聚苯硫醚复合涂层的耐磨性能

研究了用固体润滑石墨、碳化硅、二硫化钼等填料改性的聚苯硫醚 (PPS)涂层的耐磨性能。实验结果表明 ,聚苯硫醚复合涂层具有优良的耐磨性 ;加入适量 ( 3 0 % )的石墨、碳化硅等固体润滑剂 (石墨 :碳化硅 =2∶3 ) ,可以有效提高涂层的耐磨性能 ,而二硫化钼和三氧化二铬的减摩效果更佳     

火焰图像特征在火灾数字图像识别中的运用

火焰尖角数目和圆形度是早期火灾火焰的主要特征,本文主要论述了如何在数学形态学基础上,利用火灾火焰的两个特点判断和识别早期火情。实验中,对火焰的二值图像进行开运算,即先腐蚀,再膨胀,目的是为了对火焰图像进行形态学滤波,去噪。从实验结果可以看出,该算法可以很好的识别火焰和干扰源。     

Peculiarities of erosion-corrosion processes

Investigations have been carried out on an erosion-corrosion apparatus to investigate the behaviour of corrosion-resistant highalloy iron-base materials containing hard phases. These materials had been optimized for increased wear resistance under complex stress conditions. As expected, in dry erosion tests, very low mass losses were established; there was little difference between the materials. Also, in corrosive environments (NaCl, H₂SO₄), the materials showed good stability; however, the duplex structures were superior to the martensitic ones. The combination of erosion and corrosion produced large differences and, in some cases, markedly reduced resistance to damage. These results confirmed observations that it is impossible to deduce the environmentally influenced mechanical behaviour of an alloy from its behaviour in separate corrosion and erosion experiments. The basic mechanisms underlying these processes have been investigated only tentatively.     

钒钛渣对刚玉莫来石耐火材料的侵蚀研究

通过不同温度下钒钛渣对刚玉莫来石耐火材料的侵蚀实验，分析了炉渣、温度对材料的影响，认为致密结构、低气孔率是提高炉衬寿命的关键，板条状莫来石的存在利于减缓渣的侵蚀过程。     

Stages of surface erosion under ion irradiation

Initial stages of surface erosion have been studied for NaCl and LiF single crystals bombarded by Ar⁺ ions with 20 keV. For irradiation with doses D=10¹⁰-10¹¹ ions/cm², exoelectron emission has been used, whereas for higher doses, we have used electron microscopy. Two stages of initial surface erosion have been identified; for small doses, there is slow development of atomic-scale roughening, which reaches its peak when areas damaged by closest incident ions start to overlap, and then, beginning with D=10¹⁶ ions/cm², there is rapid etching, deep into the crystal, followed by the emergence of secondary microscopic structure, i.e. caverns, concentric closed steps and terraces. Ion-induced surface structure of alkali halide crystals has been shown to depend strongly on the presence of foreign particles on the surface, as well as on segregation. Topography of thin carbon films and some metals have been discussed.     

腐蚀算法在重建一类特殊管道中的应用

针对一类特殊而不能直接对其观察的管道（如动物的血管），为了准确了解其内部特征和形态，借助计算机给出了一种用腐蚀算法来重建管道原形的方法。这种方法简单易行，而且精确度高。     

浅谈计算机在建筑物修复改造鉴定中的应用

计算机应用技术伴随着行业工程技术的发展同步开发。它已广泛应用于建筑工程中。从三个方面分析了计算机在建筑工程中的应用问题：1）在建筑物可靠鉴定领域、工程设计、管理中的应用；2）不足：包括计算机软件的开发受限制，已开发软件的局限性，已有档案资料复用技术水平低，缺乏资料共享、信息库支援；3）发展方向：建立强大信息库，开发全面应用系统，日常使用管理系统，典型问题治理专家系统。并提出未来发展重点－信息库（共享）机制。     

硫氰酸钠湿纺腈纶设备的孔蚀与防护

本文重点讨论了硫氰酸钠湿纺腈纶设备因钝化膜缺陷和Cl-侵入而产生孔蚀的机理及环境因素对孔蚀的影响,并针对产生孔蚀的主要原因提出了防护措施。