An infinite chain, {[Ni(tn)2]3[Fe(CN)4(μ-CN)2]2}n,a new catalyst for electrochemical-driven water splitting and photochemical-driven hydrogen evolution from water under blue light

A new catalyst for both water reduction and oxidation, based on an infinite chain, {[Ni(tn)₂]₃ [Fe(CN)₄ (μ-CN)₂]₂}_n, is formed by the reaction of NiCl₂, 1,3-propanediamine (tn) and K₃ [Fe(CN)₆]. {[Ni(tn)₂]₃ [Fe(CN)₄ (μ-CN)₂]₂}_n can electro-catalyze hydrogen evolution from a neutral aqueous buffer (pH 7.0) with a turnover frequency (TOF) of 1561 mol of hydrogen per mole of catalyst per hour (H₂/mol catalyst/h) at an overpotential (OP) of 837 mV {[Ni(tn)₂]₃ [Fe(CN)₄ (μ-CN)₂]₂}_n also can electro-catalyze O₂ production from water with a TOF of ～45 mol O₂ (mol cat)^?1s^?1 at an OP of 591 mV. Under blue light (λ = 469 nm), together with CdS nanorods (CdS NRs) as a photosensitizer, and ascorbic acid (H₂A) as a sacrificial electron donor, {[Ni(tn)₂]₃ [Fe(CN)₄ (μ-CN)₂]₂}_n can photo-catalyze hydrogen generation from an aqueous buffer (pH 4.0) with a turnover number (TON) of 11,450 mol H₂ per mole of catalyst (mol of H₂ (mol of cat)^?1) during 10 h irradiation. The average of apparent quantum yield (AQY) is as high as 40.96% during 10 h irradiation. Studies indicate that {[Ni(tn)₂]₃ [Fe(CN)₄ (μ-CN)₂]₂}_n exists in two forms: a cyano-bridged chain ({[Ni(tn)₂]₃ [Fe(CN)₄ (μ-CN)₂]₂}_n) in solid, and a salt ([Ni(tn)₂]₃ [Fe(CN)₆]₂) in aqueous media; Catalytic reaction occurs on the nickel center of [Ni(tn)₂]²⁺, and the introduction of [Fe(CN)₆]^3- can improve the catalytic efficiency of [Ni(tn)₂]²⁺ for H₂ or O₂ generation. We hope these findings can afford a new method for the design of catalysts for both water reduction and oxidation.     

Investigation of the changes in physical properties of PES/PVC fabrics after aging

The aim of this work was to investigate the physical and mechanical performance of architectural polyester (PES)–poly(vinyl chloride) (PVC) membranes exposed to different artificial aging conditions. Two commercially available architectural membranes were chosen as research objects. The durability of the PES/PVC fabrics was evaluated by the loss in mechanical performance, scanning electron microscopy, and X-ray diffraction analysis in order to understand the effect of the degradation agents on the surface of the membranes. The mechanical performance of the PES/PVC membranes was unchanged. Scanning electron microscopy images of the tested materials showed initial cracks after aging. The X-ray fluorescence analysis showed that at the time of aging, the amount of Cl and Si decreased slightly, while Ti decreased by half, and Ca by volume increased twice. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 47523.     

建筑工业化发展的多群体演化博弈与仿真研究

新型建筑工业化具有高质量、低消耗、可循环发展等特征，其推广已上升到国家战略层面。利用演化博弈方法，建立“政府-开发商-银行” 的三方动态演化博弈模型，进行各博弈主体策略的演化稳定性分析，并针对初始状态、奖惩力度、借贷风险和开发成本等对演化结果的影响进行动态仿真。在此基础上， 考虑开发商群体的网络拓扑特征对演化真实性的影响，引入复杂网络理论， 以无标度网络为载体描述开发商个体的连接偏好和决策机制，构建政府监管下的建筑工业化扩散模型，并通过仿真深入研究相关因素对扩散深度的影响作用，最后结合仿真结果给出相应对策建议。     

Statistical Piezotronic Effect in Nanocrystal Bulk by Anisotropic Geometry Control

Utilizing inner-crystal piezoelectric polarization charges to control carrier transport across a metal-semiconductor or semiconductor–semiconductor interface, piezotronic effect has great potential applications in smart micro/nano-electromechanical system (MEMS/NEMS), human-machine interfacing, and nanorobotics. However, current research on piezotronics has mainly focused on systems with only one or rather limited interfaces. Here, the statistical piezotronic effect is reported in ZnO bulk composited of nanoplatelets, of which the strain/stress-induced piezo-potential at the crystals’ interfaces can effectively gate the electrical transport of ZnO bulk. It is a statistical phenomenon of piezotronic modification of large numbers of interfaces, and the crystal orientation of inner ZnO nanoplatelets strongly influence the transport property of ZnO bulk. With optimum preferred orientation of ZnO nanoplatelets, the bulk exhibits an increased conductivity with decreasing stress at a high pressure range of 200–400 MPa, which has not been observed previously in bulk. A maximum sensitivity of 1.149 µS m⁻¹ MPa⁻¹ and a corresponding gauge factor of 467–589 have been achieved. As a statistical phenomenon of many piezotronic interfaces modulation, the proposed statistical piezotronic effect extends the connotation of piezotronics and promotes its practical applications in intelligent sensing.     

Preparation and electrochemical characterization of Ti-based amorphous metallic glass with high strength

Ti-based amorphous metallic glasses have excellent mechanical, physical, and chemical properties, which is an important development direction and research hotspot of metal composite reinforcement. As a stable, simple, efficient, and large-scale preparation technology of metallic powders, the gas atomization process provides an effective way of preparing amorphous metallic glasses. In this study, the controllable fabrication of a Ti-based amorphous powder, with high efficiency, has been realized by using gas atomization. The scanning electron microscope, energy-dispersive spectrometer, and X-ray diffraction are used to analyze surface morphology, element distribution, and phase structure, respectively. A microhardness tester is used to measure the mechanical property. An electrochemical workstation is used to characterize corrosion behavior. The results show that as-prepared microparticles are more uniform and exhibit good amorphous characteristics. The mechanical test shows that the hardness of amorphous powder is significantly increased as compared with that before preparation, which has the prospect of being an important part of engineering reinforced materials. Further electrochemical measurement shows that the corrosion resistance of the as-prepared sample is also significantly improved. This study has laid a solid foundation for expanding applications of Ti-based metallic glasses, especially in heavy-duty and corrosive domains.     

Characterization of barium titanate reinforced acrylonitrile butadiene rubber composites for flexible electronic applications: influences of barium titanate content

The aim of this study was to develop high dielectric constant flexible polymers with a highly efficient and cost‐effective approach using acrylonitrile butadiene rubber (NBR) as the polymer matrix and barium titanate (BT) as the high dielectric constant filler. The BT powder was synthesized with a solid‐state reaction and was characterized using a particle size analyzer, XRD, SEM and Fourier transform infrared spectroscopy. NBR/BT composites were fabricated using an internal mixer with various BT loadings up to 160 phr. The influence of BT loading on the cure characteristics and mechanical, dynamic mechanical, thermal, dielectric and morphological properties was determined. The incorporation of BT in the NBR matrix shortened scorch time and increased delta torque. The mechanical properties, thermal stability and dielectric constant were greatly improved and increased with BT loading. The results suggest that the reinforcement effect was achieved due to strong hydrogen bonding or polar–polar interactions between NBR matrix and BT filler. This is further corroborated by the good dispersion of BT filler in the NBR matrix observed with SEM imaging. These findings can be applied to produce high‐performance dielectric elastomers. © 2020 Society of Industrial Chemistry     

Gluten-free cakes with walnut flour: a technological,sensory, and microstructural approach

Walnut flour (WF), a by-product of walnut oil production, is characterised by high polyunsaturated fatty acids, proteins, and fibre contents and presents suitability for bakery products. However, when using non-traditional ingredients, it is essential to evaluate the effect on the quality properties of the final product. So, this work aimed to assess the impact of WF on the technological, physicochemical, and sensory properties of gluten-free (GF) cakes. WF was added at a flour blend (cassava (CS) and maize (MS) starches and rice flour) at 0, 10%, 15%, and 20%. The results showed that WF modified starch gelatinisation, increased amylose–lipid complex (ALC) content, and made crumbs easier to chew. Besides, the total dietary fibre (TDF) and protein content significantly increased. Cakes with 15% WF presented the highest specific volume (SV) and no differences in overall acceptability with respect to control. Hence, WF is a suitable ingredient for gluten-free bakery products.     

Hydraulic reactivity and cement formation of baghdadite

In this study, the hydraulic reactivity and cement formation of baghdadite (Ca₃ZrSi₂O₉) was investigated. The material was synthesized by sintering a mixture of CaCO₃, SiO₂, and ZrO₂ and then mechanically activated using a planetary mill. This leads to a decrease in particle and crystallite size and a partial amorphization of baghdadite as shown by X-ray powder diffraction (XRD) and laser diffraction measurements. Baghdadite cements were formed by the addition of water at a powder to liquid ratio of 2.0 g/ml. Maximum compressive strengths were found to be ~2 MPa after 3-day setting for a 24-h ground material. Inductively coupled plasma mass spectrometry (ICP-MS) measurements showed an incongruent dissolution profile of set cements with a preferred dissolution of calcium and only marginal release of zirconium ions. Cement formation occurs under alkaline conditions, whereas the unground raw powder leads to a pH of 11.9 during setting, while prolonged grinding increased pH values to approximately 12.3.