镍基耐海水腐蚀材料的研究概况

综述了镍基耐海水腐蚀材料的研究概况,阐述了Ni-Cu,Ni-Cr,Ni-Mo和Ni-Cr-Mo合金的耐腐蚀性能及其影响因素,展望了该材料研究未来的发展方向。     

The magnetic applications choice among ferrite ceramics,metallic strips,or metal powder cores

Iron-based metallic strip materials such as iron, silicon-iron, and amorphous metal are used for low frequency (50–60 Hz. line) power applications. Low-loss Nickel-based alloys as high permeability strip or insulated powder cores are the choices for stable, low-level higher frequency applications. Iron-based powder cores offer low cost as power supply filter chokes. Ceramic ferrites combine highest frequency operation with low cost and reduced component size as transformers and chokes in telecommunication and high frequency power supply applications.     

层片状堆焊材料的研制

为了研制一种柔性比较好的层片状堆焊材料,用来修复易磨损的零件表面和小型的管材类零件等,选择有机硅密封胶、聚乙烯醇、环氧树脂、水玻璃为粘结剂,与硬质材料Ni60H进行混合,做成层片状堆焊材料;另外再加入WC(碳化钨)作为硬质相,利用TIG焊在Q235钢基体上进行堆焊.结果表明:以有机硅密封胶、有机硅密封胶与环氧树脂1∶1为粘结剂的堆焊材料具有良好的柔韧性,可以任意弯折.以有机硅密封胶与环氧树脂1∶1为粘结剂的堆焊材料加入WC和CaF2后的焊接组织均匀、无缺陷,且堆焊层具有良好的耐磨性能,其洛氏硬度值为HRC43.83.     

喷涂与激光重熔技术制备镍基纳米钴包碳化物复合涂层的研究

采用横流2．0kW CO2激光器，在45钢表面制备了表面较平整、较细密、基本消除了裂纹与孔隙并与基体呈冶金结合的镍基纳米WC／Co复合涂层。通过SEM，EDAX，XRD，AFM及Nano Indenter XP分析了熔覆层的显微组织、成分、物相及结合强度。结果表明，涂层的显微组织为涂层中镶嵌着大量与Ni基合金结合良好的WC／C。颗粒，其中在原子力显微镜下可见相当数量的粒度≤100μm的纳米颗粒。涂层的结合强度比传统热喷涂涂层提高了2．1倍。涂层中纳米WC／Co的纳米效应在激光熔覆中起着重要作用。     

Cr与B对镍基高温钎料在Cf/SiC陶瓷基复合材料上润湿性的影响

研究了Cr和B元素对镍基高温钎料在3D-Cf/SiC陶瓷基复合材料上的润湿性的影响.试验结果发现,在真空度小于10-3 Pa,工作温度1100 ℃,保温时间10 min条件下,当钎料中的Cr元素含量为15%,B元素含量为0.6%时,镍基钎料在Cf/SiC上的润湿角为10°,然而B元素含量增加到2.4%后,润湿角增大到62°,表明钎料中的元素B降低钎料在Cf/SiC上的润湿性.钎料中的活性元素Cr对润湿有重要影响.镍基钎料在Cf/SiC上的润湿过程属于反应润湿,润湿界面生成多种碳化物和硅化物.采用扫描电镜与能谱仪分析界面的微观结构与成分,通过X射线衍射仪检测界面产物.     

High Temperature Creep Deformation Mechanisms of a Hot Corrosion-Resistant Nickel-based Superalloy

Creep properties of the experimental superalloy were investigated in the temperature range 1073–1223 K and stress range 110–550 MPa. The observations of dislocation structures during different creep conditions reveal that in the high stress region, particle-shearing mechanisms including stacking fault formation and antiphase boundary creation are operative and in the low stress region, the dislocation climb mechanism is dominant. From the plot of minimum creep rate versus applied stress, a very low stress region with exponent n < 2, which is related to diffusional creep, is found. Based on the experimental results, a stress–temperature creep deformation mechanism map for the alloy is constructed. On the basis of particle hardening theories and various dislocation-creep theories, the dislocation-creep transitions in terms of internal stress are discussed and calculated threshold stresses of various creep deformation mechanisms indicates that the particle shearing is easier to operate than Orowan looping at high stresses, and general climb is easy to happen at low stresses.     

一种新型镍基高温合金组织及性能的研究

GH4742(俄ЭП742)合金属于典型的高合金化难变形镍基高温合金涡轮盘材料，本文通过调整Al、Ti、Nb的成分对GH4742合金进行改进，发明了一种新型镍基高温合金。利用JMatPro模拟得到平衡相图，再利用光学金相显微镜和场发射扫描电镜对合金的晶粒组织、碳化物以及γ′相分布情况进行观察，同时对力学性能进行了检测。结果表明：平衡状态下的合金从1 400 ℃到300 ℃的冷却过程中相转变可概括为L → L+γ → L+γ+MC →γ+MC+γ′ → γ+γ′+MC+μ → γ+γ′+μ+MC+M23C6 → γ+γ′+μ+MC+M23C6+σ，780 ℃下析出γ′相的质量分数为40.88%；锻造变形工艺为γ+γ′双相区变形，1 120 ℃固溶后经过标准双时效处理(850 ℃/6 h/AC＋780 ℃/6 h/AC)后的显微组织明显可见两种不同尺寸晶粒，小晶粒(13 μm)呈项链状分布于大晶粒(100 μm)周围；该合金中的碳化物主要为大尺寸、不规则形状的MC(NbC、TiC、VC)，断续穿晶和沿晶分布；强化相γ′相的分布状态也有大小两种不同尺寸，γ′I相平均直径为600 nm，γ′II相平均直径为150 nm，两种尺寸γ′相强化的良好匹配，使得该合金在具有较高强度的同时又具有较高的塑性，力学性能优异，室温抗拉强度1 478 MPa，尤其是650 ℃/863 MPa下的持久性能为194 h，远远超过GH4742合金650 ℃/823 MPa持久下50 h的标准。     

对一种组合式钎料的试验分析

针对一种以固定牌号使用的俄罗斯组合式钎料ВПР11-40H进行了试验分析，结果表明，该钎料表现出不同于一般钎料的熔化特性，对不锈钢及高温合金薄壁件具有较弱的溶蚀作用，适用于不等间隙、较大间隙钎缝以及薄壁零件的钎焊，对采用该钎料钎焊GH3044和GH3039接头的性能测试结果表明，接头具有满意的室温和高温性能。     

镍基惰性阳极的耐腐蚀性研究(下)

探讨Ni0—NiFe204基金属陶瓷惰性阳极在冰晶石——氧化铝熔体中的腐蚀行为，通过实验作出电解质分子比、电流密度及氧化铝浓度与腐蚀速率的关系曲线。针对该镍基惰性阳极，找出了该惰性阳极材料腐蚀速率较小时对应分子比，电流密度及氧化铝浓度等电解过程控制的较佳条件。     

等离子熔覆Mo/Ni基合金涂层的组织结构及耐磨性能

应用光学显微镜、扫描电镜(SEM)、X射线衍射(XRD)、透射电镜(TEM)以及滑动磨损实验,研究不同Mo加入量对等离子熔覆镍基合金涂层组织结构和性能的影响。结果表明,熔覆层主要是由面心立方结构的(γNi,Fe)固溶体、六方结构的M7(C,B)3和四方结构的Cr2B等物相构成,在镍基固溶体中存在明显的成分偏析。Mo的加入没有改变熔覆层的相结构,但硼碳化物的相对含量却有所提高,成分偏析逐渐减弱,直至消失,并且促进了等轴晶的形成。Mo的加入可以提高熔覆层的耐磨性能,当其加入量在6%以内时,随着Mo加入量的提高,熔覆层的耐磨性逐渐提高。但是,当加入量达到8%时,耐磨性能开始降低。