La0.6Sr0.4Co1-yFeyO3钙钛矿复合氧化物的结构与电学性能

采用固相反应法合成出La0.6Sr0.4Co1-yFeyO3体系复合氧化物样品，XRD分析结果证实不同Co／Fe比例的样品中均形成菱形六面体钙钛矿结构，采用固相烧结法制备出致密的La0.6Sr0.4Co1-yFeyO3体系陶瓷。研究结果表明，在室温到900℃温度范围内La0.4Sr0.4CoO3(y=0)的电导率随温度的增加而单调降低，其它Co／Fe比例样品的电导率随着温度的增加出现最大值，电导率达到最大值的温度随Co／Fe比例的降低而提高。在低温段，La0.6Sr0.4Co1-yFeyO3体系的导电行为符合小极子导电机制，导电活化能随Co／Fe比例的降低而增加。     

La0．8Ca0．2CrO3钙钛矿复合氧化物的GNP法合成与表征

采用GNP（Glycine-Nitrate Process）法合成La0.8Ca0.2CrO3初级粉料，研究甘氨酸用量对产物的晶体结构和显微形貌的影响，并测试烧结体的相对密度和电导率。研究结果表明，甘氨酸与金属离子的摩尔比（G／M^n＋）控制在2．0～2．5时可得到颗粒尺寸细小、均匀（100nm～200nm）的单相钙钛矿粉体，烧结温度为1350℃时样品的相对密度达到91．0％，测试温度为800℃时样品的电导率达到30．5S.cm^-1。与常规固相法相比，GNP法制备的样品具有更好的烧结活性和导电性能。     

NOx adsorption behavior of LaFeO3 and LaMnO3+δ and its influence on potentiometric sensor response

NO_x adsorption behavior on LaFeO₃ (LFO) and LaMnO_3+δ (LMO) was characterized using temperature controlled methods and mass spectrometry. Temperature program desorption revealed decomposition of complex surface species formation when NO or NO₂ was adsorbed on LFO and LMO. LFO exhibited higher adsorption capacity for NO_x species than LMO and was shown to be more active for NO_x surface conversion. Both effects were attributed to the different B-site cations, with iron in LFO in the 3+ valence state, and manganese in LMO in the 3+ and 4+ valence states. Results from diffuse reflectance infrared spectroscopy were used to identify specific nitrite and nitrate species that are formed on the surfaces of LFO and LMO at room temperature. Temperature programmed reaction revealed a complex NO₂ decomposition mechanism to NO and O₂ for LFO and LMO in which the formation of nitrite and nitrate species serve as intermediates below ∼600 °C. NO_x sensing mechanisms were considered and predicted based on the types and quantities of surface species formed.     

钙钛矿结构锰氧化物Pr_(1-x)Ca_xMnO_3(0.4≤x≤0.5)纳米材料的磁性质研究

采用溶胶凝胶法制备了Pr1-xCaxMnO3(0.4≤x≤0.5)系列纳米样品,对其磁性质进行了研究.所有样品在M-T曲线中250K附近的电荷有序转变和170K附近的顺磁-反铁磁转变都消失,与Dong等人的理论模拟计算相符.所有样品在40K都出现了Reentrant spin glass(RSG)态.随着Ca2+掺杂浓度的增加,Mn3+/Mn4+的比例迅速变小,破坏了Mn-O-Mn导电通道,导致磁化强度M逐渐变小.     

Nd0.5Sr0.4Pb0.1Mn0.96Fe0.04O3微观结构的中子衍射

采用固相反应法制备了混价钙钛矿型锰氧化物多晶样品Nd0.5Sr0.4Pb0.1Mn0.96Fe0.04O3,在室温下进行了中子粉末衍射测量并用Rietveld峰形精修程序Fullprof2k对实验数据进行了拟合。结果表明:Nd0.5Sr0.4Pb0.1Mn0.96Fe0.04O3样品具有正交的GdFeO3型结构,空间群为Pnma,Nd(Sr、Pb)原子占据4c晶位,Mn(Fe)原子占据4b晶位,O原子分别占据4c和8d两个不等价的晶位,并得到了MnO6八面体中Mn—O—Mn键角和Mn—O键的键长。     

La0.6Sr0.4Co1-yFeyO3的混合导电性研究

采用直流四探针法和两端子电子阻塞电极交流阻抗谱研究了GNP法制备La0．6Sr0．4Co1-yFeyO3陶瓷的电子-离子混合导电性能．在室温-900℃范围内，La0．6Sr0．4CoO3的电子电导率随温度的升高而单调降低，其它样品的电子电导率随温度的升高在600℃附近达到最大值．La0．6Sr0．4Co1-yFeyO3陶瓷的氧离子电导率随温度的升高而增加．在相同温度下，随着Co／Fe比例的增加，La0．6Sr0．4Co1-yFeyO3陶瓷的电子电导率和氧离子电导率增加，电子导电活化能和离子导电活化能降低．氧离子迁移数随温度的升高而增加，随Co／Fe比例的增加而降低．     

Anomalous Magnetic Behavior in Phase-separated La0.5 Sr0.5 MnO3 +δ Films

(001)La0.5 Sr0.5MnO3 δ films on (001)LaA1O3 substrates were prepared by using a RF magnetron sputtering with powder target.At low temperature, the films exhibit two phase coexistence, which means that ferromagnetic (FM) clusters are embedded in antiferromagnetic (AFM) matrix.Moreover, a shift in hysteresis loop is unexpectedly observed in this inhomogeneous system.We suggest that the anomalous hysteresis loop may result from the unidirectional exchange anisotropy at the interface between AFM and FM clusters.     

Behavior of Mn2+ in perovskite manganites with nominal composition La0.6-xNdxSr0.1MnO3

The fact that there are Mn2+ at the A sites in the ABO3 perovskite phase of manganites with the nominal composition La0.6-xNdxSr0.1MnO3 showed by detailed experimental study and theoretical calculations.The magnetic moments of these Mn2+ are antiparallel to those of the Mn ions at the B sites.The content of the Mn2+ increases as the average ionic radius,(rA),of the ions at A sites decreases,resulting in the experimentally observed phenomenon that the content of the Mn3O4 phase in the manganites decreases with decreasing 〈rA〉.     

Electric transport properties of rare earth doped YbxCa1-xMnO3 ceramics (part I: Optimization of ceramic processing)

A comprehensive study was performed in order to find the effect of different calcination and sintering conditions on the physical properties of calcium manganite ceramics in dependence of temperature T and partial pressure of oxygen p(O₂). The eventual formation of oxygen vacancies during sintering was investigated and the results were confirmed by monitoring the release of oxygen using a ZrO₂ oxygen sensor. The phase transition behavior was studied using thermogravimetric analysis (TGA) in a wide range of p(O₂) ≈ 10^?1 MPa down to 10^-19 MPa at high temperatures accompanied by dilatometry- and XRD-measurements. Furthermore, the present study reveals for the first time a way for reducing and preventing crack formation that may occur during sintering. The present systematic research provides essential fundamental information before performing electrical measurements necessary in order to understand important factors about charge carriers and electrical transport mechanism.     

氧电极催化剂钙钛矿氧化物的制备及催化性能

采用无定形前驱体法,以苹果酸作络合剂,制备了La1-xCaxCoO3和La1-xSrxMnO3系列钙钛矿氧化物,运用差热分析(DTA)和X射线衍射分析(XRD),探讨了催化剂的制备条件,制备La1-xCaxCoO3的最佳pH值为3.0,煅烧温度为650℃,制备La1-xSrxMnO3的pH值影响不大,煅烧温度为600℃。电化学研究结果表明,La0.6Ca0.4CoO3和La0.8Sr0.2MnO3具有较好的催化活性。