Eco-friendly tape casting of borosilicate glass/Al2O3 sheets for LTCC applications

This work reports the innovative development of a borosilicate glass/Al₂O₃ tape for LTCC applications using an eco-friendly aqueous tape casting slurry. Polyvinylpyrrolidone (PVP) and polyacrylic acid (PAA) were the respective dispersants, while carboxymethyl cellulose (CMC) and styrene acrylic emulsion (SA) were the respective binders. The results showed that PVP was more suitable than PAA as the dispersant for the aqueous casting slurry, and that 1.5 wt% PVP would achieve well dispersion of CABS glass/Al₂O₃ powder in the aqueous slurry. Moreover, a small amount of 2.0 wt% CMC binder could yield smooth CABS glass/Al₂O₃ tapes crack free. A high-quality CABS glass/Al₂O₃ tape with a smooth surface was made from an aqueous slurry containing 1.5 wt% PVP dispersant, 2.0 wt% CMC binder, and 2.0 wt% PEG-400 plasticizer. The density, tensile strength, and surface roughness of the green tape were 2.05 g/cm³, 0.87 MPa, and 148 nm, respectively. The resulting CABS glass/Al₂O₃ composites sintered at 875 °C exhibited a bulk density of 3.14 g/cm³, a dielectric constant of 8.09, a dielectric loss of 1.0 × 10^?3, a flexural strength of 213 MPa, a thermal expansion coefficient of 5.30 ppm/^°C, and a thermal conductivity of 3.2 W m^?1 K^?1, thus demonstrating its broad prospects in LTCC applications.     

Effect of microwave heating time on the gel properties of chicken myofibrillar proteins and their formation mechanism

The present work was conducted to illustrate the mechanism of gel formation of myofibrillar proteins (MPs) under different microwave heating times. The results showed that the denaturation enthalpy (ΔH) of the MPs significantly decreased when the heating time increased from 3 to 9 s and then completely disappeared as the heating time progressed, indicating that the MPs gradually denatured and subsequently aggregated with increasing heating time, which was further verified by the changes in the secondary structure, electrophoretic bands, and gel properties (e.g., water holding capacity and textural profiles) of the MPs. Microstructural images indicated that the MP gel formed under 12 s had the most compact network, indicating that extended microwave heating time could induce quality deterioration of MP gels. Moreover, the hydrophobic forces, electrostatic forces, and disulphide bonds of the MPs gradually intensified with increasing microwave heating time, suggesting that both non-covalent and covalent bonds could promote molecular denaturation and subsequent aggregation of MPs. In addition, correlation analysis revealed that the changes in the molecular conformation of MPs induced by different microwave heating times could effectively regulate the formation of MP gels and their related properties.     

Anisotropic thermal expansion and ionic conductivity of a crystal-oriented,Mg2+-conducting NASICON-type solid electrolyte

Multivalent ion-conducting ceramics are required for the manufacture of high-safety, high-capacity rechargeable batteries. However, the low ionic conductivity of solid electrolytes and discrepancies in the thermal expansion between the battery components limit their widespread application. Furthermore, anisotropic thermal expansion in crystals during battery manufacturing and the charge-discharge cycles causes the formation of microcracks, which degrade the battery performance. The physical properties of ceramic materials with anisotropic crystal structures can be modified by varying the crystallographic orientation of their grains. In this study, a co-precipitation approach was used to synthesize an Mg²⁺-conducting (Mg_0.1Hf_0.9)_4/3.8Nb(PO₄)₃ solid electrolyte, and the grain orientation in the bulk sample was controlled using strong magnetic fields during the slip casting process. The results showed that inducing an orientation along the c-axis enhanced the apparent ionic conductivity of the bulk sample. It was also observed that (Mg_0.1Hf_0.9)_4/3.8Nb(PO₄)₃ crystal has a negative volumetric thermal expansion despite a positive linear thermal expansion along its c-axis. By adjusting the c-axis orientation of the grains, (Mg_0.1Hf_0.9)_4/3.8Nb(PO₄)₃ electrolytes with negative or positive linear thermal expansion coefficient have been produced. The findings of this study suggest that solid-electrolytes with negative, positive, or zero linear thermal expansion can be produced to create more compatible and higher-performance solid-state devices.     

Understanding grain refining and anti Si-poisoning effect in Al-10Si/Al-5Nb-B system

Grain refinement is critical for fabricating high-quality Al-Si casting components in the application of automobile and aerospace industries,while the well-known Si-poisoning effect makes it difficult.Nbbased refiners offer an effective method to refine Al-Si casting alloys,but their anti Si-poisoning capability is far from being understood.In this work,the grain refining mechanism and the anti Si-poisoning effect in the Al-10 Si/Al-5 Nb-B system were systematically investigated by combining transmission electron microscope,first-principles calculations,and thermodynamic calculations.It is revealed that NbB₂provides the main nucleation site in the Al-10 Si ingot inoculated by 0.1 wt.%Nb Al-5 Nb-B refiner.The exposed Nb atoms on the(0001)NbB₂and(1-100)NbB₂surface can be substituted by Al to form(Al,Nb)B₂intermedia layers.In addition,a layer of NbAl₃-like compound(NbAl₃')can cover the surface of NbB₂with the orientation relation of(1-100)[11-20]NbB_2//(110)[110]NbAl₃'.Both of the(Al,Nb)B₂and NbAl₃'intermedia layers contribute to enhancing the nucleation potency of NbB₂particles.These discoveries provide fundamental insight to the grain refining mechanism of the Nb-B based refiners for Al-Si casting alloys and are expected to guide the future development of stronger refiners for Al-Si casting alloys.     

Hierarchical electromagnetic absorption in micro-waveguide stuffed with magnetic media for resin-based composites of graphene nanosheets and manganese oxides

Waveguide configurations of hierarchical system are proposed as new microstructures for composites in absorbing enhancement. Supercritical fluid (SCF) one-pot exfoliation of layered graphite and manganese oxide mixing materials is developed to obtain a hierarchical system, containing graphene nanosheets (GNS) and exfoliated manganese oxides (EMO) in different sizes. Composites with GNS–EMO embedded in epoxy resin matrix are produced for a design of dielectric and magnetic loss integrated absorber. Volume fraction of GNS–EMO in composites is given for an optimal quantity of resin epoxy in fixation and formation. The effect of mixing ratios between electric and magnetic components is provided for the design of dielectric and magnetic loss integrated absorbers. Frequency shifting phenomena are revealed in the component adjusting course. Excluding the offsetting sizes, reflection loss of composites is enhanced as thickness increases. Synergistic effect of electric and magnetic coordinated materials demonstrates the superiority of micro-waveguide structures in GNS–EMO composite absorber.     

Photochemical Reactions in Supramolecular Assemblies of Gels: Dimerizations and Polymerizations via Pericyclic Reactions

Gel state reactions offer new direction for the reactivity of the organic molecules or metal‐organic materials upon photoirradiation with shorter reaction times and high yields compared to solid and solution states. The restricted molecular movement among the molecules in the soft solids control the stereoselectivity of the photoproducts in the gel state reactions. To date, most of the strategies based on self‐assembly have been demonstrated in the solid state, in particular for [2+2] reactions of olefins and polymerization reactions of diacetylenes via 1,4 addition. The soft materials are of emerging materials in recent days given their many applicative day‐to‐day aspects. This review gives a glimpse of recent reports on pericyclic reactions in the gel state that are designed based on the self‐assembly concept. Also it highlights how such reactions accompany the physical changes in the structure of the gels and stereo controlled products with high yields.     

Effect of Li2O on the crystallization behavior of CaO-Al2O3-SiO2-Li2O-Ce2O3 mold slags

The effect of Li₂O on the crystallization properties of CaO-Al₂O₃-SiO₂-Li₂O-Ce₂O₃ slags was investigated. With increasing the Li₂O content, LiAlO₂ and CaCeAlO₄ were the main crystalline phases. LiAlO₂ formed for the charge compensating of Li⁺ ions to [AlO₄^5?]-tetrahedrons, and CaCeAlO₄ formed as a result of the charge balance of Ce³⁺ ions, Ca²⁺ ions, and [AlO₆^9?]-octahedrons. Increasing the content of Li₂O to 10%, the crystallization temperature was the highest, and the incubation time was the shortest. The crystallization ability was strong due to the three factors of strengthening the interaction between ions and ion groups, decreasing the polymerization degree, and increasing the melting temperature. Further increasing the content of Li₂O, the crystallization performance was obviously suppressed, because the melting temperature and the force between the cations and the anion groups decreased.     

Quasi-static compressive behaviour of aluminium cenosphere syntactic foams

In this paper, cenosphere particles embedded in AA2014 aluminium matrix are used to fabricate syntactic foam by stir casting method. The particle size is about 100?µm and foam density is about 1990?kg?m^?3. Compression tests at strain rate 0.001/s are performed on foam samples to characterise their mechanical properties which are then used in numerical analysis on commercial finite element analysis software ABAQUS/CAE with isotropic elastic-plastic material model. Experimental and numerical results show good conformity in deformation behaviour with elastic and plateau zones showing average deviations less than 5% and 20%, respectively. Foams showed high yield stress and energy absorption capabilities that can be useful in making blast and impact resistant structures.     

Structures and properties of chicken myofibrillar protein gel induced by microwave heating

Structures and properties of myofibrillar protein gel prepared at different power (300–800 W) were evaluated. Amino acid analysis demonstrated that changes in microwave power did not alter primary structure of gel. However, an increase in microwave power could change higher structures of gel. As microwave power increased, α-helix content decreased and β-sheet content increased. Increased microwave power probably facilitated protein to unfold and expose the internal groups, causing surface hydrophobicity and the formation of disulphide bonds were enhanced, which indicated changes in tertiary and quaternary structures of protein. At 500 W, gel had the best ultrastructure where surface morphology, springiness and water holding capacity reached the optimum. Our findings suggested that microwave at an appropriate power (500 W) could change higher structures of myofibrillar protein gel to achieve desired processing and quality protein gel characteristics.