CuZnAl形状记忆合金热机械循环滞回曲线与振动衰减特性研究

运用电子万能拉伸试验机、动态数据采集分析仪,测试了CuZnAl形状记忆合金的力-变形滞回曲线和安装有CuZnAl形状记忆合金耗能器框架结构的减振性能.借助透射电镜、X射线衍射仪,分析了CuZnAl形状记忆合金热机械循环过程中显微组织的变化.比较了不同热处理方式、不同相变点的CuZnAl形状记忆合金热机械循环后的滞回曲线面积及减振性能.试验结果表明:CuZnAl形状记忆合金用于框架结构的被动振动控制具有较好的减振性能,同时明显降低框架结构的振动频率.马氏体CuZnAl形状记忆合金耗能器具有较大的耗能能力,热机械循环数十次以后滞回面积亦大幅度减小,但相变点高的CuZnAl形状记忆合金的滞回面积减小幅度较小.     

Effect of test frequency and water content on localized crack-tip heating in nylon-6,6

Fatigue crack propagation (FCP) tests were conducted at various frequencies on nylon-6,6 specimens equilibrated over a range of moisture levels to determine the crack growth rates and the crack-tip temperatures as a function of water content. Frequency-sensitivity was correlated with the amount of crack-tip heating taking place, with crack-tip temperature being found to depend strongly on the estimated loss compliance, D″, of the material. The frequency-sensitivity of FCP in nylon was seen also to be affected by mean stress, suggesting that creep processes are often significant in FCP of nylon.     

摩擦滑移水平隔震支座的性能试验

对一种新型的聚四氟乙烯板摩擦滑移水平隔震支座进行了性能试验,支座由聚四氟乙烯摩擦滑移装置隔震,而并联的水平弹簧使其在震后具有复位能力.试验测定了不锈钢板与聚四氟乙烯摩擦片间的摩擦系数及支座在简谐激励与地震激励下的滞回性能,并对竖向输入动压力时支座的滞回特征进行了测试.结果表明,滑移速度、竖向压力及地震激励的类别是影响摩擦系数与滞回性能的主要因素,为支座理论模型的建立提供了基础.     

梁端翼缘扩大型梁柱节点抗震性能和设计方法

为使钢框架梁柱节点满足强柱弱梁的抗震设计原则,并使梁上塑性铰远离梁柱节点区,对梁端翼缘扩大型(包括侧板加强型和翼缘端部放大型)钢框架梁柱节点进行了往复荷载下的试验研究,得到了节点类型和梁端翼缘扩大尺寸对节点滞回性能、延性和耗能能力等指标的影响规律.在使用非线性有限元程序对试验结果进行数值模拟的基础上,研究了梁端翼缘扩大段的长度及宽度等参数对节点性能的影响规律和有效取值范围,给出了实用设计方法.使用梁端翼缘扩大型钢框架节点可以有效实现梁端塑性铰外移,是一种在抗震设计中值得推广的具有良好延性和塑性转动能力的新型节点形式.     

磁流变阻尼器S型滞环模型的改进及辨识

磁流变阻尼器控制系统的性能很大程度取决于阻尼器的数学模型,由于磁流变液在高速剪切速率下容易发生剪切稀化,因此,本文在原有S型滞环模型的基础上,引入了行为指数”从而改进了S型滞环模型。根据试验数据,并运用遗传算法和传统优化算法相结合求取全局最优解的方法,求解出了模型中的参数值。结果表明：改进后的S型滞环模型能够很好拟合高速区的速度-阻尼力试验特性曲线。     

圆钢管空间滞回性能试验

为考察圆钢管空间滞回性能、获得考虑损伤累积的材料本构模型,设计并开展了圆钢管空间滞回试验.试验加载装置可用于空间三向加载.考虑构件长细比及不同空间加载方案的情况,确定了不同截面及长度的30根试件,加载方案为5种.通过试验方案优化,实现了圆钢管空间加载的模拟,并获得了这些试件的荷载位移滞回曲线及典型部位的应变曲线.试验结果表明:圆钢管具有良好的滞回性能,在很大的位移作用情况下,仍能保持良好的耗能能力.为后续开展符合圆钢管截面钢材的本构模型研究奠定基础.     

Seismic Behaviour of Beam-Column Joints of Precast and Partial Steel Reinforced Concrete

A beam-column joint of precast and partial steel reinforced concrete( PPSRC) is proposed for precast reinforced concrete frames. The PPSRC consists of partial steel and reinforced concrete. The partial steel is located in the core joint region and the connections between concrete members. This paper presents an experimental study of a series of PPSRC specimens. These specimens are tested under low cyclic loading.Experimental results demonstrate that the bearing capacity of the PPSRC specimens is 3 times that of the ordinary reinforced concrete( RC) beam-column joints. The strength and stiffness degradation rates are slower compared with that of the RC beam-column joints. In addition,the strength of the core joint region and the connections is higher than other parts of the PPSRC specimens. Beam failure occurs firstly for the PPSRC specimens,followed by column failure and connections failure. The failure of the core joint region occurs finally.Test results show that the seismic performance of the PPSRC is better than that of the ordinary RC beam-column joints.     

基于变截面支撑的半刚接钢框架抗震性能

为了深入研究钢框架体系抗震性能,基于支撑杆件受力情况以及实际钢结构工程中梁柱节点连接形式,提出了基于变截面支撑-半刚接钢框架结构体系.首先,通过拟静力试验加载考察变截面支撑构件的滞回性能;进而,将试验结果与ANSYS有限元分析结果进行对比;最后,通过有限元模拟对结构体系进行时程分析,以考察体系的抗震性能.结果表明:变截面支撑的半刚接钢框架体系抗震性能良好.     

环口套管加强型T型圆钢管节点的滞回性能研究

为了提高桁架管节点的承载力及抗震性能,采用环口套管加强方式对管节点进行加强.基于有限元分析环口套管加强型管节点在承受轴向循环荷载作用下的滞回性能.通过分析发现:环口套管加强模型滞回曲线包围的面积显著大于未加固模型滞回曲线所包围的面积.同时,由于环口套管提高了节点相贯部位的主管刚度,使得破坏部位于相贯处的焊趾处转移到了套管两端边缘部位的主管表面.此外,基于有限元计算结果,分析了模型的延性比和能量耗散等抗震性能参数.结果表明:加强型节点的延性比和能量耗散值均有大幅度提高.     

基于CuZnAl形状记忆合金的框架结构抗震减振控制

利用形状记忆合金的本构关系,分析了在自由应力状态下的残余应变与温度的关系.使用动态数据采集分析仪,测试了安装CuZnAl形状记忆合金耗能器的框架结构的减振性能;应用电子万能拉伸试验机测试了CuZnAl形状记忆合金的应力-应变滞回曲线,借助透射电子显微镜,分析了CuZnAl形状记忆合金在热机械循环过程中显微组织的变化;比较了不同热处理工艺对CuZnAl形状记忆合金热机械循环后的滞回曲线面积及减振性能的影响.结果表明:CuZnAl形状记忆合金用于框架结构具有较好的减振效果,可明显降低框架结构的振动频率,其中马氏体CuZnAl形状记忆合金耗能器具有较大的耗能能力,经室温水淬时效7 h处理后减振效果最好.