Microstructure,mechanical, tribological,and oxidizing properties of AlCrSiN/AlCrVN/AlCrNbN multilayer coatings with different modulated thicknesses

Multilayer structure design is one of the most promising methods for improving the comprehensive performance of AlCrN-based hard coatings applied to cutting tools. In this study, four types of AlCrSiN/AlCrVN/AlCrNbN multilayer coatings, with different modulated thicknesses, were deposited to investigate their microstructure, mechanical, tribological, and oxidizing properties. All multilayer coatings exhibited grain growth along the crystallographic plane of (200) with a NaCl-type face-centered cubic (FCC) structure. The results show that, as the modulation thickness decreases from ～35 nm to ～10 nm, (1) the grain refinement effect is increasingly evident; (2) all multilayer coatings show a hardness of >30 GPa and an elastic modulus of >300 GPa. Both the ability to resist elastic strain to failure and the plastic deformation of multilayer coatings increase. In addition, their resistance to cracking reduces; (3) the wear rates of these multilayer coatings reduce successively from 1.78 × 10^?16 m³ N^?1 m^?1 to 7.7 × 10^?17 m³ N^?1 m^?1. This is attributed to an increase in self-lubricating VO_x and a decrease in adhesives from the counterparts; (4) the best high-temperature oxidation resistance was obtained for the multilayer coating with a modulated thickness of ～15 nm.     

The formed surface characteristics of SiCf/SiC composite in the nanosecond pulsed laser ablation

For the advantages of high-temperature resistance, corrosion resistance and ultra-high hardness, SiC_f/SiC composite is becoming a preferred material for manufacturing aero-engine parts. However, the anisotropy and heterogeneity bring great challenges to the processing technology. In this study, a nanosecond pulsed laser is applied to process SiC_f/SiC composite, where the influence of the scanning speed and laser scanning direction to the SiC fibers on the morphology of ablated grooves is investigated. The surface characteristics after ablation and the involved chemical reaction of SiC_f/SiC are explored. The results show that the increased laser scanning speed, accompanied by the decreasing spot overlap rate, leads to the less accumulation of energy on the material surface, so the ablation effect drops. In addition, for the anisotropy of the SiC_f/SiC material, the obtained surface characteristics are closely dependent on the laser scanning direction to the SiC fibers, resulting in different groove morphology. The element composition and phase analysis of the machined surface indicate that the main deposited product is SiO₂ and the carbon substance. The results can provide preliminary technical support for controlling the machining quality of ceramic matrix composites.     

High-temperature oxidation behavior of monolithic Zr3[Al(Si)]4C6 and its composite incorporating 30vol% ZrB2-SiC: Providing a basis for broadening the service temperature

To provide a basis for the high-temperature oxidation of ultra-high temperature ceramics (UHTCs), the oxidation behavior of Zr₃[Al(Si)]₄C₆ and a novel Zr₃[Al(Si)]₄C₆-ZrB₂-SiC composite at 1500 °C were investigated for the first time. From the calculation results, the oxidation kinetics of the two specimens follow the oxidation dynamic parabolic law. Zr₃[Al(Si)]₄C₆ exhibited a thinner oxide scale and lower oxidation rate than those of the composite under the same conditions. The oxide scale of Zr₃[Al(Si)]₄C₆ exhibited a two-layer structure, while that of the composite exhibited a three-layer structure. Owing to the volatilization of B₂O₃ and the active oxidation of SiC, a porous oxide layer formed in the oxide scale of the composite, resulting in the degradation of its oxidation performance. Furthermore, the cracks and defects in the oxide scale of the composite indicate that the reliability of the oxide scale was poor. The results support the service temperature of the obtained ceramics.     

Effect of microwave heating time on the gel properties of chicken myofibrillar proteins and their formation mechanism

The present work was conducted to illustrate the mechanism of gel formation of myofibrillar proteins (MPs) under different microwave heating times. The results showed that the denaturation enthalpy (ΔH) of the MPs significantly decreased when the heating time increased from 3 to 9 s and then completely disappeared as the heating time progressed, indicating that the MPs gradually denatured and subsequently aggregated with increasing heating time, which was further verified by the changes in the secondary structure, electrophoretic bands, and gel properties (e.g., water holding capacity and textural profiles) of the MPs. Microstructural images indicated that the MP gel formed under 12 s had the most compact network, indicating that extended microwave heating time could induce quality deterioration of MP gels. Moreover, the hydrophobic forces, electrostatic forces, and disulphide bonds of the MPs gradually intensified with increasing microwave heating time, suggesting that both non-covalent and covalent bonds could promote molecular denaturation and subsequent aggregation of MPs. In addition, correlation analysis revealed that the changes in the molecular conformation of MPs induced by different microwave heating times could effectively regulate the formation of MP gels and their related properties.     

Development and characterisation of a Y2Ti2O7-based glass-ceramic as a potential oxidation protective coating for titanium suboxide (TiOx)

A silica-based glass-ceramic, with Y₂Ti₂O₇ as the major crystalline phase, is designed, characterised and tested as an oxidation-protective coating for a titanium suboxide (TiO_x) thermoelectric material at temperatures of up to 600 °C. The optimised sinter-crystallisation treatment temperatures are found to be 1300 °C and 855 °C for a duration of 30 min, and this treatment leads to a glass-ceramic with cubic Y₂Ti₂O₇ and CaAl₂Si₂O₈ as crystalline phases. An increase of ~270 °C in the dilatometric softening temperature is observed after devitrification of the parent glass, thus further extending its working temperature range.Excellent adhesion of the glass-ceramic coating to the thermoelectric material is maintained after exposure to a temperature of 600 °C for 120 h under oxidising conditions, thus confirming the effectiveness of the T1 glass-ceramic in protecting the TiO_x material.     

Sputtered Fe1·5CoNi0.5 coating: An improved protective coating for SOFC interconnect applications

In an attempt to optimize the properties of FeCoNi coating for planar solid oxide fuel cell (SOFC) interconnect application, the coating composition is modified by increasing the ratio of Fe/Ni. An Fe_1·5CoNi_0.5 (Fe:Co:Ni = 1.5:1:0.5, atomic ratio) metallic coating is fabricated on SUS 430 stainless steel by magnetron sputtering, followed by oxidation in air at 800°C. The Fe_1·5CoNi_0.5 coating is thermally converted to (Fe,Co,Ni)₃O₄ and (Fe,Co,Mn,Ni)₃O₄ without (Ni,Co)O particles. After oxidation for 1680 h, no further migration of Cr is detected in the thermally converted coating region. A low oxidation rate of 5.9 × 10^?14 g² cm^?4 s^?1 and area specific resistance of 12.64 mΩ·cm² is obtained for Fe_1·5CoNi_0.5 coated steels.     

Synthesis and Characterization of Co Nanocomposite Based on Poly(benzimidazole-amide) Matrix and Their Behavior as Catalyst in Oxidation Reaction

2,6-Bis(5-amino-1H-benzimidazol-2-yl)pyridine was prepared and characterized by Fourier transform infrared spectroscopy, elemental analysis, ¹H-NMR, and ¹³C-NMR spectroscopic methods. Then a new poly(benzimidazole-amide) was synthesized by polymerization of the corresponding diamine and isophthalic acid. The obtained poly(benzimidazole-amide) exhibited good yield and high thermal stability. Due to the existence of benzimidazole moieties in polymer’s structure, it has the tendency to form complexes with metal ions. So, a new poly(benzimidazole-amide)/Co nanocomposite was prepared. Morphological studies revealed that metal nanoparticles were dispersed in the polymer matrix without any aggregation. poly(benzimidazole-amide)/Co nanocomposite was used as a catalyst in the oxidation of ethyl benzene to acetophenone with tert-butyl hydroperoxide.     

The improvement of the self-healing ability of MoSi2 coatings at 900–1200 °C by introducing SiB6

The brittleness of MoSi₂ ceramic and the thermal mismatch between MoSi₂ coating and C / C composite lead to brittle cracking of the coating at 900−1200 °C. This problem has been overcome in this studyby introducing submicron-SiB₆ into the coating. The pre-fabricated cracks and a kinetics model of hot-pressed SiB₆-MoSi₂ ceramic could quantitatively predict the glass growth and crack healing. As expected, enhancing temperature and SiB₆ content increased the growth rate of the borosilicate glass and the crack healing ability of MoSi₂ ceramic, which was ascribed to the lower oxidation activation energy and larger specific surface area of submicron-SiB₆. For the plasma sprayed coating, SiB₆ with submicron structure was benefit for cracking inhibition and formation of borosilicate glass during oxidation, reducing the oxygen permeability and the consumption of inner coating. Hence, the 15 % SiB₆-MoSi₂ coatings raised the protection times to 84 and 120 h at 900 and 1200 °C respectively, presenting favorable oxidation protective performance.     

A methodology for the estimation of transverse failure strength of an oxidized lamina from isothermal aging studies

Surface oxidation and ensuing damage substantially decrease the service life of High Temperature Polymer Matrix Composite (HTPMC) structures. Oxidative degradation behavior of composites is strongly dependent on the coupling between chemical and mechanical responses of the material. In a composite lamina, the onset of damage and subsequent coupled acceleration of both damage and oxidation are controlled by the transverse failure strength of the oxidized regions. The direct measurement of this strength from experimentation is challenging and cumbersome. A model-based methodology for estimating the mean transverse failure strength of the oxidized regions of a unidirectional composite is described in this paper. As the strength of the oxidized region is expected to show a high-degree of spatial variability, the estimated mean is shown to be relatively insensitive to the effect of strength variance. The developed methodology is illustrated with isothermal aging data available for a typical high-temperature composite system.     

Research on the effects of surface modification of ceramic powder on cure performance during digital light processing (DLP)

Digital light processing (DLP) is one of the most important additive manufacture technologies to fabricate ceramic parts with complex geometries. Compared with pure photosensitive resin, the cure performance of ceramic suspensions is obviously different due to the optical property change after the addition of ceramic powders. In this paper, a unique oxidation process was used to modify the optical properties of nitride powders including AlN and Si₃N₄. The properties of oxidized ceramics were investigated and the cure performance of ceramic suspensions was then characterized. The effect of oxidation time on cure performance was evaluated. The results showed that for AlN, oxidation process leads to the smaller cure depth and smaller excess cure width as compared with non-oxidized AlN and for Si₃N₄, oxidation process leads to the larger cure depth and larger excess cure width as compared with non-oxidized Si₃N₄, indicating that both refractive index and light absorbance of ceramic powders have obvious effects on cure behaviors. Additionally, the cure behavior of oxidized ceramic suspension in this study shows that the relationship of cure depth vs. incident energy agrees well with Beer- Lambert model, but the excess cure width vs. incident energy is not consistent with quasi Beer-Lambert model due to the nature of digital micromirror device (DMD).