Catalytic combustion synthesis of CNTs/MgO composite powders and the influences on the thermal shock resistance of low-carbon Al2O3–C refractories

Using MgC₂O₄, Mg powders as raw materials and Ni(NO₃)₂?6H₂O as a catalyst, CNTs/MgO composite powders were prepared by a catalytic combustion synthesis method. The CNTs/MgO composite powders were characterized by XRD, Raman spectroscopy, FESEM/EDS and HRTEM. The effects of catalyst content on the degree of graphitization and aspect ratio of the CNTs in composite powders were investigated. Moreover, the thermal shock resistance of low-carbon Al₂O₃–C refractories after adding the composite powder was investigated. The results indicated that the CNTs prepared with 1 wt% Ni(NO₃)₂?6H₂O addition had a higher degree of graphitization and aspect ratio. In particular, the aspect ratio could reach approximately 200. The growth mechanism of hollow bamboo-like CNTs in the composite powders was proven to be a V-L-S mechanism. The thermal shock resistance of Al₂O₃–C samples could be improved significantly after adding CNTs/MgO composite powders. In particular, compared with CM0, the residual strength ratio of Al₂O₃–C samples with added 2.5 wt% composite powders could be increased 63.9%.     

Electrospun Zn-doped Ga2O3 nanofibers and their application in photodegrading rhodamine B dye

Ultrawide band gap semiconductor materials have attracted considerable attention in recent years owing to their great potential in the photocatalytic field. In this study, Zn-doped Ga₂O₃ nanofibers with various concentrations were synthesized via electrospinning; they exhibited a superior photocatalytic degradation performance of rhodamine B dye compared to that of undoped Ga₂O₃ nanofibers. The Zn dopant replaced Ga sites via replacement doping, which could increase the concentration of oxygen vacancies and lead to enhanced photocatalytic properties. When the Zn concentration increased, a Ga₂O₃/ZnGa₂O₄ hybrid structure formed, which could further enhance the photocatalytic performance. The separation of photogenerated carriers due to Zn doping and heterojunctions were the primary causes of the enhanced photocatalytic performance. This study provides experimental data for the fabrication of high-performance photocatalysts based on Ga₂O₃ nanomaterials.     

Determination of optical and structural properties of lithium silicate ceramics with different ratios of Sm doped

In this study, the synthesis and luminescence characterization of Samarium (Sm³⁺) doped lithium metasilicate (Li₂SiO₃) phosphor ceramic were investigated. It was presented and discussed the results obtained on the luminescence and other optical studies such as X-ray diffraction (XRD), optical absorption and luminescence properties of Li₂SiO₃:Sm³⁺ phosphor ceramic. The Li₂SiO₃ compound was shown a characteristic phase in XRD. The doping in the lithium compound was not having a significant effect on the basic crystal structure of the material. The maximum photoluminescence (PL) emission for Sm³⁺ doped Li₂SiO₃ was observed at 554, 583, 641, 725 nm and bore resemblance to the visible region of the spectrum. The glow curves of all synthesized materials have a complex peak structure after being irradiated with a ⁹⁰Sr–⁹⁰Y beta source. In addition, the peak between 400 and 600 nm was seen in the radioluminescence (RL) spectrum because of a wide peak thought to be caused by silicate.     

Current advances concerning the most cited metal ions doped bioceramics and silicate-based bioactive glasses for bone tissue engineering

Studies related to biomaterials that stimulate the repair of living tissue have increased considerably, improving the quality of many people's lives that require surgery due to traumatic accidents, bone diseases, bone defects, and reconstructions. Among these biomaterials, bioceramics and bioactive glasses (BGs) have proved to be suitable for coating materials, cement, scaffolds, and nanoparticles, once they present good biocompatibility and degradability, able to generate osteoconduction on the surrounding tissue. However, the role of biomaterials in hard tissue engineering is not restricted to a structural replacement or for guiding tissue regeneration. Nowadays, it is expected that biomaterials develop a multifunctional role when implanted, orchestrating the process of tissue regeneration and providing to the body the capacity to heal itself. In this way, the incorporation of specific metal ions in bioceramics and BGs structure, including magnesium, silver, strontium, lithium, copper, iron, zinc, cobalt, and manganese are currently receiving enhanced interest as biomaterials for biomedical applications. When an ion is incorporated into the bioceramic structure, a new category of material is created, which has several unique properties that overcome the disadvantages of primitive material and favors its use in different biomedical applications. The doping can enhance handling properties, angiogenic and osteogenic performance, and antimicrobial activity. Therefore, this review aims to summarize the effect of selected metal ion dopants into bioceramics and silicate-based BGs in bone tissue engineering. Furthermore, new applications for doped bioceramics and BGs are highlighted, including cancer treatment and drug delivery.     

Annealing and doping-dependent magnetoresistance in single layer poly(3-hexyl-thiophene) organic semiconductor device

We compare the current density–voltage (J–V) and magnetoconductance (MC) response of a poly(3-hexyl-thiophene) (P3HT) device (Au/P3HT(350 nm)/Al) before and after annealing above the glass transition temperature of 150 °C under vacuum. There is a decrease of more than 3 orders of magnitude in current density due to an increase of the charge injection barriers after de-doping through annealing. An increase, approaching 1 order of magnitude, in the negative MC response after annealing can be explained by a shift in the Fermi level due to de-doping, according to the bipolaron mechanism. We successfully tune the charge injection barrier through re-doping by photo-oxidation. This leads to the charge injection and transport transitioning from unipolar to ambipolar, as the bias increases, and we model the MC response using a combination of bipolaron and triplet-polaron interaction mechanisms.     

Electrical and optical properties of semi-insulating polycrystalline silicon thin films: the role of microstructure and doping

We have investigated the relationship between microstructure and electrical conductivity in semi-insulating polycrystalline silicon (SIPOS) with oxygen concentrations in the 2–35 at.% range and the effect of doping with boron, phosphorus, arsenic and erbium by ion implantation. SIPOS thin films are mixtures of silicon and silicon oxide phases. The chemical and morphological evolution of these phases upon annealing is emphasized. Electrical conductivity measurements are interpreted in terms of a physical model containing few free parameters related to the material microstructure. A direct extension of this model explains also the conductivity increase in SIPOS doped with elements of the third or the fifth group. In the last part of the paper, data of electroluminescence at 1.54 μm in Er-implanted SIPOS due to intra-4f transitions of the Er³⁺ ion are shown and discussed.     

Electrochemical C-V Characteristics and Photoluminescence of a-C∶N Films

Amorphous carbon (a-C) films and amorphous carbon films incorporating with the nitrogen (a-C∶N) were deposited on silicon substrates in a radio-frequency driven plasma enhanced chemical vapour deposition system, while the surface electrical properties of films were investigated by electrochemical capacitance-voltage measurements. It was examined the effect of the interface defects on the properties and deduced that the conducting type of a-C∶N films was n-type. Subsequently, a comparative studies of a-C and a-C∶N films were performed by photoluminescence spectra depending on the temperature. With the decrease of the temperature, the main band with peak energy of 2.48 eV in the a-C∶N films was more intense compared with the other three bands caused by amorphous C in the a-C films.     

掺Nd纳米ZnO薄膜特性研究

研究了用真空蒸发法在玻璃衬底上制备稀土掺杂纳米ZnO薄膜结构、导电性及光透射性能。结果显示 ,在 5 0 0℃氧化、热处理稀土元素Nd掺杂后能够明显改善纳米ZnO薄膜的结构特性 ,薄膜的晶粒尺寸随掺杂含量的增加而减小。掺Nd使ZnO薄膜的电性能有所改善但使纳米ZnO薄膜的光透射性有所降低。