高精度冷轧带钢的开发前景

通过对高精度冷轧带钢的市场调研和重点项目分析，提出对该产品开发工作的建议。     

铜元素和退火温度对TRIP冷轧钢板组织和力学性能的影响

将含铜和不含铜的两种TRIP钢板(0．2％C、1．5％Si、1．5％Mn)冷轧至1mm厚，然后分别在750℃、760℃、770℃、780℃下退火5min，最后在450℃等温3min，获得了不同含量和不同稳定性的残留奥氏体。金相和力学性能试验结果表明，铜元素能提高残留奥氏体量和钢板的力学性能；退火温度影响残留奥氏体量和力学性能，当退火温度选择在Ac1 10％时可获得最佳的力学性能。     

人工智能在冷轧带肋钢筋工艺参数优化中的应用

论述了人工智能在冷轧带肋钢筋工艺参数优化中的应用,首先利用神经网络建立起冷轧带肋钢筋工艺参数与产品抗拉强度之间关系的数学模型,然后用遗传算法对工艺参数优化。按优化后的工艺参数在某拉丝加工厂进行了大批量生产试验,产品的合格率达到98%以上,从而为控制冷轧带肋钢筋工艺参数提供了一条行之有效的途径。     

断后伸长率A测量结果的不确定度评定

文章按照GB/T 228-2002《金属材料室温拉伸试验方法》标准的要求,对冷轧奥氏体不锈钢板的断后伸长率进行了测试,并对检测结果的不确定度进行了评定。当k=2时,置信概率p=95%,断后伸长率不确定度评定结果为A=62.5%±2.0%。     

Effect of silicon content and annealing temperature on formation of retained austenite and mechanical properties in multi-phase steels

Cold-rolled and annealed ultra-high strength sheet steels with good ductility accompanied by TRIP of retained austenite have received considerable attention in recent years. This paper discusses the effect of silicon content and annealing temperature on the formation of retained austenite and the mechanical properties in Fe-0.34%C-1.7% Mn steels whose structure consists of ferrite, bainite and retained austenite. Silicon inhibited the cementite formation in bainite during isothermal holding and partitioned carbon from bainite to austenite, resulting in an increase in retained austenite content. When the silicon content was increased to 1.0 wt.% or higher, the amount of retained austenite markedly increased leading to good mechanical properties. 0.34%C-1.03%Si-1.7%Mn steel showed a high tensile strength of 1,030 MPa and a total elongation of 34.5% when annealed at 780°C for 5 min followed by isothermal holding at 400°C for 5 min. In this case, the amount of retained austenite was about 25%. The variation in tensile strength-elongation combination had good correlation with that in the amount of retained austenite with both annealing temperature and silicon content. The most retained austenite was obtained in the steel annealed at just above A_C1 temperature. The annealing temperature which gives the most retained austenite was decreased with decreasing the silicon content.     

冷轧扭钢筋在工程中的应用

本文主要介绍了冷轧扭钢筋的原理、特点、制作、材料成品检验及其有关规定。     

平整机张力控制系统的改造

结合广州金莱冷轧带钢有限公司的生产实际，对平整机张力控制系统进行改造．着重介绍了改造后的平整机张力控制系统的构成及设计考虑．改造后工艺流程合理，带钢表面质量大大提高．     

《油汀用冷轧钢带》行业标准解读

简要介绍了《油汀用冷轧钢带》行业标准的制定原则，同时对相关技术内容确定依据进行了说明。     

加热速度对冷轧双相钢组织性能的影响

通过模拟连续退火研究了不同加热速度对冷轧双相钢组织性能的影响。研究发现,快速加热可以明显地细化晶粒,但组织的遗传性导致微观组织中有不同程度的带状组织,材料的加热速度不宜超过100℃/s;材料的加工硬化速率及加工硬化指数对冷速的增加呈规律变化。     

水基乳化液润滑冷轧1100铝板表面腐蚀分析

生产现场发现水基乳化液润滑冷轧铝及铝合金板,沿着轧制方向板材边缘的上、下表面几乎对应地出现明显的白色腐蚀条纹.试验以冷轧1100纯铝板为研究对象,采用SEM,XPS等测试分析手段对其表面腐蚀成分及腐蚀机理进行研究.试验研究结果表明,铝材腐蚀面的成分是A100H.