Dependence of mechanical and tribological performance on the microstructure of (CrAlTiNbV)Nx high-entropy nitride coatings in aviation lubricant

The (CrAlTiNbV)N_x coatings are fabricated by controlling the substrate bias via magnetron sputtering method. Under low substrate bias, the coating tends to form a loose columnar crystal structure with (200) preferred orientation. However, when the substrate bias increases, the coating transforms into a dense nanocrystalline structure, and the (111) orientation is enhanced. As the substrate bias increases, the residual stress and hardness of the coating gradually increase, while the adhesion strength decreases slightly. Friction tests show that the coating possesses the lowest average friction coefficient (about 0.06) and wear rate (8.7 × 10^-9 mm³/N·m) in 4050# aviation lubricant, which is achieved under the substrate bias of -96 V and -126 V, respectively.     

A knowledge-based archive multi-objective simulated annealing algorithm to optimize series–parallel system with choice of redundancy strategies

Redundancy allocation problem (RAP) is one of the best-developed problems in reliability engineering studies. This problem follows to optimize the reliability of a system containing s sub-systems under different constraints, including cost, weight, and volume restrictions using redundant components for each sub-system. Various solving methodologies have been used to optimize this problem, including exact, heuristic, and meta-heuristic algorithms. In this paper, an efficient multi-objective meta-heuristic algorithm based on simulated annealing (SA) is developed to solve multi-objective RAP (MORAP). This algorithm is knowledge-based archive multi-objective simulated annealing (KBAMOSA). KBAMOSA applies a memory matrix to reinforce the neighborhood structure to achieve better quality solutions. The results analysis and comparisons demonstrate the performance of the proposed algorithm for solving MORAP.     

Ca2+ doping effects on the structural and electrical properties of Na0.5Bi4.5Ti4O15 piezoceramics

Bismuth layer structured Na_0.5Bi_4.5Ti₄O₁₅ (NBT) ferroelectric is one of the most promising materials for potential applications at high temperature. However, it is challenged to achieve a balance between high Curie temperature piezoelectric coefficient and excellent thermal stability for NBT piezoceramics. Here, through chemical modification at the A site of NBT with Ca²⁺, novel (Na_0.5Bi_0.5)_1-xCa_xBi₄Ti₄O₁₅ piezoceramics with excellent properties fabricated by solid state reaction were studied. After doping of Ca²⁺, the Curie temperature T_C increased from 648 °C to 662 °C while the piezoelectric coefficient d₃₃ increased from 14 pC/N to 22 pC/N which can be attributed to the intrinsic contribution of TiO₆ octahedral lattice distortion (tilting and rotation) and the extrinsic contribution of the increased density of domain walls. The composition of (Na_0.5Bi_0.5)_0.95Ca_0.05Bi₄Ti₄O₁₅ ceramics with x = 0.05 has the optimal performance with high T_C of 655 °C, large d₃₃ of 22 pC/N, high electrical resistivity ρ close to 10⁷ Ω cm at 500 °C and especially excellent thermal stability of d₃₃ only about 5% reduction after being annealed at 625 °C. The work effectively reveals the great potential of CNBT-5 ceramics for high-temperature piezoelectric applications.     

Damage mechanism at different transpassive potentials of solution-annealed 316 and 316l stainless steels

Electrochemical impedance spectroscopy (EIS), anodic polarization and scanning electron microscopy techniques were used to investigate the damage mechanism in the transpassive potential region of AISI ...     

Enhancement of optical and electrical properties of SILAR deposited ZnO thin films through fluorine doping and vacuum annealing for photovoltaic applications

Undoped and fluorine doped ZnO thin films were deposited onto glass substrates using successive ionic layer adsorption and reaction (SILAR) technique and then annealed at 350 °C in vacuum ambience. The F doping level was varied from 0 to 15 at% in steps of 5 at%. The XRD analysis showed that all the films are polycrystalline with hexagonal wurtzite structure and preferentially oriented along the (002) plane. Crystallite sizes were found to increase when 5 at% of F is doped and then decreased with further doping. It was seen from the SEM images that the doping causes remarkable changes in the surface morphology and the annealing treatment results in well-defined grains with an improvement in the grain size irrespective of doping level. All the films exhibit good transparency (>70%) after vacuum annealing. Electrical resistivity of the film was found to be minimum (1.32×10⁻³ Ω cm) when the fluorine doping level was 5 at%.     

Stability and cytotoxicity study of NiFe2O4 nanocomposites synthesized by co-precipitation and subsequent thermal annealing

In this article, NiFe₂O₄ nanoparticles (NPs) were prepared by co-precipitation method with subsequent thermal annealing leading to obtainment NPs with average sizes of 78 nm. Structure and magnetic analysis were performed by X-ray diffraction, transmission electron microscopy, Mössbauer spectroscopy and vibrating sample magnetometry techniques. Stability of NiFe₂O₄ NPs was evaluated in PBS solution during 20 days. The toxicity of prepared NPs was evaluated in vitro using different cancer cell lines: HeLa (cervical cancer cell), PC-3 (prostate cancer cell). Fibroblasts like cells of L929 obtained from subcutaneous adipose tissue of mouse were used as normal cells. Results indicate successful synthesis of NiFe₂O₄ NPs that exhibit low cytotoxicity in concentration range from 1 to 100 μg/ml. Presented physical and biological results indicate the possibility of application investigated magnetic nanoparticles in hyperthermia, targeted drug delivery, magnetic resonance imaging or cell separation.     

DP980+Z烘烤硬化值与退火温度的关系

摘要：为了研究退火温度对镀锌DP980+Z烘烤硬化值的影响，退火温度控制在760～820℃之间，系统分析退火温度对烘烤硬化值的影响。通过准静态拉伸试验机测量烘烤硬化值及抗拉强度，采用lepara试剂对组织中的马氏体进行着色，利用金相显微镜及图像处理软件测量马氏体的体积分数；采用扫描电镜观察DP980+Z的双相组织特点，并且将组织图片通过CAD转化成有限元图进行网格划分，建立代表性体积单元（RVE），通过有限元分析铁素体、马氏体强度对烘烤硬化值的影响。在同样的变形量情况下，DP980+Z的原始屈服强度越高，烘烤硬化值越高。     

RF磁控溅射制备钛酸锶钡BST纳米薄膜

钛酸锶钡(BST)薄膜作为一种高K介质材料在微电子和微机电系统等领域具有广阔的应用前景,人们已对BST薄膜的制备工艺技术和介电性能进行了大量的研究。BST纳米薄膜的制备工艺直接影响和决定着薄膜的介电性能(介电常数、漏电流密度、介电强度等)。对RF磁控反应溅射制备BST纳米薄膜的工艺技术进行了综述。从溅射靶的制备、溅射工艺参数的优化、热处理、薄膜组分的控制,及制备工艺对介电性能的影响等方面,对现有研究成果进行了较全面的总结。     

利用整合区域特性约束提高孔隙率模拟精度

本文将空间结构变化的要求与动态资料确定的储量共同作为约束,建立了包含两个约束条件的目标函数, 应用模拟退火算法对孔隙率的空间分布进行预测。在实现过程中,通过初始控制参数的给定及目标函数修改提高了运算效率。由于目标函数有效地整合了静、动态信息,从而降低了模拟结果的不确定性．提高了模拟的精度。合成数据及实际数据的模拟试验表明,整合区域特性约束不仅提高了孔隙率模拟精度,而且算法收敛快、稳定性高。