Effects of an inhomogeneous electron density distribution on the hydrogen distribution in TiZrTaNbAl multi-principal element alloys

A body-centered cubic equiatomic TiZrTaNbAl multi-principal element alloy (MPEA) with elemental fluctuations was investigated to further understand the relationship between the microstructure and hydrogen distribution. In this study, a composition dependence of the hydrogen distribution was observed in the TiZrTaNbAl MPEA. An inhomogeneous electron density distribution of the MPEA was revealed by advanced differential phase-contrast scanning electron microscopy (DPC-STEM) for the first time. The results showed that the electron density has a significant effect on the hydrogen distribution in TiZrTaNbAl MPEAs. This work provides new insight into the design of materials with high hydrogen storage capacity and high hydrogen embrittlement resistance.     

Performance evaluation of basalt fiber-reinforced geopolymer composites with various contents of nano CaCO3

High carbon footprint of cement production is the major drawback of plain cement concrete resulting in environmental pollution. Geopolymer composites paste can be effectively used as an alternative to Portland cement in the construction industry for a sustainable environment. The demand for high-performance composites and sustainable construction is increasing day by day. Therefore, the present experimental program has endeavored to investigate the mechanical performance of basalt fiber-reinforced fly ash-based geopolymer pastes with various contents of nano CaCO₃. The content of basalt fibers was fixed at 2% by weight for all specimens while the studied contents of nano CaCO₃ were 0%, 1%, 2%, and 3%, respectively. The compressive strength, compressive stress-strain response, flexural strength, bending stress-strain response, elastic modulus, toughness modulus, toughness indices, fracture toughness, impact strength, hardness, and microstructural analysis of all four geopolymer composite pastes with varying contents of nano CaCO₃ using scanning electron microscopy (SEM) were evaluated. The results revealed that the use of 3% nano CaCO₃ in basalt fiber-reinforced geopolymer paste presented the highest values of compressive strength and hardness while the use of 2% nano CaCO₃ showed the highest values of flexural strength, impact strength, and fracture toughness of composite paste. The SEM results indicated that the addition of nano CaCO₃ improved the microstructure and provided a denser geopolymer paste by refining the interfacial zones and accelerating the geopolymerization reaction.     

Designing amorphous formulations of polyphenols with naringin by spray-drying for enhanced solubility and permeability

Naringin (NAR), a major flavanone (FVA) glycoside, is a component of food mainly obtained from grapefruit. We used NAR as a food additive to improve the solubility and permeability of hydrophobic polyphenols used as supplements in the food industry. The spray-dried particles (SDPs) of NAR alone show an amorphous state with a glass transition temperature (T_g) at 93.2 °C. SDPs of hydrophobic polyphenols, such as flavone (FVO), quercetin (QCT), naringenin (NRG), and resveratrol (RVT) were prepared by adding varying amounts of NAR. All SDPs of hydrophobic polyphenols with added NAR were in an amorphous state with a single T_g, but SDPs of hydrophobic polyphenols without added NAR showed diffraction peaks derived from each crystal. The SDPs with NAR could keep an amorphous state after storage at a high humidity condition for one month, except for SDPs of RVT/NAR. SDPs with NAR enhanced the solubility of hydrophobic polyphenols, especially NRG solubility, which was enhanced more than 9 times compared to NRG crystal. The enhanced solubility resulted in the increased membrane permeability of NRG. The antioxidant effect of the hydrophobic NRG was also enhanced by the synergetic effect of NAR. The findings demonstrated that NAR could be used as a food additive to enhance the solubility and membrane permeability of hydrophobic polyphenols.     

Boron doping induced electronic reconfiguration of Fe-Nx sites in N-doped carbon matrix for efficient oxygen reduction reaction in both alkaline and acidic media

Developing non-precious metal-based catalysts as the substitution of precious catalysts (Pt/C) in oxygen reduction reaction (ORR) is crucial for energy devices. Herein, a template and organic solvent-free method was adopted to synthesize Fe, B, and N doped nanoflake-like carbon materials (Fe/B/N–C) by pyrolysis of monoclinic ZIF-8 coated with iron precursors and boric acid. Benefiting from introducing B into Fe–N–C, the regulated electron cloud density of Fe-N_x sites enhance the charge transfer and promotes the ORR process. The as-synthesized Fe/B/N–C electrocatalyst shows excellent ORR activity of a half-wave potential (0.90 V vs 0.87 V of Pt/C), together with superior long-term stability (95.5% current density retention after 27 h) in alkaline media and is even comparable to the commercial Pt/C catalyst (with a half-wave potential of 0.74 V vs 0.82 V of Pt/C) in an acidic electrolyte. A Zn-air battery assembled with Fe/B/N–C as ORR catalyst delivers a higher open-circuit potential (1.47 V), specific capacity (759.9 mA h g^?1_Zn at 10 mA cm^?2), peak power density (62 mW cm^?2), as well as excellent durability (5 mA cm^?2 for more than 160 h) compared to those with commercial Pt/C. This work provides an effective strategy to construct B doped Fe–N–C materials as nonprecious ORR catalyst. Theoretical calculations indicate that introduction of B could induce Fe-N_x species electronic configuration and is favorable for activation of OH1 intermediates to promote ORR process.     

High-resolution FIB-TEM-STEM structural characterization of grain boundaries in the high dielectric constant perovskite CaCu3Ti4O12

In this work, the grain boundaries composition of the polycrystalline CaCu₃Ti₄O₁₂ (CCTO) was investigated. A Focused Ion Beam (FIB)/lift-out technique was used to prepare site-specific thin samples of the grain boundaries interface of CCTO ceramics. Scanning transmission electron microscopy (STEM) coupled with energy dispersive X-ray spectrometry (EDXS) and Electron Energy Loss Spectroscopy (EELS) systems were used to characterize the composition and nanostructure of the grain and grain boundaries region. It is known that during conventional sintering, discontinuous grain growth occurs and a Cu-rich phase appears at grain boundaries. This Cu-rich phase may affect the final dielectric properties of CCTO but its structure and chemical composition remained unknown. For the first time, this high-resolution FIB-TEM-STEM study of CCTO interfacial region highlights the composition of the phases segregated at grain boundaries namely CuO, Cu₂O and the metastable phase Cu₃TiO_4.     

Alloying behavior and novel properties of CoCrFeNiMn high-entropy alloy fabricated by mechanical alloying and spark plasma sintering

An equiatomic CoCrFeNiMn high-entropy alloy was synthesized by mechanical alloying (MA) and spark plasma sintering (SPS). During MA, a solid solution with refined microstructure of 10 nm which consists of a FCC phase and a BCC phase was formed. After SPS consolidation, only one FCC phase can be detected in the HEA bulks. The as-sintered bulks exhibit high compressive strength of 1987 MPa. An interesting magnetic transition associated with the structure coarsening and phase transformation was observed during SPS process.     

Red-shift and improved afterglow of Sr3Al2-xBxO5Cl2:Eu2+, Dy3+ phosphors via a cation substitution strategy

Sr₃Al_2-xB_xO₅Cl₂:Eu²⁺, Dy³⁺ (x = 0, 0.2, 0.4) long persistent phosphors were prepared via solid-state process. The pristine Sr₃Al₂O₅Cl₂:Eu²⁺, Dy³⁺ phosphor exhibits orange/red broad band emission around 609 nm, which can be attributed to the electric radiation transitions 4f⁶5 d¹→4f⁷ of Eu²⁺. Upon the same excitation, the B³⁺-doped Sr₃Al_2-xB_xO₅Cl₂:Eu²⁺, Dy³⁺ phosphors display red-shift from 609 nm to 625 nm with increasing B³⁺ concentrations. The XRD patterns show that Al³⁺ can be replaced by B³⁺ in the host lattice at the tetrahedral site, which causes lattice contraction and crystal field enhancement, and thereafter achieves the red-shift on the emission spectrum. The XPS investigation provides direct evidence of the dominant 2-valent europium in the phosphor, which can be ascribed for the broad band emission of the prepared phosphors. The afterglow of all phosphors show standard double exponential decay behavior, and the afterglow of Sr₃Al₂O₅Cl₂:Eu²⁺, Dy³⁺is rather weak, while the sample co-doped with B³⁺shows longer and stronger afterglow, as confirmed after the curve simulation. The analysis of thermally stimulated luminescence showed that, when B³⁺ is introduced, a much deeper trap is created, and the density of the electron trap is also significantly increased. As a result, B³⁺ ions caused redshift and enhanced afterglow for the Sr₃Al_2-xB_xO₅Cl₂:Eu²⁺, Dy³⁺ phosphor.     

Preparation,characterization and properties of polycaprolactone diol-functionalized multi-walled carbon nanotube/thermoplastic polyurethane composite

Multi-walled carbon nanotubes (MWCNTs) were chemically functionalized to prepare thermoplastic polyurethane (PU) composites with enhanced properties. In order to achieve a high compatibility of functionalized MWCNTs with the PU matrix, polycaprolactone diol (PCL), as one of PU’s monomers, was selectively grafted on the surface of MWCNTs (MWCNT–PCL), while carboxylic acid groups functionalized MWCNTs (MWCNT–COOH) and raw MWCNTs served as control. Both MWCNT–COOH and MWCNT–PCL improved the dispersion of MWCNTs in the PU matrix and interfacial bonding between them at 1 wt% loading fraction. The MWCNT–PCL/PU composite showed the greatest extent of improvement, where the tensile strength and modulus were 51.2% and 33.5% higher than those of pure PU respectively, without sacrificing the elongation at break. The considerable improvement in both mechanical properties and thermal stability of MWCNT–PCL/PU composite should result from the homogeneous dispersion of MWCNT–PCL in the PU matrix and strong interfacial bonding between them.     

Binary Ti–Fe system. Part I: Experimental investigation at high pressure

The present work illustrates the effect of quasi-hydrostatic pressure on the positions and widths of the homogeneity ranges of the intermetallic phases TiFe and TiFe₂ at high temperatures. The experiments were performed with Ti–Fe diffusion couples that were heat treated in a multi-anvil press at 2.5 GPa. The solubility limits of the phases were derived from the concentration profiles that were measured using electron probe microanalysis. It was found that the homogeneity ranges of TiFe and TiFe₂ extend to higher titanium concentrations, if the pressure is applied. The positions of the phase boundaries of the intermetallics on the iron-rich side are not affected by the pressure. The accuracy of the experimental data including the homogeneity ranges and temperatures was verified by comparing the homogeneity ranges of β-Ti(Fe), α/δ-Fe(Ti) and γ-Fe measured in this study with the homogeneity ranges taken from literature. The pressure was calibrated using the pressure-induced phase transitions of bismuth.     

Synthesis,structure, stability and phase diagrams of selected bimetallic silver- and nickel-based nanoparticles

An overview of the research on silver-based (Ag-Sn, Ag-Cu, Ag-Ni) and nickel-based (Cu-Ni, Au-Ni, Ni-Pt) bimetallic nanoparticles is presented. The investigated nanoparticles in this review are formed by elements that represent an important group of metals revealing fcc lattice under macro-sized conditions (with the exception of Sn). The effects of surface stabilizing layer of the alloy nanoparticles are also described. Our experience with synthesis, characterization and stabilization of alloy nanoparticles is summarized. The development of the nanoparticle synthesis represents an important and mandatory part of the experimental nanoalloy research. Main synthetic routes under focus are the low temperature borohydride reduction method, the high temperature oleylamine synthesis, and the high pressure method in autoclave. The subsequent structural studies are focused on both nanoparticle core and outer stabilizing layer. The cores of the nanoparticles are studied mainly by electron microscopy techniques. The phase stability of the nanoparticle core is investigated by thermal analysis. The Knudsen effusion mass spectrometry was applied for studies of stabilizing organic molecules that can be found on the surface of the nanoparticles. The presented overview of the experimental results is complemented by thermodynamic calculations of phase diagrams by the CALPHAD method.