Catalyst samples for CH₄ decomposition were prepared from red mud (RM) by an acid-leaching neutralization precipitation approach. Water-washing the resultant precipitates multiple times, followed by drying at 105 °C and calcination at 500 °C, resulted in a threshold of residual Na₂O, equivalent to 96% Na₂O removal. Drying the precipitate at a higher temperature of 200 °C, followed by repeated water washing, provided a deeper Na₂O removal of 99% and made the resultant samples more active for the targeted reaction. Subsequently, four catalyst samples with a simulated red mud composition and NaOH contents from 0 to 0.3 wt% were prepared and the catalytic test results revealed that the Na₂O remaining in the RM-derived catalysts did not only inhibit their activation in CH₄ but also lower their maximal activities for CH₄ decomposition. Finally, two catalysts with the same simulated red mud composition and their Na impregnated respectively on Fe₂O₃ and a mixture support of Al₂O₃-SiO₂-TiO₂ were prepared and tested to explore the effect of Na distribution on the activation behavior of RM-derived catalysts for CH₄ decomposition. The activity testing results showed that it was the Na residual dispersed on iron oxides in the RM-derived samples to significantly inhibit the activation of CH₄ decomposition.     

Dense and core-rim structured B4C-TiB2 ceramics with Mo-Co-WC additive

B₄C-TiB₂ ceramics (TiB₂ ranging 5~70 vol%) with Mo-Co-WC as the sintering additive were prepared by spark plasma sintering. In comparison with B₄C-TiB₂ without additive, the enhanced densification was evident in the sintered specimen with Mo-Co-WC additive. Core-rim structured grain was observed around TiB₂ grains. The interface of the rim between TiB₂ and B₄C phases demonstrated different feature: the inner borderline of the rim exhibited a smooth feature, whereas a sharp curved grain boundary was observed between the rim and the B₄C grain. The formation mechanism is discussed: the epitaxial growth of (Ti,Mo,W)B₂ rim around the TiB₂ core may occur as a result of the solid solution and dissolution-precipitation between TiB₂ phase and the sintering additive. It was revealed that the fracture toughness increased as the content of TiB₂ content increased, alongside the decreased hardness. B₄C-30 vol% TiB₂ specimen demonstrated the optimal combination of mechanical properties, reaching Vickers hardness of 24.3 GPa and fracture toughness of 3.33 MPa·m^1/2.     

Microbial susceptibility of various polymers and evaluation of thermoplastic elastomers with antimicrobial additives

The incursion of microbial growth on polymeric products can deteriorate their performance and lead to the development of undesirable staining and odors. A growing trend in the industry has aimed to reduce microbial populations on high-touch surfaces via the use of antimicrobials to protect material aesthetics and durability or to prevent the spread of pathogenic microorganisms. In this study, a variety of plastic substrates (30 unique polymer compounds), including poly(acrylonitrile-co-butadiene-co-styrene), poly(butylene terephthalate), poly(etherimide), various thermoplastic elastomers (TPEs), poly(carbonates), and poly(amides), were screened for susceptibility to microbial attack using American Society for Testing and Materials (ASTM) G21 (fungi susceptibility), Japanese Industrial Standard (JIS) Z2801, and modified ASTM E1428-15a (bacterial susceptibility) test standards. TPEs were determined to be most susceptible to microbial attack under the appropriate environmental conditions. Subsequent studies assessed the use of an antimicrobial additive, zinc pyrithione (ZPT), for potential efficacy in a variety of TPE blends for diverse target market applications. ZPT proved to be very effective in protecting TPEs, reducing Staphylococcus aureus and Escherichia coli populations by 99.9% or more in JIS Z2801 testing and inhibiting fungal growth (rating = 0) according to the ASTM G21 standard.     

Microstructure and mechanical properties of α/β-Si3N4 composite ceramics with novel ternary additives prepared via spark plasma sintering

In this study, α/β-Si₃N₄ composite ceramics with high hardness and toughness were fabricated by adopting two different novel ternary additives, ZrN–AlN–Al₂O₃/Y₂O₃, and spark plasma sintering at 1550 °C under 40 MPa. The phase composition, microstructure, grain distribution, crack propagation process and mechanical properties of sintered bulk were investigated. Results demonstrated that the sintered α/β-Si₃N₄ composite ceramics with ZrN–AlN–Al₂O₃ contained the most α phase, which resulted in a maximum Vickers hardness of 18.41 ± 0.31 GPa. In the α/β-Si₃N₄ composite ceramics with ZrN–AlN–Y₂O₃ additives, Zr₃AlN MAX-phase and ZrO phase were found and their formation mechanisms were explained. The fracture appearance presented coarser elongated β-Si₃N₄ grains and denser microstructure when 20 wt% TiC particles were mixed into Si₃N₄ matrix, meanwhile, exhibited maximum mean grain diameter of 0.98 ± 0.24 μm. As a result, the compact α/β-Si₃N₄ composite ceramics containing ZrN–AlN–Y₂O₃ additives and TiC particles displayed the optimal bending strength and fracture toughness of 822.63 ± 28.75 MPa and 8.53 ± 0.21 MPa?m^1/2, respectively. Moreover, the synergistic toughening of rod-like β-Si₃N₄ grains and TiC reinforced particles revealed the beneficial effect on the enhanced fracture toughness of Si₃N₄ ceramic matrix.     

减水剂类型对赤泥—矿渣基地聚物注浆材料性能的影响及机理研究

针对赤泥等固体废弃物对环境危害性大且利用率低等问题,以碱激发赤泥-矿渣基地聚物注浆材料为 研究对象,研究了不同掺量的聚羧酸(PA)减水剂、醛酮缩合物(AKC)减水剂和萘系(N)减水剂对材料凝结时间、流动 性及强度等的影响,并通过 XRD、傅里叶红外光谱及 SEM 等设备对减水剂的作用机理进行研究。 结果表明:减水剂增 强了材料的流动性但降低了材料的剪切应力;N 和 PA 减水剂能缩短材料的凝结时间,但 AKC 减水剂会延长材料的凝 结时间;N 和 AKC 减水剂能提高材料的强度,但 PA 减水剂会降低材料的强度;N 减水剂对材料的综合性能提升效果 更加明显,其最优掺量为 0. 7%;减水剂对赤泥-矿渣基地聚物性能提升的作用机理主要是促进地聚合物凝胶的形成。 研究成果为拓展赤泥在工程上的使用途径和效率提供了理论指导。     

V2O5/RGO/Pt nanocomposite on oxytetracycline degradation and pharmaceutical effluent detoxification

The cover image is based on the Research Article V₂O₅/RGO/Pt nanocomposite on oxytetracycline degradation and pharmaceutical effluent detoxification by Mohan, H et al., DOI: 10.1002/jctb.6238 .

     

Low-temperature hot-press sintering of AlN ceramics with MgO–CaO–Al2O3–SiO2 glass additives for ceramic heater applications

Aluminum nitride (AlN) is used a ceramic heater material for the semiconductor industry. Because extremely high temperatures are required to achieve dense AlN components, sintering aids such as Y₂O₃ are typically added to reduce the sintering temperature and time. To further reduce the sintering temperature, in this study, a low-melting-temperature glass (MgO–CaO–Al₂O₃–SiO₂; MCAS) was used as a sintering additive for AlN. With MCAS addition, fully dense AlN was obtained by hot-press sintering at 1500 °C for 3 h at 30 MPa. The mechanical properties, thermal conductivity, and volume resistance of the sintered AlN–MCAS sample were evaluated and compared with those of a reference sample (AlN prepared with 5 wt% Y2O3 sintering aid sintered at 1750 °C for 8 h at 10 MPa). The thermal conductivity of AlN prepared with 0.5 wt% MCAS was 91.2 W/m?K, which was 84.8 W/m?K lower than that of the reference sample at 25 °C; however, the difference in thermal conductivity between the samples was only 14.2 W/m?K at the ceramic-heater operating temperature of 500 °C. The flexural strength of AlN–MCAS was 550 MPa, which was higher than that of the reference sample (425 MPa); this was attributed to the smaller grain size achieved by low-temperature sintering. The volume resistance of AlN–MCAS was lower than that of the reference sample in the range of 200–400 °C. However, the resistivity of the proposed AlN–MCAS sample was higher than that of the reference sample (500 °C) owing to grain-boundary scattering of phonons. In summary, the proposed sintering strategy produces AlN materials for heater applications with low production cost, while achieving the properties required by the semiconductor industry.     

一种可替代漂珠的低密度材料

漂珠低密度水泥浆由于密度低、强度高、体系稳定而在油田低压易漏层及低压油气层长封固段固井作业中获得了广泛的应用。但近年来,由于漂珠的产量越来越少,油田低成本要求急需开发代替漂珠的新型减轻材料,以满足配制低密度水泥浆的需求。开发了BCL-10S低密度混合减轻材料,其物化性能与漂珠相当,用它作减轻剂配制的低密度水泥浆性能与用漂珠作减轻剂配制的低密度水泥浆性能相媲美,并已经在长庆油田获得了应用。     

泥页岩井壁稳定研究及在临盘地区的应用

从岩石力学和物理化学两个主要因素简要分析了井壁失稳的机理，指出泥页岩井壁失稳是由力学与化学两方面因素共同作用的结果。钻井液与泥页岩存在化学势差，并改变了井壁附近的孔隙压力，降低岩石强度。借助于井壁处有效应力的变化,将泥页岩与钻井液相互作用时页岩水化所产生的力学效应与纯力学效应结合起来，计算出任意井斜方位井眼围岩应力状态，利用测井资料求出有关岩石力学参数和Mohr Couloumb准则，计算得出防塌的临界钻井液密度。     

储层泥浆侵入深度预测方法研究

泥浆侵入半径的确定尚缺乏严格的验证标准.以油水两相渗流理论和离子扩散方程为基础,结合储集层特点,研究了不同储层参数下泥浆滤液对地层的侵入特性.数值模拟侵入时间选取10 d和20 d.数值模拟结果表明,侵入半径在渗透率不变的情况下随孔隙度的增大而减小,在孔隙度不变的情况下随渗透率的增大而增大;当渗透率和孔隙度都发生变化时,泥浆侵入半径一般随孔隙度的增加呈幂函数增加.依据这种关系对测井资料约束处理,得到的泥浆侵入半径较客观地反映了地层的真实情况.