、携砂能力强等优点。现场应用表明,低密度微泡沫压井液稳定时间大于48 h,密度在0.70~0.99 g/cm3之间可调,抗油污染能力强,抗油大于8%,抗温在100℃以上,岩心污染后渗透率恢复值大于80%;并且施工方便,成本低,具有储层保护能力,使用微泡沫压井液的井表皮系数在0.20~2.34之间。     

激光熔覆专用铁基合金粉末的研究进展

指出了目前防止熔覆层开裂所采取的主要措施中存在的问题,阐述了激光熔覆和热喷涂对于所用合金粉末性能要求之异同,评述了激光熔覆专用铁基合金粉末的研制现状,提出了成分与组织设计的新思想。     

MIM隧道发光结的负阻现象

本文介绍了薄膜隧道发光结的基本结构、发光机理，阐述了其Ｉ－Ｖ特性中的负阻现象。简单介绍了ＭＩＭ结构负阻的几种解释，根据热像仪照片和低温测试结果分析，再结合Ｄｅａｒｍａｌｅｙ导电模型，我们提出了ＭＩＭ负阻的物理模型，理论与实验符合较好，最后分析了负阻现象的应用前景。     

回热损失对磁斯特林制冷循环制冷率的影响

从铁磁质的磁化强度一般表示式出发，探讨热阻和回热损失对磁斯特林制冷循环性能的影响，导出最大制冷率及其它性能参数。得到了结果适用于以顺磁质为工质的磁斯特林制冷循环。并指出在理想回热条件下的结论也适用于磁卡诺制冷循环。