Modulation of electrical transport in calcium cobaltite ceramics and thick films through microstructure control and doping

Ca₃Co₄O₉ is a promising p-type thermoelectric oxide material having intrinsically low thermal conductivity. With low cost and opportunities for automatic large scale production, thick film technologies offer considerable potential for a new generation of micro-sized thermoelectric coolers or generators. Here, based on the chemical composition optimized by traditional solid state reaction for bulk samples, we present a viable approach to modulating the electrical transport properties of screen-printed calcium cobaltite thick films through control of the microstructural evolution by optimized heat-treatment. XRD and TEM analysis confirmed the formation of high-quality calcium cobaltite grains. By creating 2.0 at% cobalt deficiency in Ca_2.7Bi_0.3Co₄O_9+δ, the pressureless sintered ceramics reached the highest power factor of 98.0 μWm^?1 K^-2 at 823 K, through enhancement of electrical conductivity by reduction of poorly conducting secondary phases. Subsequently, textured thick films of Ca_2.7Bi_0.3Co_3.92O_9+δ were efficiently tailored by controlling the sintering temperature and holding time. Optimized Ca_2.7Bi_0.3Co_3.92O_9+δ thick films sintered at 1203 K for 8 h exhibited the maximum power factor of 55.5 μWm^?1 K^-2 at 673 K through microstructure control.     

Diluted chemical bath deposition of CdZnS as prospective buffer layer in CIGS solar cell

In this study, dilute chemical bath deposition technique has been used to deposit CdZnS thin films on soda-lime glass substrates. The structural, morphological, optoelectronic properties of as-grown films have been investigated as a function of different Zn²⁺ precursor concentrations. The X-ray diffractogram of CdS thin-film reveals a peak corresponding to (002) plane with wurtzite structure, and the peak shift has been observed with the increase of the Zn²⁺ concentration upon formation of CdZnS thin film. From morphological studies, it has been revealed that the diluted chemical bath deposition technique provides homogeneous distribution of film on the substrate even at a lower concentration of Zn²⁺. Optical characterization has shown that the transparency of the film is influenced by Zn²⁺ concentration and when the Zn²⁺ concentration is varied from 0 M to 0.0256 M, bandgap values of resulting films range from 2.42 eV to 3.90 eV while. Furthermore, electrical properties have shown that with increasing zinc concentration the resistivity of the film increases. Finally, numerical simulation validates and suggests that CdZnS buffer layer with composition of 0.0032 M Zn²⁺ concentration would be a promising candidate in CIGS solar cell.     

Large domain-wall currents in epitaxial Au/BiFeO3/SrRuO3 thin-film capacitors with modulated oxygen vacancy and wall densities

Large domain wall (DW) conductivity in an insulating ferroelectric plays an important role in the future nanosensors and nonvolatile memories. However, the wall current was usually too small to drive high-speed memory circuits and other agile nanodevices requiring high output-powers. Here, a large domain-wall current of 67.8 μA in a high on/off ratio of ~4460 was observed in an epitaxial Au/BiFeO₃/SrRuO₃ thin-film capacitor with the minimized oxygen vacancy concentration. The studies from read current-write voltage hysteresis loops and piezo-response force microscope images consistently showed remaining of partially unswitched domains after application of an opposite poling voltage that increased domain wall density and wall current greatly. A theoretical model was proposed to explain the large wall current. According to this model, the domain reversal occurs with the appearance of head-to-head and tail-to-tail 180° domain walls (DWs), resulting in the formation of highly conductive wall paths. As the applied voltage increased, the domain-wall number increased to enhance the on-state current, in agreement with the measurements of current-voltage curves. This work paves a way to modulate DW currents within epitaxial Au/BiFeO₃/SrRuO₃ thin-film capacitors through the optimization of both oxygen vacancy and domain wall densities to achieve large output powers of modern domain-wall nanodevices.     

Photophysical investigation of the formation of defect levels in P doped ZnO thin films

Zinc oxide (ZnO) offers a major disadvantage of asymmetry doping in terms of reliability, stability, and reproducibility of p-type doping, which is the main hindrance in realization of optoelectronic devices. The problem is even more complicated due to formation of various native defects in unintentionally doped n-type ZnO. The realization of p-type conductivity in doped ZnO requires an in-depth understanding of the formation of an effective shallow acceptor, as well as donor-acceptor compensation. Photophysical properties such as photoconductivity along with photoluminescence (PL) studies have unprecedentedly and effectively been utilized in this work to monitor the evolution of various in-gap defects. Phosphorus (P) doped ZnO thin films have been grown by RF magnetron sputtering under various Ar to O₂ gas ratios to investigate the effect of O₂ on the donor-acceptor compensation by comprehensive photoconductivity measurements supported by the PL studies. Initial elemental analyses indicate presence of abundant zinc vacancies (V_Zn) in O-rich ambience. The results predict that P sits in the zinc (Zn) site rather than the oxygen (O) site causing the formation of P_Zn–2V_Zn acceptor-like defects, which compensates the donor defects in P doped ZnO films. Photocurrent spectra uniquely reveal presence of more oxygen vacancies (V_O) defects states in lower O₂ flow, which gets compensated with an increase in the O₂ flow. Successive photocurrent transients indicate probable presence of more V_O in the films grown with lower O₂ flow and more V_Zn in higher O₂ flow. Overall the photosensitivity measurements clearly present that O-rich ambience expedites the formation of acceptor defects which are compensated, thereby lowering the dark current and enhancing the ultraviolet photosensitivity.     

基准平面垂直断面法在爆破漏斗试验中的应用

系统阐述了基准平面垂直断面法在爆破漏斗试验中测量爆破漏斗体积的基本原理,并将隧道激光断面仪应用于金厂河矿1 750 m水平15^#采场底部切割巷道爆破漏斗试验爆破漏斗体积测量中。通过与传统体重法等计算法所得漏斗体积分析比较,结果表明基于隧道激光断面仪与3D Mine软件分析的基准平面垂直断面法实用性强、操作方便、结果直观可靠,达到试验预期目的。     

毫米波三维异质异构集成技术的进展与应用

三维异质异构集成技术是实现电子信息系统向着微型化、高效能、高整合、低功耗及低成本方向发展的最重要方法,也是决定信息化平台中微电子和微纳系统领域未来发展的一项核心高技术。文章详细介绍了毫米波频段三维异质异构集成技术的优势、近年来的发展趋势以及面临的挑战。利用硅基MEMS 光敏复合薄膜多层布线工艺可实现异质芯片的低损耗互连,同时三维集成高性能封装滤波器、高辐射效率封装天线等无源元件,还能很好地处理布线间的电磁兼容和芯片间的屏蔽问题。最后介绍了一款新型毫米波三维异质异构集成雷达及其在远距离生命体征探测方面的应用。     

水压爆破拆除超大容积水池

简要介绍了组合式超大容积（８５０ｍ３）水池在水压爆破拆除过程中爆破方案选择、参数选取等方面的经验，并对爆破效果进行了分析，为同类工程施工提供了可借鉴的经验。     

Spray pressure variation effect on the properties of CdS thin films for photodetector applications

Herein, we report the photosensing property of CdS thin films. CdS thin films were coated onto glass substrates via a spray pyrolysis method using different spray pressures. Prepared films were characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), and optical and photoluminescence spectroscopy. XRD analysis demonstrated the growth of crystalline CdS films with crystallite sizes varying from 26 to 29 nm depending on the pressure. The SEM and EDAX analyses revealed nearly-stoichiometric CdS films with smooth surfaces and slight variation in grain morphology due to pressure changes. Optical measurements showed a direct bandgap varying from 2.37 eV to 2.42 eV due to pressure changes. A photodetector was also fabricated using the grown CdS films; the fabricated photodetector exhibited good performance depending on the spray pressure. A spray pressure of 1.5 GPa resulted in high photoresponsivity and external quantum efficiency.     

Sputtered Ir–Ru based catalysts for oxygen evolution reaction: Study of iridium effect on stability

Magnetron sputtered low-loading iridium-ruthenium thin films are investigated as catalysts for the Oxygen Evolution Reaction at the anode of the Proton Exchange Membrane Water Electrolyzer. Electrochemical performance of 50 nm thin catalysts (Ir pure, Ir–Ru 1:1, Ir–Ru 1:3, Ru pure) is tested in a Rotating Disk Electrode. Corresponding Tafel slopes are measured before and after the CV-based procedure to compare the activity and stability of prepared compounds. Calculated activities prior to the procedure confirm higher activity of ruthenium-containing catalysts (Ru pure > Ir–Ru 1:3 > Ir–Ru 1:1 > Ir pure). However, after the procedure a higher activity and less degradation of Ir–Ru 1:3 is observed, compared to Ir–Ru 1:1, i.e. the sample with a higher amount of unstable ruthenium performs better. This contradicts the expected behavior of the catalyst. The comprehensive chemical and structural analysis unravels that the stability of Ir–Ru 1:3 sample is connected to RuO₂ chemical state and hcp structure. Obtained results are confirmed by measuring current densities in a single cell.     

Mixing enhancement mechanism of combined H2–Water jets in supersonic crossflows in a combustor with an expanded section

To obtain the mixing enhancement mechanism of H₂–Water combined jets in supersonic crossflows in a combustor with expanded section for rotating detonation ramjet, the flow field shape and spray structure were studied by experimental and numerical methods. The Eulerian–Lagrangian method was used to investigate the diffusion mechanism and H₂–Water interaction law of combined jets with different sequences. At the same time, high-speed photography and the schlieren technique were used to capture the flow field. The effects of jet pressure drop, orifice diameter, orifice spacing, incoming Mach number, and other parameters on the penetration depth of water jets were studied. The results of experiment and simulation show that using H₂–Water combined jets, the penetration depth of the jet spray can be greatly increased and the jet mixing effect can be significantly improved, which will contribute to the engine's ignition and stable combustion. In the case of pre-water/post-H₂, the penetration depth of the hydrogen jet is greater. In the case of pre-H₂/post-water, the hydrogen jet raises the water spray mainly by protecting the integrity of the water column.