Influence of iron oxide pigments on the properties of concrete interlocking blocks

Concrete interlocking blocks (CIBs) are utilized in a variety of commercial, municipal, and industrial applications. Superior engineering properties, low maintenance, ease of placement and removal, reuse of original blocks, aesthetic appeal, and immediate availability are the primary reasons for choosing concrete block pavement over other paving surfaces. It is a common practice to pigment building materials, such as mortar, concrete pavers, concrete roof tiles, and prefabricated concrete products; CIBs are colored using iron oxide pigments. This article presents experimental results detailing the properties of CIBs dyed with pigments. The results of these experiments are as follows: Because the particles of iron oxide pigments are finer than those of brown iron oxide, interlocking blocks mixed with the former acquired higher color strength than with the latter. Additional analysis determined a definite relationship between the flexural strength and the absorption ratio of pigment-dyed blocks; the correlation coefficient (R²) of interlocking blocks at 91 days was .90. It is suggested that if iron oxide pigments are to be used to color CIBs, the pigment-to-cement ratio should be below 4%.     

Scale Up from Small Oven-Drying Tests of Mineral Concentrate to Pilot-Scale Drying with a Heated Pad

While Fickian diffusion models are commonly used in other applications, there are few reports of them being applied to the batch drying of a mineral concentrate. Diffusion coefficients estimated from small-scale oven-drying tests were used to predict the drying behavior of a concentrate sample 1 m × 1 m in area and 50 cm deep, with a heated bottom pad. These pilot-scale tests included both daily turning of the sample and turning every three days. The excellent quantitative agreement between the predicted and observed pilot-scale behavior gives a high level of confidence in the model predictions and suggests that a Fickian diffusion model is adequate to predict the behavior of mineral concentrates at the low moisture contents used here.     

用硫酸铁铵容量法测定钛精矿中二氧化钛含量

样品在过氧化钠熔融、水浸取及盐酸酸化后，在盐酸和硫酸介质中，隔绝空气，用金属铝将钛(Ⅳ)还原至钛(Ⅲ)，以硫氰酸盐为指示剂，用硫酸铁铵标准溶液滴定。     

Physico-chemical properties of ceramic pigments for high-temperature application

Heat resistant coatings are required primarily for stacks, exhaust pipes, reactors, space crafts and similar equipments that are permanently or occasionally exposed to elevated temperatures. High-temperature coatings are generally based on silicone resin with ceramic and metallic pigments. In this study, iron oxide, cobalt oxide (thermo chromic compound) and aluminum oxide are used for the preparation of four new types of coloured pigments. The thermal resistant characteristics of these ceramic pigments were studied by differential thermal analysis, thermo gravimetric analysis and differential scanning calorimetric analysis. These ceramic pigments are found to be thermally stable up to 400 °C.     

A simple mathematical analysis on the effect of sand in Cr(VI) reduction using zero valent iron

A simple mathematical model was proposed to analyze the enhancement of Cr(VI) reduction when sand materials are added to the zero valent iron (ZVI). Natural decay of Cr(VI) in a control experiment was analyzed by using a zero-order decay reaction. Adsorption kinetics of Cr(VI) to sand was modeled as a first-order reversible process, and the reduction rate by ZVI was treated as a first-order reaction. Natural decay of Cr(VI) was also included in other experiments, i.e., the adsorption to sand, the reduction by ZVI, and both adsorption and reduction when sand and ZVI are present together. The model parameters were estimated by fitting the solution of each model to the corresponding experimental data. To observe the effect of sand addition to ZVI, both adsorption and reduction rate models were considered simultaneously including the natural decay. The solution of the combined model was fitted to the experimental data to determine the first-order adsorption and reduction rate constants when sand as well as ZVI is present. The first-order reduction rate constant in the presence of sand was about 35 times higher than that with ZVI only.     

Preparation of one-dimensional polymer films by modification of a hydroxymethylbenzene self-assembled monolayer on iron with alkyltriethoxysilanes for preventing iron corrosion

A self-assembled monolayer (SAM) of p-hydroxymethylbenzene HOCH₂C₆H₄ - (HOMB) moiety adsorbed on iron by the formation of a covalent bond between carbon and iron atoms was prepared by electrochemical derivatization of an iron electrode with p-hydroxymethylbenzenediazonium tetrafluoroborate HOCH₂C₆H₄N₂BF₄. The electrode covered with the HOMB SAM was modified with alkyltriethoxysilanes C_nH_2n+1Si(OC₂H₅)₃ (C_nTES, n = 8 or 18) to prepare a film of one-dimensional polymer. The protective ability of the polymer film was determined by polarization measurement of the covered electrode in an aerated 0.5 M NaCl solution. The ability was enhanced by modification of the HOMB SAM with C_nTES markedly. The iron surface coated with the one-dimensional polymer film of the HOMB SAM modified with C₈TES was characterized by contact angle measurement and FTIR reflection and X-ray photoelectron spectroscopies. The persistence in the protective ability of the polymer film against iron corrosion in 0.5 M NaCl may be associated with the strong adsorption via the covalent bond, revealed by electron-probe microanalysis.     

钛精矿回转窑直接还原过程结圈可能性的探讨

通过煤种，入窑球冷态强度和还原过程强度，以及钛精矿与煤灰混合物的软化温度等分析探讨了钛精矿预热球团回转窑直接还原产生结圈的可能性，获得了可以避免结圈的结论。     

影响铁精矿K2O、Na2O、SiO2含量的因素分析

用统计分析方法 ,分析了影响精矿K2 O、Na2 O、SiO2 含量的因素 ,并根据分析结论提出了对生产工艺进行定向控制的条件     

Growth of Fe on Si (100) at room temperature and formation of iron silicide

Low-energy electron diffraction (LEED), Auger electron spectroscopy and X-ray photoelectron spectroscopy (XPS) investigations of both the growth of an iron film on silicon (100) at room temperature and the subsequent formation of iron silicide are the subjects of this paper. An in-situ cleaned silicon (100) wafer without carbon or oxygen contamination exhibiting the known 2 × 1 reconstruction in the LEED pattern served as the substrate. Iron was deposited on this reconstructed surface at 300 K. The comparison of theoretical calculations based on three growth mechanisms with XPS data obtained with take-off angles of 0° and 50° clearly demonstrates a layer-by-layer growth of the iron film on silicon (100). At 300 K no formation of iron silicide was observed, although an interaction between iron and silicon could be detected at the interface. The formation of iron silicide was observed at annealing temperatures of 630–730 K. Quantitative XPS analysis yields the presence of FeSi₂, when the thickness is large enough. Neither the iron film on silicon nor the silicide shows any LEED pattern.     

Corrosion protection of iron by polypyrrole coatings electrosynthesised from a surfactant solution

This work is a study of the electropolymerisation of pyrrole onto iron electrodes in the presence of sodium bis(2-ethylhexyl) sulfosuccinate in a wide pH interval. The characterisation of the films was done using electrochemical techniques, SEM/EDX and IR spectroscopy. We show that it is possible to synthesise homogeneous, adherent and very compact films in the pH range between 7 and 12 under potentiodynamic, galvanostatic and potentiostatic conditions without substrate dissolution. The effects of various parameters on electrodeposition were investigated. The new procedure for the electrochemical synthesis of polypyrrole results in improved anticorrosion properties. The inhibition is proposed to be due to the sum of a repulsion of chloride ions because AOT remains entrapped in the polymer matrix and the presence of the iron oxide. Advantages of the use of surfactants in the electropolymerisation solution are discussed.