针对矿石中硅线石微细嵌布，铁矿物嵌布亦较细。且有近二分之一铁在非金属矿物晶格之中，除铁难的特点，通过试验研究对比采用一段磨矿磁选除铁后磁尾浮选富集硅线石．浮选精矿再磨后酸浸再除铁的工艺方法，获得了理想的除铁效果，使硅线石精矿质量达到较高品质。     

微细旦粘胶长丝仿真丝绸面料基本力学性能与风格研究

利用FAST仪器对4种微细旦粘胶长丝仿丝绸面料的基本力学性能与风格进行研究,发现其剪切刚度与总紧度比是真丝绸面料的1．52～2．80倍,面料悬垂性及尺寸稳定性明显优于真丝面料,而耐褶皱能力小于真丝面料且面料交织阻力较大,微细旦粘胶长丝仿真丝绸面料单位紧度透气量及透湿率明显小于真丝绸面料,可对同类产品研究提供借鉴．     

从香花岭尾矿库中回收锡石的研究与生产实践

在对尾矿性质研究基础之上,进行了尾矿脱硫及锡石富集试验,发现从尾矿中浮选合格的铅锌混合精矿或者锡石精矿均存在较大难度,但采用浮选方法首先脱除尾矿中的含硫成分,继而采用摇床分选锡石是可行的,在生产实践中获得了合格的锡石精矿.     

某微细粒难选铁矿选矿试验研究

某铁矿为微细粒弱磁性铁矿,有用矿物主要是赤铁矿和磁铁矿,脉石矿物主要是石英．在磨矿中产生许多矿泥,影响其可浮性．采用重选、磁选、浮选、选择性絮凝和磁化焙烧等工艺处理该矿石．结果表明,采用选择性絮凝脱除矿泥,阳离子反浮选工艺最合适．在原矿含铁45．27％的情况下,获得铁品位59．67％,回收率78．84％的铁精矿．     

含砷含碳微细浸染型难处理金矿石浮选工艺改造实践

某选矿厂采用浮选工艺处理含砷含碳微细浸染型难处理金矿石,近年来富集比低,金回收指标不理想.为改善浮选效果,进行了选矿工艺流程考查,并在此基础上实施了工艺流程改造及药剂制度改进.通过对中矿处理工艺、循环载体工艺进行改造及添加调整剂等,提高了富集比、金精矿金品位和金回收率,获得了较好的经济效益,净收益119.6万元/a,同...     

某难处理金矿石工艺矿物学研究

为探索某金矿石特性,采用BPMA自动测试系统、显微镜、化学分析等技术手段,对其开展了详细的工艺矿物学研究,查明矿石矿物组成、主要矿物嵌布特征等,并分析了影响金、银回收的矿物学因素.结果表明:该矿石为高硫、高砷、高钙难处理金矿石,金品位为6.62 g/t、银品位为58.90 g/t;金属矿物主要有黄铁矿、毒砂,多呈粗—中...     

某锡石多金属硫化矿锌高效回收工艺研究

某复杂锡石多金属矿为锡石硫化物-夕卡岩型,含锌、锡矿物分别以铁闪锌矿、锡石为主,主要有价元素含量Zn 6.04％、Sn1.05％,Fe、S含量分别为29.33％、19.08％,主要脉石成分SiO2含量16.63％.为设计合理、高效回收锌工艺流程,对锌回收流程进行了对比实验研究.研究结果表明,采用脱硫—锌硫混合浮选流程,经一段脱硫、二粗一扫三精,获得了锌精矿Zn品位47.06％、Zn回收率90.76％的良好指标,为同类矿石的开发利用提供可利用途径.     

生物氧化—氰化炭浸提金工艺的优化改造

对三和金业生物氧化—氰化炭浸提金工艺进行了优化改造。通过优化生物氧化作业参数,使其处理能力提高了42.49 t/d;增设氧化洗涤液二段沉淀回收高品位含金微细氧化渣、采用二段沉淀—压滤工艺回收粉炭、增设摇床重选工艺回收氰渣中的金等,金的总回收率提高了0.46%。企业年增产黄金884.4 kg,取得了显著的经济效益。     

Enhancement of pentlandite surface magnetism and implications for its separation from serpentine via magnetic separation

The magnetism of pentlandite surface was enhanced through the selective precipitation of micro-fine magnetite fractions on pentlandite surfaces. This was achieved through adjustment of slurry pH and addition of surfactants. The results showed that at pH 8.8 with the addition of 100 g/t sodium hexametaphosphate, 4.5 L/t oleic acid, and 4.5 L/t kerosene, significant amount of fine magnetite particles adhered to the pentlandite surface, while trace amount of coating was found on serpentine surfaces. Thus, the magnetism of pentlandite was enhanced and pentlandite was well separated from serpentine by magnetic separation under the magnetic field intensity of 200 kA/m. Scanning electron microscopy (SEM) and zeta potential measurement were performed to characterize changes of mineral surface properties. Calculations of the extended Derjaguin–Landau–Verwey–Ocerbeek (EDLVO) theory indicated that, in the presence of surfactants the total interaction energy between magnetite and pentlandite became stronger than that between magnetite and serpentine. This enabled the selective adhesion of magnetite particles to pentlandite surfaces, thereby enhancing its magnetism.     

锡石多金属硫化矿微波助磨试验研究

本文以广西某选矿厂锡石多金属硫化矿矿石为原料,研究了微波预处理对矿石磨矿产物粒度组成、磨矿动力学、破碎速率及磨机生产能力的影响。结果表明,微波预处理后,矿石在不同磨矿时间下的磨矿产物粒度均变细,-0.074mm粒级含量提高了4.41%~12.90%;微波预处理前后该矿石磨矿均符合一级磨矿动力学模型;微波预处理使矿石的破碎速率(S₁)值提高近57%,且磨机的生产能力得到了明显提升。因此,微波预处理可以降低矿石的强度,强化矿石的磨矿过程,是一种有效的降低磨矿能耗、提高磨矿效率的方法。