Transient liquid phase sintering of high-purity mullite for high-temperature structural ceramics

High-purity mullite ceramics, promising engineering ceramics for high-temperature applications, were fabricated using transient liquid phase sintering to improve their high-temperature mechanical properties. Small amounts of ultrafine alumina or silica powders were uniformly mixed with the mullite precursor depending on the silica-alumina ratio of the resulting ceramics to allow for the formation of a transient liquid phase during sintering, thus, enhancing densification at the early stage of sintering and mullite formation by the reaction between additional alumina and the residual glassy phase (mullitization) at the final stage of sintering. The addition of alumina powder to the silica-rich mullite precursor resulted in a reaction between the glassy silica and alumina phases during sintering, thereby forming a mullite phase without inhibiting densification. The addition of fine silica powder to the mullite single-phase precursor led to densification with an abnormal grain growth of mullite, whereas some of the added silica remained as a glassy phase after sintering. The resulting mullite ceramics prepared using different powder compositions showed different sintering behaviors, depending on the amount of alumina added. Upon selecting an optimum process and the amount of alumina to be added, the pure mullite ceramics obtained via transient liquid phase sintering exhibited high density (approximately 99%) and excellent high-temperature flexural strength (approximately 320 MPa) at 1500 °C in air. These results clearly demonstrate that pure mullite ceramics fabricated via transient liquid phase sintering with compositions close to those of stoichiometric mullite could be a promising process for the fabrication of high-temperature structural ceramics used in an ambient atmosphere. The transient liquid phase sintering process proposed in this study could be a powerful processing tool that allows for the preparation of superior high-temperature structural ceramics used in the ambient processing atmosphere.     

A knowledge-based archive multi-objective simulated annealing algorithm to optimize series–parallel system with choice of redundancy strategies

Redundancy allocation problem (RAP) is one of the best-developed problems in reliability engineering studies. This problem follows to optimize the reliability of a system containing s sub-systems under different constraints, including cost, weight, and volume restrictions using redundant components for each sub-system. Various solving methodologies have been used to optimize this problem, including exact, heuristic, and meta-heuristic algorithms. In this paper, an efficient multi-objective meta-heuristic algorithm based on simulated annealing (SA) is developed to solve multi-objective RAP (MORAP). This algorithm is knowledge-based archive multi-objective simulated annealing (KBAMOSA). KBAMOSA applies a memory matrix to reinforce the neighborhood structure to achieve better quality solutions. The results analysis and comparisons demonstrate the performance of the proposed algorithm for solving MORAP.     

Ca2+ doping effects on the structural and electrical properties of Na0.5Bi4.5Ti4O15 piezoceramics

Bismuth layer structured Na_0.5Bi_4.5Ti₄O₁₅ (NBT) ferroelectric is one of the most promising materials for potential applications at high temperature. However, it is challenged to achieve a balance between high Curie temperature piezoelectric coefficient and excellent thermal stability for NBT piezoceramics. Here, through chemical modification at the A site of NBT with Ca²⁺, novel (Na_0.5Bi_0.5)_1-xCa_xBi₄Ti₄O₁₅ piezoceramics with excellent properties fabricated by solid state reaction were studied. After doping of Ca²⁺, the Curie temperature T_C increased from 648 °C to 662 °C while the piezoelectric coefficient d₃₃ increased from 14 pC/N to 22 pC/N which can be attributed to the intrinsic contribution of TiO₆ octahedral lattice distortion (tilting and rotation) and the extrinsic contribution of the increased density of domain walls. The composition of (Na_0.5Bi_0.5)_0.95Ca_0.05Bi₄Ti₄O₁₅ ceramics with x = 0.05 has the optimal performance with high T_C of 655 °C, large d₃₃ of 22 pC/N, high electrical resistivity ρ close to 10⁷ Ω cm at 500 °C and especially excellent thermal stability of d₃₃ only about 5% reduction after being annealed at 625 °C. The work effectively reveals the great potential of CNBT-5 ceramics for high-temperature piezoelectric applications.     

Damage mechanism at different transpassive potentials of solution-annealed 316 and 316l stainless steels

Electrochemical impedance spectroscopy (EIS), anodic polarization and scanning electron microscopy techniques were used to investigate the damage mechanism in the transpassive potential region of AISI ...     

On the thermally-induced seizure in bearings: A review

This paper presents a state-of-the-art survey of papers reported on the nature of a troublesome failure mode in bearings known as seizure. This mode of failure is thermally-induced and it occurs in both journal and rolling element bearings. To gain insight, particular attention is given to reported experimental observation, various mechanisms involved, and available prediction methodologies.     

Enhancement of optical and electrical properties of SILAR deposited ZnO thin films through fluorine doping and vacuum annealing for photovoltaic applications

Undoped and fluorine doped ZnO thin films were deposited onto glass substrates using successive ionic layer adsorption and reaction (SILAR) technique and then annealed at 350 °C in vacuum ambience. The F doping level was varied from 0 to 15 at% in steps of 5 at%. The XRD analysis showed that all the films are polycrystalline with hexagonal wurtzite structure and preferentially oriented along the (002) plane. Crystallite sizes were found to increase when 5 at% of F is doped and then decreased with further doping. It was seen from the SEM images that the doping causes remarkable changes in the surface morphology and the annealing treatment results in well-defined grains with an improvement in the grain size irrespective of doping level. All the films exhibit good transparency (>70%) after vacuum annealing. Electrical resistivity of the film was found to be minimum (1.32×10⁻³ Ω cm) when the fluorine doping level was 5 at%.     

Stability and cytotoxicity study of NiFe2O4 nanocomposites synthesized by co-precipitation and subsequent thermal annealing

In this article, NiFe₂O₄ nanoparticles (NPs) were prepared by co-precipitation method with subsequent thermal annealing leading to obtainment NPs with average sizes of 78 nm. Structure and magnetic analysis were performed by X-ray diffraction, transmission electron microscopy, Mössbauer spectroscopy and vibrating sample magnetometry techniques. Stability of NiFe₂O₄ NPs was evaluated in PBS solution during 20 days. The toxicity of prepared NPs was evaluated in vitro using different cancer cell lines: HeLa (cervical cancer cell), PC-3 (prostate cancer cell). Fibroblasts like cells of L929 obtained from subcutaneous adipose tissue of mouse were used as normal cells. Results indicate successful synthesis of NiFe₂O₄ NPs that exhibit low cytotoxicity in concentration range from 1 to 100 μg/ml. Presented physical and biological results indicate the possibility of application investigated magnetic nanoparticles in hyperthermia, targeted drug delivery, magnetic resonance imaging or cell separation.     

Animations showing Lego manipulative tasks: Three potential moderators of effectiveness

Evidence suggests that transient visual information, such as animations, may be more challenging to learn than static visualizations. However, when a procedural-manipulative task is involved, our evolved embodied cognition seems to reverse this transitory challenge. Hence, for object manipulative tasks, instructional animations may be more suitable than statics. We investigated this argument further by comparing animations with statics using a Lego task shown to university students, by examining three potential moderators of effectiveness: (a) the environment of manipulation (virtual or physical), (b) the quality of visual information (focused or unfocused), and (c) the presence of hands (no hands or with hands). In Experiment 1 we found an advantage of animation over statics, and no differences among the environments. In Experiment 2, we again observed an animation advantage, a small advantage of focused static information compared to unfocused static information, and a positive effect of not showing the hands.     

WC/Cu复合材料制备及其高温性能

用机械合金化法结合冷变形，制备了WC／Cu复合材料，研究了冷变形后复合材料的组织特征和高温退火时韵性能变化。结果表明：烧结后的材料经冷变形，组织呈显著纤维状，WC颗粒弥散分布，密度明显提高，达到理论密度的99．2％；复合材料经600～900℃高温退火，强度和硬度略有下降，塑性则有大幅提高；900℃退火时未发生明显的再结晶，界面结合良好；所制备的WC／Cu复合材料有优良的综合性能。