EIS evaluation of the filiform corrosion of aluminium coated by a cataphoretic paint

Filiform corrosion is mainly considered as a cosmetic attack and is undesirable in most applications. The initiation and propagation of the filaments are related to different parameters such as the presence of defects, the permeability of the coating to water and oxygen, the adherence of the paint system and the presence of salts.

The aim of this work is to study the behaviour of painted aluminium samples towards filiform corrosion or delamination. The 6082 Aluminium alloy was selected and the samples were covered with a cataphoretic epoxy primer without lead (PPG Industries France). Prior to the application of the electrocoat, the samples were pre-treated by a commercial Zr/Ti or chromate conversion treatment or simply etched with a commercial acid etching product.

Filiform corrosion was studied by the normalized test (ISO/DIS 4623): painted and scratched samples were inoculated in HCl and exposed in a constant humidity chamber at 40 °C and 82% RH for 3 weeks. After exposure the samples were subjected to a visual and optical microscopic examination.

Electrochemical impedance spectroscopy was used to study the sensitivity to filiform corrosion. The operating mode of this test is similar to the normalized one. The samples were scratched before inoculation for 1 h in HCl and then exposed to the humidity chamber for a maximum of 4 days. The samples were tested by EIS in an acidified 0.1 M Na₂SO₄ electrolyte solution. The resulting impedance spectra were analyzed with an appropriate equivalent electrical circuit which allows the evaluation of the exposed metallic surface area, directly related to the extent of filiform corrosion or delamination. Different parameters were varied: the exposure time in the humidity chamber; the immersion time in the electrolyte sulphate solution as well as its pH and the coating thickness.     

Characterization of one-step,chromate-free,primer systems using liquid-state Si and C NMR

Coatings derived from organofunctional silanes have been investigated as possible replacements for the chromate-based systems used in the aerospace industry. In this study, organofunctional silanes [bis-(triethoxysilylpropyl)ethane and bis(triethoxysilylpropyl) tetrasulfide] were reacted with commercially available acrylate (ECO-CRYL™ 9790) and epoxy (EPI-REZ™ WD-510) resins, resulting in a one-step, low-VOC, chromate-free primer. Liquid-state ²⁹Si and ¹³C NMR were used to determine structural characteristics of various optimized formulations.     

厌氧胶快速渗补技术在汽车发动机上的应用

将金属铜易与过氧化物发生氧化还原反应生成游离基的原理应用于厌氧胶，开发了针时金属零件表面微孔进行局部渗补的实用技术。在相关技术可靠性和工艺可行性得以论证的前提下。将局部渗补技术成功地应用于渗补发动机泄漏缸盖，减少了废品损失，取得了良好的经济效益。     

Optimisation of metallic pigments in coatings by an electrochemical technique and an investigation of manganese powder as pigment for metal rich primers

Zinc dust and manganese powder as pigments were incorporated in epoxy-polyamide and butyl titanate medium, with different pigment volume concentration (PVC) ranging from 20 to 74. These protective coatings were coated on sand blasted mild steel substrates and immersed in 3 wt.% sodium chloride solution and the corrosion current was measured by the Tafel extrapolation method. From the corrosion current produced by these primers, the optimum level of the pigments in these binders was identified. Thus the protective performance of optimised primers was evaluated on a sand blasted mild steel surface by the Tafel polarisation method in 3 wt.% sodium chloride solution, over different periods of time. The results were found to be comparable with the salt spray test and galvanic current measurements. The manganese powder used for this investigation showed that it could be used as an alternative to zinc powder for metal rich primers.     

环氧富锌车间底漆的研制

通过大量的试验研究，设计了一个合理的环氧富锌车间底漆配方，制备出的涂料漆膜性能符合国家标准，且降低了涂料整体的污染程度。     

米糠油改性环氧酯铁红防锈底漆

米糠油主要由油酸、亚油酸和棕榈酸组成，属半干性油，具有了作为涂料基料的良好理化特性。研究表明，选用米糠油、桐油、环氧树脂和氧化铁红合成的铁红环氧酯防锈底漆，具有无毒、低温固化、防锈能力强等特点。本介绍了底漆的配方、生产工艺，并讨论了影响底漆性能的因素。     

Interphases in the Adhesive Bonding of Fluoropolymers

Strong and durable adhesive bonds may be made between polytetrafluoroethylene (PTFE) and either cyanoacrylate (CA) or epoxy adhesives, if the PTFE surface is modified by the use of a “primer” such as triphenylphosphine (TPP) or diaminodiphenylmethane (DDM). The primer mixes with the PTFE surface, and the modified surface is then capable of forming an interphase, tens to hundreds of nanometers thick, where interpenetration of the adhesive and adherend occurs. Using CA adhesives, PTFE/CA/PTFE block compression shear bond strength (ASTM D4501-85) of over 10 MPa can be achieved, with failure occurring cohesively. Initial work with epoxy adhesives indicates that the use of DDM primer gives adhesive bonds comparable in strength with those produced by modification of the fluoropolymer surface by sodium naphthalenide.     

腰果壳液改性胺固化无溶剂环氧底漆的特性研究

腰果壳液改性胺是一种新型环氧树脂固化剂,市场反映良好。对其固化性质作了进一步的探索,主要通过表干时间、附着力、剪切强度以及适用期的测试,研究腰果壳液改性酚醛胺类固化剂及其复配体系对无溶剂环氧底漆的固化特性。实验结果表明,腰果酚醛胺类固化剂在保持优异的附着力和剪切强度的情况下,提高了固化速度,是一种综合性能优异的固化剂。     

纤维素醚对瓷砖粘结剂主要性能的影响

本文通过正交试验摸索出纤维素醚对瓷砖粘结剂主要性能的影响及规律,通过比对胶粉的掺量、胶砂比对其部分性能的作用效果摸索出纤维素醚能够对其进行优化的主要方面,对于调节瓷砖粘结剂的部分性能具有一定的参考意义．     

有机-无机复合型建筑用封闭底漆的制备

采用硅溶胶、耐碱型苯丙乳液、云母粉、二氧化钛等颜填料制备有机-无机复合型建筑用非透明封闭底漆，以对比测试方法重点对其附着力、耐碱、抗渗透等性能进行验证，同时探讨了乳液、颜填料的选择因素以及硅溶胶对体系的作用和影响。