Electromagnetism-like algorithms for optimized tool path planning in 5-axis flank machining

Optimization of tool path planning using metaheuristic algorithms such as ant colony systems (ACS) and particle swarm optimization (PSO) provides a feasible approach to reduce geometrical machining errors in 5-axis flank machining of ruled surfaces. The optimal solutions of these algorithms exhibit an unsatisfactory quality in a high-dimensional search space. In this study, various algorithms derived from the electromagnetism-like mechanism (EM) were applied. The test results of representative surfaces showed that all EM-based methods yield more effective optimal solutions than does PSO, despite a longer search time. A new EM-MSS (electromagnetism-like mechanism with move solution screening) algorithm produces the most favorable results by ensuring the continuous improvement of new searches. Incorporating an SPSA (simultaneous perturbation stochastic approximation) technique further improves the search results with effective initial solutions. This work enhances the practical values of tool path planning by providing a satisfactory machining quality.     

Low cycle fatigue behavior of a eutectic 80Au/20Sn solder alloy

The eutectic 80Au/20Sn solder alloy is widely used in high power electronics and optoelectronics packaging. In this study, low cycle fatigue behavior of a eutectic 80Au/20Sn solder alloy is reported. The 80Au/20Sn solder shows a quasi-static fracture characteristic at high strain rates, and then gradually transforms from a transgranular fracture (dominated by fatigue damage) to intergranular fracture (dominated by creep damage) at low strain rates with increasing temperature. Coffin-Manson and Morrow models are proposed to evaluate the low cycle fatigue behavior of the 80Au/20Sn solder. Besides, the 80Au/20Sn solder has enhanced fatigue resistance compared to the 63Sn/37Pb solder.     

基于注意力机制与文本信息的用户关系抽取

随着社交媒体的发展,用户之间的关系网络对于社交媒体的分析有很大的帮助。因此,该文主要研究用户好友关系检测。以往的关于用户好友关系抽取的研究主要基于社交媒体上的结构化信息,比如其他好友关系,用户的不同属性等。但是,很多时候用户本身并没有大量的好友信息存在,同时也不一定有很多确定的属性。因此,我们希望基于用户发表的文本信息来对用户关系进行预测。不同于以往的潜在好友推荐算法,该文提出了一种基于注意力机制以及长短时记忆网络(long short-term memory,LSTM)的好友关系预测模型,将好友之间的评论分开处理,通过分析用户之间的评论来判断是否具备一定的好友关系。该模型将好友双方信息拼接后的结果作为输入,并将注意力机制应用于LSTM的输出。实验表明,用户之间的评论对于好友关系预测确实有较大的实际意义,该文提出的模型较之于多个基准系统的效果,取得了明显的提升。在不加入任何其它非文本特征的情况下,实验结果的准确率达到了77%。     

Verhalten von Magnesiumlegierungen für Anwendungen im Fahrzeugbau bei mechanisch‐elektrochemischer Komplexbeanspruchung: Einfluss passivierender Deckschichten und Mechanismen der lokalen Schädigung

Behavior of Magnesium‐Alloys for Automotive Applications under Mechanical and Environmental Loading: Influence of Passivating Films and Mechanisms of Local Breakdown To assure an efficient design of components under cyclic loading, all available data concerning fatigue have to be observed. Therefore the influences of manufacturing on the material condition, the mechanical loads and environmental effects have to be analysed. Magnesium‐alloys are of special interest for lightweight applications because of their excellent strength‐density ratio. The corrosion resistance of magnesium‐alloys depends on the same factors that are critical to other metals. The alloys have a good stability to atmospheric exposure and a good resistance to attack by alkali, chromic and hydrofluoric acids. However, because of the electrochemical activity of magnesium, the relative importance of some factors is greatly amplified. The nature and composition of passive films formed on magnesium‐alloys depend on the prevailing conditions, viz. alloy‐composition, passivation potential, pH, electrolyte composition and temperature. Passive films may be damaged by local breakdown. Because of this, magnesium‐alloys suffer a degradation of their properties when exposed to an aqueous environment. The main topic of the present investigations is the verification of mechanisms of the local breakdown of the protecting film. At least two mechanisms are possible for this localization: mechanical breakdown by slip steps and electrochemical breakdown (for e.g. by the effects of chloride ions). Corrosion and passivation of different high purity alloys have been studied in different solutions (neutral, alkaline with specific anions and cations) using electrochemical techniques. The diecasted alloys were tested as produced and machined. The results clarified that depending on alloy/material and surface condition/corrosion environment different mechanisms for electrochemical breakdown of the protecting films are possible. Hence fatigue life under environmental loading is influenced by surface and testing conditions.     

新一代IP QoS的实现

文章介绍了新一代IP骨干网上的IP QoS实现技术，论述了集成业务(IntServ)与差分业务(DiffServ)解决方案的特点，详细介绍了相关的队列管理与排队机制。并结合多协议标签交换（MPLS)技术的最新发展，阐述了综合多协议标签交换流量工程与DiffServ技术体系端到端IP QoS的实现。     

6种金属材料在典型工业大气中的腐蚀规律

选取具有代表性的碳钢、不锈钢、镀锌碳钢、铝、钛和铜挂片,在某企业不同部位投放后进行为期半年的大气腐蚀试验,得出了在半年期中的腐蚀规律。在此基础上,对每种金属材料的腐蚀特点进行总结,并对大气腐蚀的各种影响因素进行分析,提出了行之有效的防护措施。     

含硫化氢气井钻井过程中的腐蚀因素与防护研究

在含硫气井的钻井过程中对于HRC大于22的钻具钢材除了腐蚀疲劳之外，在pH值小于9的环境中会发生硫化物应力腐蚀破裂，这种破坏比腐蚀疲劳更突然、更快，使钻杆大量损坏。含硫气井在钻井过程中，由于湿硫化氢的出现，常常会出现油管、套管、钻井设备、钻井仪器以及对支持保护管柱的水泥环柱等腐蚀和损坏问题，为此，阐述了湿硫化氢的腐蚀特点、机理，归纳总结了影响腐蚀的因素，综述了如何在这些方面防止其腐蚀，使损失减小，为指导油管、套管防腐工程实践提供了依据。建议在钻井过程中采用碱性钻井液，其pH值可到9或更高(至pH值12)，以减缓或防止钻井过程中电化学从硫化物应力腐蚀破裂；含硫气井用的钻杆应该间歇使用。钻杆停用堆置时间可使其放氢，使钻杆恢复韧性，防止硫化物应力腐蚀断裂。     

Fast Positive Feedback Between the Adrenocortical Stress Response and a Brain Mechanism Involved in Aggressive Behavior.

Aggressive behavior induces an adrenocortical stress response, and sudden stressors often precipitate violent behavior. Experiments in rats revealed a fast, mutual, positive feedback between the adrenocortical stress response and a brain mechanism controlling aggression. Stimulation of the aggressive area in the hypothalamus rapidly activated the adrenocortical response, even in the absence of an opponent and fighting. Hypothalamic aggression, in turn, was rapidly facilitated by a corticosterone injection in rats in which the natural adrenocortical stress response was prevented by adrenalectomy. The rapidity of both effects points to a fast, mutual, positive feedback of the controlling mechanisms within the time frame of a single conflict. Such a mutual facilitation may contribute to the precipitation and escalation of violent behavior under stressful conditions. (PsycINFO Database Record (c) 2010 APA, all rights reserved)     

径向水平井弯曲转向机构影响因素仿真研究

针对径向水平井钻进中钻杆弯曲转向前进运动困难的问题,通过建立弯曲转向机构仿真有限元模型,对其主要影响因素:滑道轨迹曲率、间隙、工作压力、滚轮形状与位置和钻杆壁厚等用ANSYS软件进行仿真研究。研究表明:影响截面变形的主要因素是滑道曲率的改变和滑道摩擦因数,钻井失败时钻杆所受阻力的增大不是因为升高工作压力导致截面变形过大与滑道干涉所致,钻杆经校直段,钻头中轴线与校直中心线存在一定的角度,即钻杆的前进轨迹就会偏离理论值,或与地层干涉,或可能再次发生弯曲变形;另一主要原因是转向器滑道工作恶化。增加钻杆壁厚,降低工作压力和滑道摩擦因数,设计合理弯曲转向机构是解决问题的关键。