The structure,vacancy characteristics,and magnetic properties of GdMn1-xCrxO3 ceramics

To investigate the evolution of the structural and enhanced magnetic properties of GdMnO₃ systems induced by the substitution of Mn with Cr, polycrystalline GdMn_1-xCr_xO₃ samples were synthesized via solid-state reactions. XRD characterization shows that all GdMn_1-xCr_xO₃ compounds with single-phase structures crystallize well and that Cr³⁺ ions entering the lattice sites of GdMnO₃ induce structural distortion. SEM results indicate that the grain size of the synthesized samples (a few microns) decreases as the Cr substitution concentration increases. Positron annihilation lifetime spectroscopy reveals that vacancy-type defects occur in GdMn_1-xCr_xO₃ ceramics and that the vacancy size and concentration clearly change with the Cr content. The temperature and field dependence of the magnetization curves show that Cr substitution significantly influences the magnetic ordering of the gadolinium sublattice, improving the weak ferromagnetic transition temperature and magnetization of GdMn_1-xCr_xO₃. The enhanced magnetization of GdMn_1-xCr_xO₃ is closely related to the vacancy defect concentration.     

Facile synthesis of Ti3C2 MXene-modified Bi2.15WO6 nanosheets with enhanced reactivity for photocatalytic reduction of Cr(VI)

Through a facile hydrothermal method, we have successfully prepared Ti₃C₂/Bi_2.15WO₆ (TC/BWO) composite, and systematically investigated their reactivity for the photocatalytic reduction of Cr(VI) under visible light. X-ray diffraction and Raman analysis confirm the formation of heterostructure between Bi_2.15WO₆ and Ti₃C₂. The resultant 7TC/BWO composite exhibits enhanced photoactivity toward Cr(VI) reduction. After 120 min irradiation, the conversion of Cr(VI) reaches 92.5% with the quasi-first-order kinetic constant of k = 0.0145 min^?1, which is higher than that of pure BWO (30% and k = 0.0005 min^?1). The electrochemical and photoluminescent characterization confirm that the introduction of Ti₃C₂ is conducive to the separation of carriers, thus significantly improves the photocatalytic performance of TC/BWO. Furthermore, the radical capture experiments verify that the electrons are important for enhancing reduction of Cr(VI) to Cr(III). As a result, this research provides a comprehensive understanding of the reduction of Cr(VI) by TC/BWO composite under visible light.     

珠光体球化的分形研究

珠光体球化反映到金相上，是一种不规则图像的变化，并且具有分形的特征，可望用分形几何的方法来进行描述。以Cr-Mo钢的珠光体球化为例，用分形维数来描述珠光体球化程度；用小岛法对15CrMo钢的珠光体球化图谱进行了测量。实验表明，珠光体球化从1级到6级，其相应的分形维数范围为1.3156-1.9282。从电厂运行了10^5h的15CrMo钢管上取样，实测了该试样的珠光体球化等级，结果表明，以分形维数表示的球化程度与按图谱评定的球化等级完全吻合。     

LD钢超塑性压缩变形参数与金相组织

通过对ＬＤ（７Ｃｒ７Ｍｏ３Ｖ２Ｓｉ）模具钢起塑性压缩变形后的金相组织观察研究，分析了变形参数、原始组织对变形后金相组织的影响。     

A simple mathematical analysis on the effect of sand in Cr(VI) reduction using zero valent iron

A simple mathematical model was proposed to analyze the enhancement of Cr(VI) reduction when sand materials are added to the zero valent iron (ZVI). Natural decay of Cr(VI) in a control experiment was analyzed by using a zero-order decay reaction. Adsorption kinetics of Cr(VI) to sand was modeled as a first-order reversible process, and the reduction rate by ZVI was treated as a first-order reaction. Natural decay of Cr(VI) was also included in other experiments, i.e., the adsorption to sand, the reduction by ZVI, and both adsorption and reduction when sand and ZVI are present together. The model parameters were estimated by fitting the solution of each model to the corresponding experimental data. To observe the effect of sand addition to ZVI, both adsorption and reduction rate models were considered simultaneously including the natural decay. The solution of the combined model was fitted to the experimental data to determine the first-order adsorption and reduction rate constants when sand as well as ZVI is present. The first-order reduction rate constant in the presence of sand was about 35 times higher than that with ZVI only.     

25Cr3Mo3NiNb二次硬化钢中的碳化物

利用TEM和萃取相分析方法，研究了25Cr3Mo3NiNb二次硬化钢淬火回火组织中的碳化物。结果表明，随淬火奥氏体化温度的升高，M6C型碳化物逐渐溶解。于1050℃奥氏体化时M6C型碳化物全部溶解，淬火态试样中只有少量的Nb(C，N)颗粒和自回火M3C型碳化物。随回火温度的升高，先后析出ε、M3C、M2C和M7C3等类型的碳化物。Nb(C，N)颗粒可以阻止淬火奥氏体晶粒的异常长大，而高温回火析出的M2C碳化物有二次硬化作用，从而提高回火稳定性和高温强韧性。     

高速钢W6Mo5Cr4V2的脱磷试验

在３０ｋｇ感应炉上用ＣａＯ－Ｎａ２ＣＯ３－ＣａＦ２－ＦｅｘＯ（ＭｏＯ３）渣、ＭｏＣｌ６粉剂和Ａｌ－Ｃａ合金作脱磷剂对高速钢Ｗ６Ｍｏ５Ｃｒ４Ｖ２进行脱磷试验。结果表明，ＣａＯ－Ｎａ２ＣＯ３－ＣａＦ２－ＦｅｘＯ渣的脱磷效果最好，一般脱磷率可达２６％￣５６％。     

Probing the early stages of polymerization of ethylene on a model chromium/silica catalyst by Fourier transform infrared spectroscopy

The nature of the interaction of monomer, and the early stages of growth of oligomers of ethylene on a rather more uniform surface of Cr/SiO₂ catalyst than hitherto studied has been investigated by differenceFTIR spectroscopy using C₂D₄ and C₂H₄ as reactants both with and without subsequent treatment of the catalyst with CO andTHF. The active catalyst was prepared by reaction of vapour phase CrO₂Cl₂ with the vicinal hydroxyls of the silica surface. Three distinct kinds of methylene groups were detected. Arguments are given for assigning the peaks at 2935 and 2860 cm^–1 to CH₂ groups directly bound to the active site and those at 2920 and 2850 to CH₂s in the growing chain well removed from the Cr. The peaks at 2160 and 2165 cm^–1 are attributed to CD₂ groups hydrogen bonded to surface hydroxyls.     

常减压蒸馏装置阻垢剂进料管腐蚀与防护

通过对常减压蒸馏装置阻垢剂进料管的材质、性能、工作条件及腐蚀形貌、腐蚀产物的全面分析,找出了使进料管发生大面积腐蚀的腐蚀介质为环烷酸.并提出了减缓阻垢剂进料管环烷酸腐蚀的措施,主要包括选用更耐蚀的316或316 L材质以及改进三通结构等.