Transient liquid phase sintering of high-purity mullite for high-temperature structural ceramics

High-purity mullite ceramics, promising engineering ceramics for high-temperature applications, were fabricated using transient liquid phase sintering to improve their high-temperature mechanical properties. Small amounts of ultrafine alumina or silica powders were uniformly mixed with the mullite precursor depending on the silica-alumina ratio of the resulting ceramics to allow for the formation of a transient liquid phase during sintering, thus, enhancing densification at the early stage of sintering and mullite formation by the reaction between additional alumina and the residual glassy phase (mullitization) at the final stage of sintering. The addition of alumina powder to the silica-rich mullite precursor resulted in a reaction between the glassy silica and alumina phases during sintering, thereby forming a mullite phase without inhibiting densification. The addition of fine silica powder to the mullite single-phase precursor led to densification with an abnormal grain growth of mullite, whereas some of the added silica remained as a glassy phase after sintering. The resulting mullite ceramics prepared using different powder compositions showed different sintering behaviors, depending on the amount of alumina added. Upon selecting an optimum process and the amount of alumina to be added, the pure mullite ceramics obtained via transient liquid phase sintering exhibited high density (approximately 99%) and excellent high-temperature flexural strength (approximately 320 MPa) at 1500 °C in air. These results clearly demonstrate that pure mullite ceramics fabricated via transient liquid phase sintering with compositions close to those of stoichiometric mullite could be a promising process for the fabrication of high-temperature structural ceramics used in an ambient atmosphere. The transient liquid phase sintering process proposed in this study could be a powerful processing tool that allows for the preparation of superior high-temperature structural ceramics used in the ambient processing atmosphere.     

Study of Pb-based and Pb-free perovskite solar cells using Cu-doped Ni1-xO thin films as hole transport material

SCAPS solar cell simulation program was applied to model an inverted structure of perovskite solar cells using Cu-doped Ni_1-xO thin films as hole transport layer. The Cu-doped Ni_1-xO film were made by co-sputtering deposition under different deposition conditions. By increasing the amount of the Cu-dopant, the film crystallinity enhanced whereas the bandgap energy decreased. The transmittance of the thin films decreased significantly by increasing the sputtering power of copper. High quality, uniform, compact, and pin-hole free films with low surface roughness were achieved. The structural, chemical, surface morphology, optical, electrical, and electronic properties of the Cu doped Ni_1-xO films were used as input parameters in the simulation of Pb-based (MAPbI_3-xCl_x) and Pb-free (MAGeI₃) perovskite solar cells. Simulation results showed that the performance of both Pb-based and Pb-free perovskite solar cell devices significantly enhanced with Cu-doped Ni_1-xO film. The highest power conversion efficiency (PCE) for the Pb-free perovskite solar cell is 8.9% which is lower than the highest PCE of 17.5% for the Pb-based perovskite solar cell.     

Changes in the content and antioxidative activity of β-carotene and its metabolite vitamin A during gastrointestinal digestion and absorption and optimisation of HPLC-based detection

The β-Carotene (BC), an important precursor of vitamin A (VA), possesses antioxidant activity but is fat-soluble and has low bioavailability. In previous in-vitro assays evaluating antioxidant and 2,2′-azobis(2-amidinopropane) dihydrochloride (AAPH) free radical scavenging, both BC and VA showed a strong ability to scavenge radicals and protected cells from oxidative stress. Here, we used artificially simulated gastrointestinal digestion and Caco-2 cell absorption models to evaluate the bioavailability of the BC during gastrointestinal digestion and absorption using high-performance liquid chromatography (HPLC) analysis. We observed high absorptive and transfer rates of BC and detected retinol metabolites (Vitamin A). Therefore, BC can be detected in the acidic gastrointestinal environment using HPLC. Optimised method provided better separation of BC and VA in the column, improving the accuracy of the test results.     

Silver-substituted (Ag1-xCux)2ZnSnS4 solar cells from aprotic molecular inks

To battle the high open-circuit voltage deficit (V_OC,def) in kesterite (Cu₂ZnSnS₄ or CZTS) solar cells, a current field of research relates to point defect engineering by cation substitution. For example, by partly replacing Cu with an element of a larger ionic radius, such as Ag, the degree of Cu/Zn disorder decreases, and likewise does the associated band tailing. In this paper, solution-processed (Ag_1-xCu_x)₂ZnSnS₄ (ACZTS) samples are prepared through the aprotic molecular ink approach using DMSO as the solvent. The successful incorporation of silver into the CZTS lattice is demonstrated with relatively high silver concentrations, namely Ag/(Ag+Cu) ratios of 13% and 26%. The best device was made with 13% Ag/(Ag+Cu) and had an efficiency of 4.9%. The samples are compared to the pure CZTS sample in terms of microstructure, phase distribution, photoluminescence, and device performance. In the XRD patterns, a decrease in the lattice parameter c/a ratio is observed for ACZTS, as well as significant peak splitting with Ag addition for several of the characteristic kesterite XRD reflections. In addition to the improvement in efficiency, other advantageous effects of Ag-incorporation include enhanced grain growth and an increased band gap. A too high concentration of Ag leads to the formation of secondary phases such as SnS and Ag₂S as detected by XRD.     

Effects of the Anti-Tumorigenic Agent AT101 on Human Glioblastoma Cells in the Microenvironmental Glioma Stem Cell Niche

Glioblastoma (GBM) is a barely treatable disease due to its profound chemoresistance. A distinct inter- and intratumoral heterogeneity reflected by specialized microenvironmental niches and different tumor cell subpopulations allows GBMs to evade therapy regimens. Thus, there is an urgent need to develop alternative treatment strategies. A promising candidate for the treatment of GBMs is AT101, the R(-) enantiomer of gossypol. The present study evaluates the effects of AT101, alone or in combination with temozolomide (TMZ), in a microenvironmental glioma stem cell niche model of two GBM cell lines (U251MG and U87MG). AT101 was found to induce strong cytotoxic effects on U251MG and U87MG stem-like cells in comparison to the respective native cells. Moreover, a higher sensitivity against treatment with AT101 was observed upon incubation of native cells with a stem-like cell-conditioned medium. This higher sensitivity was reflected by a specific inhibitory influence on the p-p42/44 signaling pathway. Further, the expression of CXCR7 and the interleukin-6 receptor was significantly regulated upon these stimulatory conditions. Since tumor stem-like cells are known to mediate the development of tumor recurrences and were observed to strongly respond to the AT101 treatment, this might represent a promising approach to prevent the development of GBM recurrences.     

In Vivo Albumin-Binding of a C-Functionalized Cyclam Platform for 64Cu-PET/CT Imaging in Breast Cancer Model

An improved glucose-chelator-albumin bioconjugate (GluCAB) derivative, GluCAB-2^Mal, has been synthesized and studied for in vivo ⁶⁴Cu-PET/CT imaging in breast cancer mice models together with its first-generation analogue GluCAB-1^Mal. The radioligand works on the principle of tumor targeting through the enhanced permeability and retention (EPR) effect with a supportive role played by glucose metabolism. [⁶⁴Cu]Cu-GluCAB-2^Mal (99 % RCP) exhibited high serum stability with immediate binding to serum proteins. In vivo experiments for comparison between tumor targeting of [⁶⁴Cu]Cu-GluCAB-2^Mal and previous-generation [⁶⁴Cu]Cu-GluCAB-1^Mal encompassed microPET/CT imaging and biodistribution analysis in an allograft E0771 breast cancer mouse model. Tumor uptake of [⁶⁴Cu]Cu-GluCAB-2^Mal was clearly evident with twice as much accumulation as compared to its predecessor and a tumor/muscle ratio of up to 5 after 24 h. Further comparison indicated a decrease in liver accumulation for [⁶⁴Cu]Cu-Glu-CAB-2^Mal.     

高岭土性质对催化裂化催化剂性能的影响

采用X射线荧光分析仪、X射线衍射仪、N2物理吸附仪、场发射扫描电子显微镜等仪器表征了苏州、广西和美国佐治亚州3个产地的高岭土，并以此3种高岭土为原料制备了模型催化裂化（FCC）催化剂，在ACE评价装置上对比了模型催化剂的反应性能。结果表明:苏州及广西高岭土主要组分为高岭石，佐治亚高岭土主要组分为地开石及珍珠陶土；苏州高岭土呈片状，还含有少量棒状颗粒；广西高岭土呈多层片状，晶粒粒径较大；佐治亚高岭土呈薄片状，晶粒粒径较小；3种高岭土制备的模型催化剂反应活性、Na2O及RE2O3质量分数相近；广西高岭土制备的模型催化剂具有最大的孔体积和磨损指数，但比表面积最小，具有较强的重油转化能力，其目标产物（液化气+汽油）和副产物（干气+焦炭）收率都高于苏州、佐治亚高岭土制备的催化剂的。