锅炉对流管爆裂原因分析

采用化学分析、金相检验及力学性能测定等方法，对锅炉对流管爆裂原因进行了分析。结果表明，长期超温运行而引起的蠕变是导致爆裂的主要原因。     

某热电厂2^#锅炉水冷壁管爆裂分析

通过宏观检验，力学性能，金相组织及断口分析，得出水冷壁管爆裂的主要原因是短期过热造成的，据此，提出了修复锅炉的措施。     

TRT入口方管道爆裂原因剖析

介绍了鞍钢7#高炉TRT装置入口方管道爆裂事故经过,进行了原因分析,并提出了解决措施。     

基于不同爆轰产物的格尼速度估算新方法（英）

A new method for prediction of Gurney velocity of explosives is introduced in which energy output is correlated with the heat of detonation, the number of moles of gaseous products of detonation per gram of explosive and the average molecular weight of gaseous products. It is assumed that the CHNO explosive reacts to form products composed of N2 , CO, H2O, CO2, H2,O2 and C（s） as determined by the oxygen balance of the unreacted compound. Good agreement is obtained between measured and calculated values of Gurney velocity as compared to previous correlations which assumed the reaction products to consist of N2 , H2O, CO2 and either C（s） or O2.     

高技术浇注料抗爆裂的研究

论述了三种添加剂A、B、C对高技术浇注料抗爆裂性能的影响。结果表明,三种添加剂均有抑制无水泥浇注料爆裂的作用,其原因是形成了贯通气孔并使试样的透气度增加。     

制氢装置弯头爆裂原因及措施

分析了制氢装置中变气蒸汽发生器出口弯头在不到 半年时间内出现两次冲刷减薄爆裂的原因，并提出采取更换材质、扩大管径、控制工艺指标及优化原料等预防措施.     

高铝质超低水泥浇注料在不同加热速率下的干燥行为

对高铝质超低水泥耐火浇注料在脱水过程中的热重变化进行了研究。对在8℃养护的含有2％铝酸钙水泥的试样以0.5～25℃·min~(-1)的速率加热进行测试。结果表明,均匀加热的浇注料中水分的减少发生于随加热速率的增大强度逐渐发生变化的阶段。干燥速率在10℃·min~(-1)以上时,干燥时间没有明显的减少,而当加热速率大于20℃·min~(-1)时,坯体出现爆裂。     

高掺量磷渣烧结砖及其生产方法

公开号：1378991 申请人：贵州省建筑材料科学研究设计院     

考虑爆裂影响的轴向约束高强混凝土柱耐火性能研究

应用有限元软件ABAQUS,基于一次爆裂模式,建立了轴向约束高强混凝土（HSC）柱的抗火分析模型.采用试验数据验证了模型的合理性.采用验证后的模型,分析了不同轴向约束刚度比下高强混凝土柱轴力及位移变化的规律,重点考虑了爆裂深度、爆裂长度、爆裂开始时间等爆裂参数对高强混凝土柱轴向位移、截面温度场和耐火极限的影响规律.研究表明：相同爆裂时间前提下,HSC柱轴向位移随爆裂深度、爆裂长度的增大而增大,耐火极限随之减小.爆裂深度、爆裂长度相同前提下,爆裂开始时间对HSC柱的耐火性能影响很小.当荷载比不变时,轴向约束刚度比对HSC柱膨胀阶段的最大轴向位移影响甚小,但是在越过初始平衡位置的收缩阶段对轴向位移影响很大.轴向约束刚度比对轴向约束HSC柱的耐火极限影响不大.