Pressure-induced transparency of MgO,Al2O3, AlN,and cBN ceramics at room temperature

The in situ axial X-ray diffraction patterns of four ceramic powder samples (MgO, Al₂O₃, AlN, and cBN) that were compressed in a diamond anvil cell under uniaxial non-hydrostatic conditions were recorded. The microscopic deviatoric stress as a function of the pressure was determined from the X-ray diffraction peak broadening analysis: the curves increased approximately linearly with the pressure at the initial compression stage and then levelled off under further compression. Pressure-induced transparency was observed in all of the samples under compression, and the pressure at the turning point on the curves of the microscopic deviatoric stress versus pressure corresponded to the pressure at which the samples became transparent. Analysis of the microstructural features of the pressure-induced transparent samples indicated that the compression caused the grains to fracture, and the broken grains bonded with each other. We demonstrated that the ceramics’ pressure-induced transparency was a process during which the grains were squeezed and broken, the pores were close between the grains, and the broken grains were re-bonded under compression.     

Effects on the crystallite growth behavior of LaPO4 nanopowders and its mechanical properties

The effects of pH of the reaction solution and the concentration of phosphoric acid on the crystal growth behavior of LaPO₄ crystallites were investigated and the mechanical properties of rare-earth phosphates were compared. As a result, the concentration of phosphoric acid of 10% was beneficial to the crystal growth of LaPO₄ nanocrystalline. When the pH value of the reaction solution was 2, the size of LaPO₄ crystallites increased gradually with the increasing reaction temperature, and the smallest crystallite size of 43.27 nm was obtained after heat-treatment at 1000 °C. Simultaneously, the activation energy for crystal growth of LaPO₄ nanocrystalline was relatively lower (26.82 kJ mol⁻¹). With the decreasing radii of rare-earth ions, the hardness, Young's modulus and fracture toughness of the bulk rare-earth phosphates exhibited a reduced tendency, resulted from the increase of porosity under the same preparation process.     

Epitaxial Growth of 2D Materials on High-Index Substrate Surfaces

Recently, the successful synthesis of wafer-scale single-crystal graphene, hexagonal boron nitride (hBN), and MoS₂ on transition metal surfaces with step edges boosted the research interests in synthesizing wafer-scale 2D single crystals on high-index substrate surfaces. Here, using hBN growth on high-index Cu surfaces as an example, a systematic theoretical study to understand the epitaxial growth of 2D materials on various high-index surfaces is performed. It is revealed that hBN orientation on a high-index surface is highly dependent on the alignment of the step edges of the surface as well as the surface roughness. On an ideal high-index surface, well-aligned hBN islands can be easily achieved, whereas curved step edges on a rough surface can lead to the alignment of hBN along with different directions. This study shows that high-index surfaces with a large step density are robust for templating the epitaxial growth of 2D single crystals due to their large tolerance for surface roughness and provides a general guideline for the epitaxial growth of various 2D single crystals.     

Biocompatibility and electron microscopy studies of epitaxial nanolaminate (Al0·5Ti0.5)N/ZrN coatings deposited by Arc-PVD technique

The ability to combine layers with high mechanical strength and additional physicochemical properties, such as biocompatibility, makes the use of multilayer coatings attractive for various applications. The transition from single layer to nanolaminate architecture can improve the mechanical performance of the coatings by increasing the number of interfaces and decreasing the modulation period of the layers. The microstructural study of the nanolaminate (Al_0·5Ti_0.5)N/ZrN coating with a modulation period λ of ≃ 20 nm was carried out using the TEM-HRTEM method. It was found that the coatings of (Al_0·5Ti_0.5)N/ZrN series consisted of two phases: the fcc-(Ti,Al)N solid solution obtained by isomorphic substitution of Ti atoms with Al ones in the TiN crystal lattice and the cubic ZrN phase. ZrN layers had a high texture structure with [111]-preferred growth texture and made a dominant effect on the nucleation and growth of (Al_0·5Ti_0.5)N layers. The epitaxial growth process was the most pronounced for fcc-(Ti,Al)N (111)||fcc-(ZrN) (111) and fcc-(Ti,Al)N (200)||fcc-(ZrN) (200) grains. Finally, the new coating demonstrated high biocompatibility, failure to toxicity and supported U2OS osteogenic cells proliferation within 7 days of cultivation.     

A thermal perspective of flash sintering: The effect of AC current ramp rate on microstructure evolution

In flash sintering experiments, the thermal history of the sample is key to understanding the mechanisms underlying densification rate and final properties. By combining robust temperature measurements with current-ramp-rate control, this study examined the effects of the thermal profile on the flash sintering of yttria-stabilized zirconia, with experiments ranging from a few seconds to several hours. The final density was maximized at slower heating rates, although processes slower than a certain threshold led to grain growth. The amount of grain growth observed was comparable to a similar conventional thermal process. The bulk electrical conductivity correlated with the maximum temperature and cooling rate. The only property that exhibited behavior that could not be attributed to solely the thermal profile was the grain boundary conductivity, which was consistently higher than conventional in flash sintered samples. These results suggest that, during flash sintering, athermal electric field effects are relegated to the grain boundary.     

Nitrogen-doped cobalt sulfide as an efficient electrocatalyst for hydrogen evolution reaction in alkaline and acidic media

The enhancement in intrinsic catalytic activity and material conductivity of an electrocatalyst can leads to promoting HER activity. Herein, a successful nitrogenation of CoS₂ (N–CoS₂) catalyst has been investigated through the facile hydrothermal process followed by N₂ annealing treatment. An optimized N–CoS₂ catalyst reveals an outstanding hydrogen evolution reaction (HER) performance in alkaline as well as acidic electrolyte media, exhibiting an infinitesimal overpotential of ?0.137 and ?0.097 V at a current density of ?10 mA/cm² (?0.309 and ?0.275 V at ?300 mA/cm²), corresponding respectively, with a modest Tafel slope of 117 and 101 mV/dec. Moreover, a static voltage response was observed at low and high current rates (?10 to ?100 mA/cm²) along with an excellent endurance up to 50 h even at ?100 mA/cm². The excellent catalytic HER performance is ascribed to improved electronic conductivity and enhanced electrochemically active sites, which is aroused from the synergy and mutual interaction between heteroatoms that might have varied the surface chemistry of an active catalyst.     

Influence of SiC microstructure on its corrosion behavior in molten FLiNaK salt

The influence of the microstructure on the corrosion rate of three monolithic SiC samples in FLiNaK salt at 900 °C for 250 h was studied. The SiC samples, labeled as SiC-1, SiC-2, and SiC-3, had corrosion rates of 0.137, 0.020, and 0.043 mg/cm²h, respectively. Compared with grain size and the presence of special grain boundaries (i.e., Σ3), the content of high-angle grain boundaries (HAGBs) appeared to have the strongest influence on the corrosion rate of SiC in FLiNaK salt, since the corrosion rate increased six times as the concentration of high-angle grain boundaries increased from 19 to 32% for SiC-2 and SiC-1, respectively. These results stress the importance of controlling the content of HAGBs during the production process of SiC.     

Understanding grain refining and anti Si-poisoning effect in Al-10Si/Al-5Nb-B system

Grain refinement is critical for fabricating high-quality Al-Si casting components in the application of automobile and aerospace industries,while the well-known Si-poisoning effect makes it difficult.Nbbased refiners offer an effective method to refine Al-Si casting alloys,but their anti Si-poisoning capability is far from being understood.In this work,the grain refining mechanism and the anti Si-poisoning effect in the Al-10 Si/Al-5 Nb-B system were systematically investigated by combining transmission electron microscope,first-principles calculations,and thermodynamic calculations.It is revealed that NbB₂provides the main nucleation site in the Al-10 Si ingot inoculated by 0.1 wt.%Nb Al-5 Nb-B refiner.The exposed Nb atoms on the(0001)NbB₂and(1-100)NbB₂surface can be substituted by Al to form(Al,Nb)B₂intermedia layers.In addition,a layer of NbAl₃-like compound(NbAl₃')can cover the surface of NbB₂with the orientation relation of(1-100)[11-20]NbB_2//(110)[110]NbAl₃'.Both of the(Al,Nb)B₂and NbAl₃'intermedia layers contribute to enhancing the nucleation potency of NbB₂particles.These discoveries provide fundamental insight to the grain refining mechanism of the Nb-B based refiners for Al-Si casting alloys and are expected to guide the future development of stronger refiners for Al-Si casting alloys.