Ion migration behavior and its interaction with sintering environment in cation conductor during flash sintering

Flash sintering has been reported in various ceramics. Nevertheless, anion and cation conductors exhibit different flash-sintering behaviors, and the interaction mechanism between the conductive species and the sintering environment has remained unclear. Herein, we report the flash-sintering phenomena of a typical cation conductor, Na₃Zr₂(SiO₄)₂(PO₄) with anode region surrounded by air and NaNO₃ environments. The results prove that the ionic behavior and joule heating distribution can be controlled by changing the electrode environment. Four possible scenarios describing the ion migration behavior and interaction with the environment are proposed for providing a guidance for controlling the ion interaction behavior during flash sintering.     

Dense and core-rim structured B4C-TiB2 ceramics with Mo-Co-WC additive

B₄C-TiB₂ ceramics (TiB₂ ranging 5~70 vol%) with Mo-Co-WC as the sintering additive were prepared by spark plasma sintering. In comparison with B₄C-TiB₂ without additive, the enhanced densification was evident in the sintered specimen with Mo-Co-WC additive. Core-rim structured grain was observed around TiB₂ grains. The interface of the rim between TiB₂ and B₄C phases demonstrated different feature: the inner borderline of the rim exhibited a smooth feature, whereas a sharp curved grain boundary was observed between the rim and the B₄C grain. The formation mechanism is discussed: the epitaxial growth of (Ti,Mo,W)B₂ rim around the TiB₂ core may occur as a result of the solid solution and dissolution-precipitation between TiB₂ phase and the sintering additive. It was revealed that the fracture toughness increased as the content of TiB₂ content increased, alongside the decreased hardness. B₄C-30 vol% TiB₂ specimen demonstrated the optimal combination of mechanical properties, reaching Vickers hardness of 24.3 GPa and fracture toughness of 3.33 MPa·m^1/2.     

超高效液相色谱-串联质谱法同时检测糕点中6种甜味剂

目的建立超高效液相色谱-串联质谱法同时测定糕点中6种常用合成甜味剂的分析方法。方法选用超纯水作为提取溶剂,涡旋和超声提取后,低温离心,取部分上清液加入正己烷除脂,Waters Atlantis■T3色谱柱、甲醇-5 mmol/L甲酸铵(含0.1%甲酸)作为流动相、亲水亲脂平衡型固相萃取柱HLB(hydrophile-lipophile balance)净化。结果6种甜味剂在质量浓度为10~200 ng/mL的曲线范围内呈良好线性关系,相关系数r均大于0.999,平均加标回收率在85.0%-98.2%之间,相对平均偏差(relative standard deviation,RSD)为1.3%~6.7%。结论该方法具有前处理简单、灵敏度高、检测速度快等优点,适合糖精钠、甜蜜素、三氯蔗糖、阿斯巴甜、阿力甜、纽甜的检测,但不适用于安赛蜜的检测。     

Enhanced electrochemical performance of LiNi0.8Co0.1Mn0.1O2 via titanium and boron co-doping

Titanium and boron are simultaneously introduced into LiNi_0.8Co_0.1Mn_0.1O₂ to improve the structural stability and electrochemical performance of the material. X-ray diffraction studies reveal that Ti⁴⁺ ion replaces Li⁺ ion and reduces the cation mixing; B³⁺ ion enters the tetrahedron of the transition metal layers and enlarges the distance of the [LiO₆] layers. The co-doped sample has spherical secondary particles with elongated and enlarged primary particles, in which Ti and B elements distribute uniformly. Electrochemical studies reveal the co-doped sample has improved rate performance (183.1 mAh·g^-1 at 1 C and 155.5 mAh·g^-1 at 10 C) and cycle stability (capacity retention of 94.7% after 100 cycles at 1 C). EIS and CV disclose that Ti and B co-doping reduces charge transfer impedance and suppresses phase change of LiNi_0.8Co_0.1Mn_0.1O_2.     

Microstructure and mechanical properties of α/β-Si3N4 composite ceramics with novel ternary additives prepared via spark plasma sintering

In this study, α/β-Si₃N₄ composite ceramics with high hardness and toughness were fabricated by adopting two different novel ternary additives, ZrN–AlN–Al₂O₃/Y₂O₃, and spark plasma sintering at 1550 °C under 40 MPa. The phase composition, microstructure, grain distribution, crack propagation process and mechanical properties of sintered bulk were investigated. Results demonstrated that the sintered α/β-Si₃N₄ composite ceramics with ZrN–AlN–Al₂O₃ contained the most α phase, which resulted in a maximum Vickers hardness of 18.41 ± 0.31 GPa. In the α/β-Si₃N₄ composite ceramics with ZrN–AlN–Y₂O₃ additives, Zr₃AlN MAX-phase and ZrO phase were found and their formation mechanisms were explained. The fracture appearance presented coarser elongated β-Si₃N₄ grains and denser microstructure when 20 wt% TiC particles were mixed into Si₃N₄ matrix, meanwhile, exhibited maximum mean grain diameter of 0.98 ± 0.24 μm. As a result, the compact α/β-Si₃N₄ composite ceramics containing ZrN–AlN–Y₂O₃ additives and TiC particles displayed the optimal bending strength and fracture toughness of 822.63 ± 28.75 MPa and 8.53 ± 0.21 MPa?m^1/2, respectively. Moreover, the synergistic toughening of rod-like β-Si₃N₄ grains and TiC reinforced particles revealed the beneficial effect on the enhanced fracture toughness of Si₃N₄ ceramic matrix.     

Optimized microwave absorption properties by tailoring the morphology of carbon coated TiC nanoparticles by N2 pressure

Increasing the dielectric loss capacity plays an important role in enhancing the electromagnetic absorption performance of materials. It remains a challenge to simultaneously introduce multiple types of dielectric losses in the material. In this work, we show that the atomic and interfacial dipole polarizations can be simultaneously enhanced by substituting N species into both carbon coating layers and bulk TiC lattices of a core-shell TiC@C material. Additionally, substitution of N species results more exposed TiC(111) facets and refines the TiC grain sizes in the bulk material, which is beneficial for enhancing the scattering of the external electromagnetic waves. The maximum reflection loss of the N substituted TiC@C material is measured as ?47.1 dB with an effective absorbing bandwidth of 4.83 GHz at 1.9 mm, which illustrates a valuable way to further tuning the electromagnetic absorption performance of this type of materials.     

Development of an SFMM/CGO composite electrode with stable electrochemical performance at different oxygen partial pressures

This paper carefully evaluates the electrocatalytic activity of Sr₂FeMo_0.5Mn_0.5O₆ (SFMM) double perovskite as a candidate to substitute the state-of-the-art Ni/YSZ fuel electrode. The electrochemical performance of a 40% SFMM/CGO composite electrode was studied in CO/CO₂ and H₂ with different oxygen partial pressure. Two different cell configurations are prepared at a relatively low temperature of 800 °C to increase the electrochemically active surface area. The cell was supported with a 150 μm 10Sc1CeSZ electrolyte in the first configuration. The cell in the second configuration was made by applying a 400 nm thin 8YSZ layer on 150 μm CGO electrolyte to improve the electrolyte ionic conductivity. Improving catalytic activity with increasing oxygen partial pressure is a key characteristic of the developed electrode. The polarization resistance of about 0.34 and 0.56 Ω cm² at 750 °C in 3%H₂O + H₂ and 60% CO/CO₂ makes this electrode a promising candidate for SOCs application.     

Effect of MoS2/PTFE coatings on performance of Si3N4/TiC ceramics in dry sliding against WC/Co

To enhance the tribological performance of Si₃N₄/TiC ceramics, MoS₂/PTFE composite coatings were deposited on the ceramic substrate through spraying method. The micrographs and basic properties of the MoS₂/PTFE coated samples were investigated. Dry sliding friction experiments against WC/Co ball were performed with the coated ceramics and traditional ones. These results showed that the composite coatings could significantly reduce the friction coefficient of ceramics, and protect the substrate from adhesion wear. The primary tribological mechanisms of the coated ceramics were abrasive wear, coating spalling and delamination, and the tribological property was transited from slight wear to serious wear with the increase of load because of the lower surface hardness and shear strength. The possible mechanisms for the effects of MoS₂/PTFE composite coatings on the friction performance of ceramics were discussed.